FOSHAN JINME MEDICAL TECHNOLOGY CO.LTD
Products
Manufacturer of a wide range of products which include HT-Plus Zirconia Block,5D Magic Zirconia Block,4D Pro Zirconia Block,etc
MOQ:
Price:
| Cytotoxicity | 0 Level |
| Density before sintering(g·cm⁻³) | 2.3 |
| Accelerated aging surface monoclinic phase content | ＜15% |
| Density after sintering(g·cm⁻³) | 6.07±0.02 |
| Transparency(1.0±0.02 mm) | 41% |
| Fracture Toughness | 5.0MPa·m¹ᐟ² |
| Bending strength after sintering (MPa) | 1200 |
| Chemical solubility after sintering(μg·cm⁻²) | ＜100 |
| Radioactivity(Bq·g⁻¹) | <0.1 |
| Sintering temperature(℃) | 1530 |
| Coefficient of thermal expansion(25-500℃) (K⁻¹) | 10.4±0.5 |
| Brand Name | APPLEDENTAL |
| Model Number | HT-Plus |
| Place of Origin | China |
| Certification | MDR、CE、ISO、FDA |
MOQ:
Price:
| Sintered Density (g·cm⁻³) | 6.07 ± 0.02 |
| Fracture Toughness | 5.0 MPa·m¹ᐟ² |
| Translucency (1.0 ± 0.02 mm) | 43% - 53% |
| Thermal Expansion Coefficient (25 - 500℃) (K⁻¹) | 10.4 ± 0.5 |
| Green Density (g·cm⁻³) | 3.15 ± 0.05 |
| Chemical Solubility after Sintering (μg·cm⁻²) | < 100 |
| Radioactivity (Bq·g⁻¹) | < 0.1 |
| Sintering Temperature (℃) | 1510 - 1560 |
| Bending Strength after Sintering (MPa) | 800 - 1200 |
| Monoclinic Phase Content after Accelerated Aging | < 15% |
| Cytotoxicity | 0 Level |
| Model Number | 5D Magic |
| Brand Name | APPLEDENTAL |
| Place of Origin | China |
| Certification | MDR、CE、ISO、FDA |
MOQ:
Price:
| Cytotoxicity | 0 Level |
| Density before sintering(g·cm⁻³) | ≥3.0 |
| Density after sintering(g·cm⁻³) | 6.07±0.02 |
| Accelerated aging surface monoclinic phase content | ＜15% |
| Transparency(1.0±0.02 mm) | 46%-53% |
| Fracture Toughness | 5.0MPa·m¹ᐟ² |
| Chemical solubility after sintering(μg·cm⁻²) | ＜100 |
| Radioactivity(Bq·g⁻¹) | ＜0.1 |
| Sintering temperature(℃) | 1510 |
| Coefficient of thermal expansion(25-500℃) (K⁻¹) | 10.4±0.5 |
| Bending strength after sintering (MPa) | 800-1300 |
| Brand Name | APPLEDENTAL |
| Model Number | 4D Pro |
| Certification | MDR、CE、ISO、FDA |
| Place of Origin | China |
MOQ:
Price:
| Density after sintering(g·cm⁻³) | 6.07±0.02 |
| Transparency(1.0±0.02 mm) | 42%-49% |
| Fracture Toughness | 5.0MPa·m¹ᐟ² |
| Cytotoxicity | 0 Level |
| Density before sintering(g·cm⁻³) | ≥3.0 |
| Accelerated aging surface monoclinic phase content | ＜15% |
| Bending strength after sintering (MPa) | 800-1350 |
| Chemical solubility after sintering(μg·cm⁻²) | ＜100 |
| Coefficient of thermal expansion(25-500℃) (K⁻¹) | 10.4±0.5 |
| Radioactivity(Bq·g⁻¹) | ＜0.1 |
| Sintering temperature(℃) | 1510 |
| Model Number | 5D Pro |
| Brand Name | APPLEDENTAL |
| Place of Origin | China |
| Certification | MDR、CE、ISO、FDA |
MOQ:
Price:
| Density after sintering(g·cm⁻³) | 6.07±0.02 |
| Transparency(1.0±0.02 mm) | 42%-49% |
| Fracture Toughness | 5.0MPa·m¹ᐟ² |
| Cytotoxicity | 0 Level |
| Accelerated aging surface monoclinic phase content | ＜15% |
