| Shape | Round |
| Technique | Hot Rolled |
| Surface Treatment | Bright |
| Diameter Range | 6-300mm |
| Production Capacity | 50000kgs |
| Tensile Strength | 1105-1310 MPa |
| Yield Strength | 1000-1170 MPa |
| Elongation | 10-16% |
| Hardness | 28-44 HRC |
| Density | 7750 kg/m³ |
| Thermal Conductivity | 18.4-22.7 W/m.K |
| Specific Heat | 460 J/kg.K |
| Electrical Resistivity | 800 nΩ.m |
| Max Temperature | 572°F (300°C) |
| Thermal Expansion | 10.8-11.6 µm/m/°C |
| Certification | ISO, AISI, ASTM, EN, DIN, JIS |
View Detail Information
Explore similar products
EN 10088-2-2005 1.4418 X4CrNiMo16-5-1 Martensitic Stainless Steel Round Bar OD
ASTM A565 616 Martensitic Alloy Round Bar OD 250mm Turbine Blade Stainless Steel
[1.4406] Stainless Steel UNI EN 10088-1 X 2 CRNIMON 17 11-2 AISI 316 LN Round
17-7PH 0Cr17Ni7Al Stainless Steel Bars And Forgings
Product Specification
| Shape | Round | Technique | Hot Rolled |
| Surface Treatment | Bright | Diameter Range | 6-300mm |
| Production Capacity | 50000kgs | Tensile Strength | 1105-1310 MPa |
| Yield Strength | 1000-1170 MPa | Elongation | 10-16% |
| Hardness | 28-44 HRC | Density | 7750 kg/m³ |
| Thermal Conductivity | 18.4-22.7 W/m.K | Specific Heat | 460 J/kg.K |
| Electrical Resistivity | 800 nΩ.m | Max Temperature | 572°F (300°C) |
| Thermal Expansion | 10.8-11.6 µm/m/°C | Certification | ISO, AISI, ASTM, EN, DIN, JIS |
| High Light | Precipitation Hardening Stainless Steel Bar ，Corrosion Resistant 17-4PH Stainless Steel ，High Strength Alloy 630 Bar | ||
17-4 Precipitation Hardening (Type 630) is a chromium-copper precipitation hardening stainless steel designed for applications requiring high strength and moderate corrosion resistance. This alloy maintains high strength up to approximately 600°F (316°C).
Alloy 17-4 PH is a precipitation hardening martensitic stainless steel with copper and niobium additions. The grade combines high strength, hardness (up to 572°F / 300°C), and corrosion resistance. Mechanical properties can be optimized through heat treatment, achieving very high yield strength up to 1100-1300 MPa (160-190 ksi).
This grade should not be used at temperatures above 572°F (300°C) or at very low temperatures. It provides adequate resistance to atmospheric corrosion and diluted acids or salts, with corrosion resistance equivalent to Alloy 304 or 430.
Alloy 17-4 PH withstands corrosive attacks better than standard hardenable stainless steels and is comparable to Alloy 304 in most media. For stress corrosion cracking risks, higher aging temperatures above 1022°F (550°C), preferably 1094°F (590°C), should be selected.
The alloy may experience crevice or pitting attack in stagnant seawater but provides corrosion resistance in chemical, petroleum, paper, dairy, and food processing industries (equivalent to 304L grade).
| Grade | C | Mn | Si | P | S | Cr | Ni | Cu | Nb+Ta |
|---|---|---|---|---|---|---|---|---|---|
| 630 | 0.07 max | 1.0 max | 1.0 max | 0.04 max | 0.030 max | 15-17.5 | 3-5 | 3-5 | 0.15-0.45 |
| Condition | Tensile Strength (MPa) | Yield Strength 0.2% Proof (MPa) | Elongation (% in 50mm) | Hardness Rockwell C (HRC) | Hardness Brinell (HB) |
|---|---|---|---|---|---|
| Solution Treated | 1105 typ | 1000 typ | 15 typ | 38 max | 363 max |
| Condition 900 | 1310 min | 1170 min | 10 min | 40 min | 388 min |
| Condition 1150 | 930 min | 724 min | 16 min | 28 min | 277 min |
| Density (kg/m³) | Mean Co-eff of Thermal Expansion (µm/m/°C) | Thermal Conductivity (W/m·K) | Specific Heat 0-100°C (J/kg·K) | Electrical Resistivity (nΩ·m) |
|---|---|---|---|---|
| 7750 | 10.8 (0-100°C) 11.6 (0-315°C) |
18.4 (100°C) 22.7 (500°C) |
460 | 800 |
Solution treatment (Condition A): Heat to 1040°C for 0.5 hours, then air-cool to 30°C. Small sections may be oil quenched.
Hardening: Age-hardened at low temperatures to achieve required mechanical properties. Typical shrinkage is 0.10% for condition H1150 and 0.05% for condition H900.
| Condition | Hardening Temp (°C) | Time (h) | Typical Hardness Rockwell C | Tensile Strength (MPa) |
|---|---|---|---|---|
| A | Ann | - | 36 | 1100 |
| H900 | 482 | 1 | 44 | - |
| H925 | 496 | 4 | 42 | 1170-1320 |
| H1025 | 552 | 4 | 38 | 1070-1220 |
| H1075 | 580 | 4 | 36 | 1000-1150 |
| H1100 | 593 | 4 | 35 | 970-1120 |
| H1150 | 621 | 4 | 33 | 930-1080 |
Welding: Grade 630 can be welded using all conventional methods without pre-heating. Careful design is required to prevent weldment stresses in high-strength applications.
Machining: Can be machined in solution-treated condition with machining rates similar to grade 304 stainless steel.
Company Details
Business Type:
Manufacturer
Year Established:
2012
Total Annual:
500,000,000-800,000,000
Employee Number:
100~200
Ecer Certification：
Verified Supplier
Company Overview ： The company has an indoor warehouse of 5000 square meters and an open warehouse of 4000 square meters, which can fully meet the temporary turnover and phased storage of customers' steel pipe reservation. The subordinate processing plant has 6 sets of medium frequency h... Company Overview ： The company has an indoor warehouse of 5000 square meters and an open warehouse of 4000 square meters, which can fully meet the temporary turnover and phased storage of customers' steel pipe reservation. The subordinate processing plant has 6 sets of medium frequency h...
Get in touch with us
Leave a Message, we will call you back quickly!