Shanghai Tankii Alloy Material Co.,Ltd
| Payment Terms | L/C, T/T, Western Union |
| Supply Ability | 100 Tons per month |
| Delivery Time | 7-20 days |
| Packaging Details | Carton + Wooden Case |
| OD | 0.3mm Min. |
| WT | 0.01mm Min. |
| Material | nickel iron alloy |
| Shape | strip, bar, wire, sheet, tube |
| Application | Industry, Electrical & electronic industry, CNC engraving, precision instrument industry, Metallurgy |
| Density | 8.20g/cm3 |
| Surface | Bright - surface |
| Brand Name | TANKII |
| Model Number | FeNi29Co18 |
| Certification | ISO9001 |
| Place of Origin | Shanghai, China |
View Detail Information
Explore similar products
Dumet Wire 0.35mm Red Color Filament Used As Sealing Material For All Kinds Of
Dia 1.2mm Aluminum Magnesium Alloy Extruding Welding Wire Az31 Az61 Az91
ROHS Standard Precision Alloys FeNi48/50 SUPRA 50 / 50T / 50SP Sheet For
Kovar / Nilo K Expansion Precision Alloy Ribbon For Glass Sealing
Product Specification
| Payment Terms | L/C, T/T, Western Union | Supply Ability | 100 Tons per month |
| Delivery Time | 7-20 days | Packaging Details | Carton + Wooden Case |
| OD | 0.3mm Min. | WT | 0.01mm Min. |
| Material | nickel iron alloy | Shape | strip, bar, wire, sheet, tube |
| Application | Industry, Electrical & electronic industry, CNC engraving, precision instrument industry, Metallurgy | Density | 8.20g/cm3 |
| Surface | Bright - surface | Brand Name | TANKII |
| Model Number | FeNi29Co18 | Certification | ISO9001 |
| Place of Origin | Shanghai, China | ||
| High Light | Kovar alloy sealing tube ，Expansion alloy 29HK tube ，Precision alloy sealing tube | ||
TK411-29 (Kovar Expansion alloy)
(Common Name: Kovar, Nilo K, KV-1, Dilver Po, Vacon 12) TK411-29 also known as Kovar alloy. it was invented to meet the need for a reliable glass-to-metal seal, which is required in electronic devices such as light bulbs, vacuum tubes, cathode ray tubes, and in vacuum systems in chemistry and other scientific research. Most metals cannot seal to glass because their coefficient of thermal expansion is not the same as glass, so as the joint cools after fabrication the stresses due to the differential expansion rates of the glass and metal cause the joint to crack.
K411-29 was invented to meet the need for a reliable glass-to-metal seal, which is required in electronic devices such as light bulbs, vacuum tubes, cathode ray tubes, and in vacuum systems in chemistry and other scientific research. Most metals cannot seal to glass because their coefficient of thermal expansion is not the same as glass, so as the joint cools after fabrication the stresses due to the differential expansion rates of the glass and metal cause the joint to crack.
K411-29 not only has thermal expansion similar to glass, but its nonlinear thermal expansion curve can often be made to match a glass, thus allowing the joint to tolerate a wide temperature range. Chemically, it bonds to glass via the intermediate oxide layer of nickel oxide and cobalt oxide; the proportion of iron oxide is low due to its reduction with cobalt. The bond strength is highly dependent on the oxide layer thickness and character. The presence of cobalt makes the oxide layer easier to melt and dissolve in the molten glass. A grey, grey-blue or grey-brown color indicates a good seal. A metallic color indicates lack of oxide, while black color indicates overly oxidized metal, in both cases leading to a weak joint.
Mainly used in electric vacuum components and emission control, shock tube, igniting tube, glass magnetron, transistors, seal plug, relay, integrated circuits lead, chassis, brackets and other housing sealing.
ormal composition%
| Ni | 28.5~29.5 | Fe | Bal. | Co | 16.8~17.8 | Si | ≤0.3 |
| Mo | ≤0.2 | Cu | ≤0.2 | Cr | ≤0.2 | Mn | ≤0.5 |
| C | ≤0.03 | P | ≤0.02 | S | ≤0.02 |
Tensile Strength, MPa
| Code of condition | Condition | Wire | Strip |
| R | Soft | ≤585 | ≤570 |
| 1/4I | 1/4 Hard | 585~725 | 520~630 |
| 1/2I | 1/2 Hard | 655~795 | 590~700 |
| 3/4I | 3/4 Hard | 725~860 | 600~770 |
| I | Hard | ≥850 | ≥700 |
Typical Physical properties
| Density (g/cm3) | 8.2 |
| Electrical resistivity at 20ºC(Om*mm2/m) | 0.48 |
| Temperature factor of resistivity(20ºC~100ºC)X10-5/ºC | 3.7~3.9 |
| Curie point Tc/ ºC | 430 |
| Elastic Modulus, E/ Gpa | 138 |
Company Details
Business Type:
Manufacturer,Exporter
Year Established:
1981
Total Annual:
8000000-100000000
Employee Number:
90~100
Ecer Certification：
Verified Supplier
Shanghai Tankii Alloy Material Co., Ltd.specialized in production of Resistance Heating Alloy, Nickel Chromium Alloy, Iron Chromium Aluminum Alloy, Nickel Aluminum Alloy, Manganin, Copper Nickel Alloy, thermocouple wire, pure nickel and other precision alloy materials in the form of round wire, ribb... Shanghai Tankii Alloy Material Co., Ltd.specialized in production of Resistance Heating Alloy, Nickel Chromium Alloy, Iron Chromium Aluminum Alloy, Nickel Aluminum Alloy, Manganin, Copper Nickel Alloy, thermocouple wire, pure nickel and other precision alloy materials in the form of round wire, ribb...
Get in touch with us
Leave a Message, we will call you back quickly!