| Density before sintering(g·cm⁻³) | ≥3.0 |
| Bending strength after sintering (MPa) | 800-1250 |
| Chemical solubility after sintering(μg·cm⁻²) | ＜100 |
| Radioactivity(Bq·g⁻¹) | ＜0.1 |
| Sintering temperature(℃) | 1550 |
| Coefficient of thermal expansion(25-500℃) (K⁻¹) | 10.4±0.5 |
| Certification | MDR、CE、ISO、FDA |
| Model Number | 4D |
| Place of Origin | China |
MOQ:
Price:
| Cytotoxicity | 0 Level |
| Density before sintering(g·cm⁻³) | ≥3.0 |
| Accelerated aging surface monoclinic phase content | ＜15% |
| Density after sintering(g·cm⁻³) | 6.07±0.02 |
| Transparency(1.0±0.02 mm) | 43% |
| Fracture Toughness | 5.0MPa·m¹ᐟ² |
| Bending strength after sintering (MPa) | 1200 |
| Chemical solubility after sintering(μg·cm⁻²) | ＜100 |
| Radioactivity(Bq·g⁻¹) | ＜0.1 |
| Sintering temperature(℃) | 1530 |
| Coefficient of thermal expansion(25-500℃) (K⁻¹) | 10.4±0.5 |
| Brand Name | APPLEDENTAL |
| Model Number | ST-C |
| Place of Origin | China |
| Certification | MDR、CE、ISO、FDA |
MOQ:
Price:
| Cytotoxicity | 0 Level |
| Density before sintering(g·cm⁻³) | ≥3.0 |
| Accelerated aging surface monoclinic phase content | ＜15% |
| Density after sintering(g·cm⁻³) | 6.07±0.02 |
| Transparency(1.0±0.02 mm) | 42%-46% |
| Fracture Toughness | 5.0MPa·m¹ᐟ² |
| Bending strength after sintering (MPa) | 900-1200 |
| Chemical solubility after sintering(μg·cm⁻²) | ＜100 |
| Radioactivity(Bq·g⁻¹) | ＜0.1 |
| Sintering temperature(℃) | 1530 |
| Coefficient of thermal expansion(25-500℃) (K⁻¹) | 10.4±0.5 |
| Brand Name | APPLEDENTAL |
| Model Number | ST-ML |
| Place of Origin | China |
| Certification | MDR、CE、ISO、FDA |
MOQ:
Price:
| Cytotoxicity | 0 Level |
| Density before sintering(g·cm⁻³) | ≥3.0 |
| Accelerated aging surface monoclinic phase content | ＜15% |
| Density after sintering(g·cm⁻³) | 6.07±0.02 |
| Transparency(1.0±0.02 mm) | 46% |
| Fracture Toughness | 5.0MPa·m¹ᐟ² |
| Chemical solubility after sintering(μg·cm⁻²) | ＜100 |
| Radioactivity(Bq·g⁻¹) | ＜0.1 |
| Sintering temperature(℃) | 1510 |
| Coefficient of thermal expansion(25-500℃) (K⁻¹) | 10.4±0.5 |
| Bending strength after sintering (MPa) | 1100 |
| Model Number | STH-ML |
| Brand Name | APPLEDENTAL |
| Certification | MDR、CE、ISO、FDA |
| Place of Origin | China |
MOQ:
Price:
| Cytotoxicity | 0 Level |
| Density before sintering(g·cm⁻³) | ≥3.0 |
| Accelerated aging surface monoclinic phase content | ＜15% |
| Density after sintering(g·cm⁻³) | 6.07±0.02 |
| Transparency(1.0±0.02 mm) | 46%-49% |
| Fracture Toughness | 5.0MPa·m¹ᐟ² |
| Bending strength after sintering (MPa) | 500-650 |
| Chemical solubility after sintering(μg·cm⁻²) | ＜100 |
| Coefficient of thermal expansion(25-500℃) (K⁻¹) | 10.4±0.5 |
| Radioactivity(Bq·g⁻¹) | ＜0.1 |
| Sintering temperature(℃) | 1450 |
| Brand Name | APPLEDENTAL |
| Model Number | UT-ML |
| Place of Origin | China |
| Certification | MDR、CE、ISO、FDA |