| Shape | Flat |
| Technique | Hot Rolled |
| Surface Treatment | Polished |
| Specification | 1220*2440, 1500*3000, 1500*6000, 2000*6000mm |
| Production Capacity | 500000kgs |
| Width Range | 600mm~2030mm |
| Thickness Range | 0.1~120.0mm |
| Length Range | 300~6000mm, Max 18000mm |
| Surface Finish | No.1, 2B, BA, No.3, No.4, No.5, No.8, HL, Etching, SB, Ti-coating, color-coating, embossing |
| Tensile Strength | 600 MPa min |
| Yield Strength | 310 MPa min |
| Elongation | 40% min |
| Hardness | Rockwell B (HR B) max 95, Brinell (HB) max 217 |
| Density | 7800 kg/m3 |
| Certification | AISI, ASTM |
| Model Number | 253MA |
View Detail Information
Explore similar products
AISI 304 SS304 1.4301 SUS304 10*1500*6000mm Stainless Steel Plate 1D Surface
SUS304 ASTM A240 AISI 304 S30408 Stainless Steel Plate For Corrosion Resistance
304 SS316 Price Per Kg S30408 20mmThick 2000*6000mm Stainless Steel Plate
ASTM A240 AISI 321 SUS321 Stainless Steel Plate S32168 For Boiler Pressure
Product Specification
| Shape | Flat | Technique | Hot Rolled |
| Surface Treatment | Polished | Specification | 1220*2440, 1500*3000, 1500*6000, 2000*6000mm |
| Production Capacity | 500000kgs | Width Range | 600mm~2030mm |
| Thickness Range | 0.1~120.0mm | Length Range | 300~6000mm, Max 18000mm |
| Surface Finish | No.1, 2B, BA, No.3, No.4, No.5, No.8, HL, Etching, SB, Ti-coating, color-coating, embossing | Tensile Strength | 600 MPa min |
| Yield Strength | 310 MPa min | Elongation | 40% min |
| Hardness | Rockwell B (HR B) max 95, Brinell (HB) max 217 | Density | 7800 kg/m3 |
| Certification | AISI, ASTM | Model Number | 253MA |
| High Light | High Temperature Resistance 253MA Plate ，Corrosion Resistant 2111HTR Plate ，Hot Rolled UNS S30815 Plate | ||
| ASTM | JIS | AISI | EN |
|---|---|---|---|
| Grade S30100 | SUS301 | 301 | 1.431 |
| S30400 | SUS304 | 304 | 1.4301 |
| S30403 | - | 304L | 1.4307 |
| S31008 | SUS310S | 310S | 1.4845 |
| S31603 | - | 316L | 1.4404 |
| S32100 | SUS321 | 321 | 1.4541 |
| S41008 | SUS410S | 410S | - |
| S43000 | SUS430 | 430 | 1.4016 |
| S43932 | - | - | 1.451 |
| S44400 | SUS444 | 444 | 1.4521 |
| S44500 | SUS430J1L | - | - |
| ASTM A182 Grade FXM-19 | ASTM A269 Grade TPXM-19 | ASTM A580 Grade S20910 |
|---|---|---|
| ASTM A193 Grade B8R Class 1C | ASTM A276 Grade S20910 | ASTM A813 Grade TPXM-19 |
| ASTM A193 Grade B8R Class 1D | ASTM A312 Grade TPXM-19 | ASTM A814 Grade TPXM-19 |
| ASTM A193 Grade B8RA Class 1C | ASTM A314 Grade S20910 | ASTM A943 Grade TPXM-19 |
| ASTM A194 Grade 8R | ASTM A336 Grade FXM-19 | ASTM A959 Grade S20910 |
| ASTM A194 Grade 8RA | ASTM A358 Grade A240 XM-19 | ASTM A965 Grade FXM-19 |
| ASTM A213 Grade XM-19 | ASTM A403 Grade CRXM-19 | AISI XM-19 |
| ASTM A240 Grade S20910 | ASTM A403 Grade WPXM-19 | SAE XM-19 |
| ASTM A249 Grade TPXM-19 | ASTM A479 Grade S20910 | UNS S20910 |
| Element | Min (%) | Max (%) |
|---|---|---|
| C | 0.05 | 0.10 |
| Mn | - | 0.80 |
| Si | 1.10 | 2.00 |
| P | - | 0.040 |
| S | - | 0.030 |
| Cr | 20.0 | 22.0 |
| Ni | 10.0 | 12.0 |
| N | 0.14 | 0.20 |
| Ce | 0.03 | 0.08 |
| Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Rockwell B (HR B) max | Brinell (HB) max |
|---|---|---|---|---|
| 600 | 310 | 40 | 95 | 217 |
| Property | Value |
|---|---|
| Density (kg/m³) | 7800 |
| Elastic Modulus (GPa) | 200 |
| Mean Coefficient of Thermal Expansion (mm/m/°C) 0-100°C | 17.0 |
| Mean Coefficient of Thermal Expansion (mm/m/°C) 0-600°C | 18.5 |
| Mean Coefficient of Thermal Expansion (mm/m/°C) 0-1000°C | 19.5 |
| Thermal Conductivity (W/m.K) at 20°C | 15.0 |
| Thermal Conductivity (W/m.K) at 1000°C | 29.0 |
| Specific Heat 0-100°C (J/kg.K) | 500 |
| Electrical Resistivity (nW.m) | 850 |
| UNS No | Euronorm No | Euronorm Name | Swedish SS | Japanese JIS |
|---|---|---|---|---|
| S30815 | 1.4835 | X9CrNiSiNCe21-11-2 | 2368 | - |
| Grade | Why it might be chosen instead of 253MA |
|---|---|
| 310 | Carburising atmospheres require a higher nickel content |
| 304H | Lower cost alternative, provided the operating temperature is below about 800°C |
| Nickel Alloys | Carburising atmospheres or temperatures above the 1100 - 1150°C maximum of 253MA |
Company Details
Business Type:
Manufacturer
Year Established:
2012
Total Annual:
500,000,000-800,000,000
Employee Number:
100~200
Ecer Certification：
Verified Supplier
Company Overview ： The company has an indoor warehouse of 5000 square meters and an open warehouse of 4000 square meters, which can fully meet the temporary turnover and phased storage of customers' steel pipe reservation. The subordinate processing plant has 6 sets of medium frequency h... Company Overview ： The company has an indoor warehouse of 5000 square meters and an open warehouse of 4000 square meters, which can fully meet the temporary turnover and phased storage of customers' steel pipe reservation. The subordinate processing plant has 6 sets of medium frequency h...