Shenzhen Upcera Dental Technology Co., Ltd.
| Payment Terms | T/T |
| Delivery Time | 10 working days after received your payment |
| Packaging Details | Carton |
| Density before sintering (g/cm3) | 3.1±0.5 g/cm3 |
| Density after sintering (g/cm3) | 6.08±0.01 g/cm3 |
| CTE after sintering (25-200℃) | (10.5±1.0)x10-6K-1 |
| 3-point bending strength after sintering (MPa) | 1200Mpa |
| Average transmittance (1.0±0.02mm) | 43% |
| Chemical solubility after sintering (μg/cm2) | < 100 |
| Radioactivity after sintering (Bq/g) | <0.1 |
| Sintering temperature (℃) | 1450-1550℃Recommended 1530℃ |
| Brand Name | UPCERA |
| Model Number | ST-White |
| Certification | CE、 FDA 、CFDA、KFDA |
| Place of Origin | China |
View Detail Information
Explore similar products
CAD/CAM Milling 3.1g/cm3 1100Mpa Prettau Zirconia Block
Translucent 600MPa 2.8g/cm3 Dental Zirconia Blocks Anterior Solid
1100Mpa 37% Translucent Dental Zirconia Blocks 3.1g/cm3 For Dental Crowns
98x14mm CAD/CAM Machine Translucent Zirconia Disc CIP
Product Specification
| Payment Terms | T/T | Delivery Time | 10 working days after received your payment |
| Packaging Details | Carton | Density before sintering (g/cm3) | 3.1±0.5 g/cm3 |
| Density after sintering (g/cm3) | 6.08±0.01 g/cm3 | CTE after sintering (25-200℃) | (10.5±1.0)x10-6K-1 |
| 3-point bending strength after sintering (MPa) | 1200Mpa | Average transmittance (1.0±0.02mm) | 43% |
| Chemical solubility after sintering (μg/cm2) | < 100 | Radioactivity after sintering (Bq/g) | <0.1 |
| Sintering temperature (℃) | 1450-1550℃Recommended 1530℃ | Brand Name | UPCERA |
| Model Number | ST-White | Certification | CE、 FDA 、CFDA、KFDA |
| Place of Origin | China | ||
| High Light | cad cam blocks ， zirconium in dentistry | ||
Zirconia Blocks Dental Translucent Shade CE FDA CFDA Certificated
Description:
| Cerac in lab(Sirona) | U14S | 14-13-13 |
| U20S | 20-14-15 | |
| U20LS | 20-19-15 | |
| U40S | 40-14-15 | |
| U40LS | 40-19-15 | |
| 55-19-15 | ||
| U55S | 55-19-15 | |
| U65S | 65-25-22 | |
| U65LS | 65-40-22 | |
| U85LS | 85-40-22 |
|
| ST -Color |
| Density before sintering (g/cm3) |
|
| Density after sintering (g/cm3) |
|
| CTE after sintering (25-200℃) |
|
| 3-point bending strength after sintering (MPa) | |
| Accelerate aging surface monoclinic phase content | < 15% |
| Average transmittance (1.0±0.02mm) | |
| Chemical solubility after sintering (μg/cm2) | < 100 |
| Cytotoxicity test | 0 level |
| Radioactivity after sintering (Bq/g) | |
| Sintering temperature (℃) |
|
|
| ST Color |
| crown | √ |
| Bridge | √ |
| 3-4 units bridge | √ |
| 5-6 units bridge | √ |
| Bridges over 7 units | √ |
| Cantilever bridge | √ |
| Inlay bridge | √ |
| Maryland bridge | √ |
| Telescopic crown | √ |
| Personalized abutment | √ |
Our zirconia discs and blocks are made from the zirconia powder which is of superior quality. Our raw material includes high translucent and super translucent zirconia ceramic powder.
The methods used in making our products are compression molding process and cold isostatic pressing process. After cold isostatic pressing, uniform and compact zirconia ceramic blocks are produced, which are very homogenous, high-strength, have excellent biocompatibility and aesthetics.
Company Details
Business Type:
Manufacturer,Seller
Year Established:
2014
Total Annual:
1000000-10000000
Employee Number:
800~1000
Ecer Certification：
Active Member
Shenzhen Upcera Co., Ltd and Liaoning Upcera Co., Ltd are comprehensive manufacturing and trading company, specializing in R & D, sales & services of dental zirconia, lithium disilicate, hyramic and other dental consumables. Our products are qualified with C E, F D A, I S O 1 3 4 8 5, C F D ... Shenzhen Upcera Co., Ltd and Liaoning Upcera Co., Ltd are comprehensive manufacturing and trading company, specializing in R & D, sales & services of dental zirconia, lithium disilicate, hyramic and other dental consumables. Our products are qualified with C E, F D A, I S O 1 3 4 8 5, C F D ...
Get in touch with us
Leave a Message, we will call you back quickly!