High Performance Fiberglass Fabric Sheets Chemical Resistant High Strength

Product Specification

​​Glass Fiber Axial Fabrics | High-Performance Composite Reinforcement​​

​​1. Product Introduction​​

Glass Fiber Axial Fabrics are specialized composite reinforcement materials engineered with unidirectional or multi-axial fiber alignment to deliver exceptional strength, durability, and design flexibility. These fabrics are critical in applications requiring high tensile strength, thermal stability, and lightweight solutions. Key features include:

• ​​Unidirectional/Multi-Axial Alignment​​: Fibers oriented in 0°, ±45°, or 90° directions for optimized directional strength

  .

• ​​High Tensile Strength​​: Ranges from ​​3,000–5,000 MPa​​, outperforming traditional woven fabrics in primary stress directions

  .

• ​​Lightweight​​: Density as low as ​​1.5–2.0 g/cm³​​, ideal for aerospace and automotive industries

  .

• ​​Thermal Resistance​​: Withstands temperatures up to ​​600°C​​ without significant degradation

  .

• ​​Chemical Stability​​: Resists acids, alkalis, and solvents, ensuring durability in harsh environments

  .

​​2. Manufacturing Process​​

1. ​​Fiber Preparation​​:

   • E-glass or S-glass filaments (6–25 µm diameter) are drawn from molten glass at ​​1,500–1,600°C

     .

2. ​​Fiber Alignment​​:

   • Filaments are aligned unidirectionally or in multi-axial patterns (0°, ±45°, 90°) using automated spreading machines

3. ​​Stitch Bonding​​:

   • Layers are stitched together with polyester or nylon threads to maintain fiber integrity and prevent displacement

     .

4. ​​Surface Treatment​​:

   • Coated with sizing agents (e.g., silane) to enhance resin adhesion and UV resistance

     .

5. ​​Quality Control​​:

   • ISO 9001-certified testing for tensile strength, fiber orientation accuracy, and thickness uniformity

     .

​​3. Usage Precautions​​

• ​​Handling​​:

  • Wear ​​PPE (gloves, goggles)​​ to avoid fiber irritation; use sharp tools cautiously to prevent breakage

    .

• ​​Resin Compatibility​​:

  • Match fabric type (e.g., E-glass for general use, S-glass for high-strength) with epoxy, polyester, or vinyl ester resins

    .

• ​​Curing Conditions​​:

  • Maintain ​​120–150°C​​ and ​​0.5–1.0 MPa pressure​​ during curing to eliminate voids

    .

• ​​Storage​​:

  • Store in dry, ventilated areas (humidity <60%); avoid prolonged UV exposure to prevent coating degradation

    .

​​4. Specifications​

​

5. Applications & Case Studies​​

​​A. Aerospace​​

• ​​Aircraft Components​​: Reinforces fuselage panels, wings, and engine mounts for lightweight durability.

  • Case: Boeing 787 Dreamliner uses multi-axial fabrics in wing structures to reduce weight by 20%

    .

​​B. Automotive​​

• ​​Body Panels​​: Enhances strength of EV door panels and chassis components.

  • Case: Tesla Model S uses axial fabrics in battery trays for crash resistance

    .

​​C. Wind Energy​​

• ​​Turbine Blades​​: Reinforces leading edges to withstand high wind loads and fatigue.

  • Case: GE Haliade-X offshore wind turbine blades use multi-axial fabrics for extended lifespan

    .

​​D. Marine​​

• ​​Boat Hulls​​: Corrosion-resistant alternative to steel/aluminum.

  • Case: Benetti superyachts employ axial fabrics in hull laminates for 15+ years of saltwater durability

    .

​​E. Industrial Piping​​

• ​​Pressure Vessels​​: Reinforces FRP tanks for chemical storage.

  • Case: Dow Chemical’s storage tanks use E-glass axial fabrics for leak-free service over 25 years.

    
    

​​F. Sports & Safety​​

• ​​Protective Gear​​: Helmets and automotive safety belts.