Shenzhen Upcera Dental Technology Co., Ltd.
| Payment Terms | T/T |
| Delivery Time | 10 working days after received your payment |
| Packaging Details | Carton |
| Density before sintering (g/cm3) | 3.1±0.5 g/cm3 |
| CTE after sintering (25-200℃) | 6.08±0.01 g/cm3 |
| 3-point bending strength after sintering (MPa) | (10.5±1.0)x10-6K-1 |
| Accelerate aging surface monoclinic phase content | 1100Mpa |
| Chemical solubility after sintering (μg/cm2) | < 15% |
| Cytotoxicity test | < 100 |
| Sintering temperature (℃) | 1450-1550℃Recommended 1530℃ |
| Brand Name | UPCERA |
| Model Number | ST-ML |
| Certification | CE、 FDA 、CFDA、KFDA |
| Place of Origin | CHINA |
View Detail Information
Explore similar products
Machinable Ceramics Full Dental Zirconia Blank 1100Mpa with C2
Zirconia Ceramic Dental Laboratory Products For CAD/CAM System Compatible
High quality Blank Dental Zirconia KAVO System Dental Implant Materiel 98*12/14
Laboratory Used Equipment CAD / CAM Milling Dental Zirconia
Product Specification
| Payment Terms | T/T | Delivery Time | 10 working days after received your payment |
| Packaging Details | Carton | Density before sintering (g/cm3) | 3.1±0.5 g/cm3 |
| CTE after sintering (25-200℃) | 6.08±0.01 g/cm3 | 3-point bending strength after sintering (MPa) | (10.5±1.0)x10-6K-1 |
| Accelerate aging surface monoclinic phase content | 1100Mpa | Chemical solubility after sintering (μg/cm2) | < 15% |
| Cytotoxicity test | < 100 | Sintering temperature (℃) | 1450-1550℃Recommended 1530℃ |
| Brand Name | UPCERA | Model Number | ST-ML |
| Certification | CE、 FDA 、CFDA、KFDA | Place of Origin | CHINA |
| High Light | zirconium dioxide ceramic ，core dental ceramics | ||
FDA Zirconium Oxide Ceramic Super Translucent Multi - Layer Zirconia In Dentistry
Specifications
| Wieland System | Cerac in lab (Sirona)System |
| D98*10 | 14*13*13 |
| D98*12 | 20*14*15 |
| D98*14 | 20*19*15 |
| D98*16 | 40*14*15 |
| D98*18 | 40*19*15 |
| D98*20 | 55*19*15.5 |
| D98*22 | 65*25*22 |
| D98*25 | 65*40*22 |
|
| 85*40*22 |
FAQ
Q: Is the fit of a zirconia coping important since the zirconia ceramic is so strong?
A: The thicker the cement the weaker the all-ceramic restoration. Cements are not as rigid as zirconia ceramic, so a thicker cement layer will cause more flexural deformation of a ceramic core, increasing the potential for fracture.
Q: Is it ok to grind on a zirconia coping without water spray?
A: Water spray is necessary when grinding on a zirconia ceramic coping. The white light or hot spot you see between a diamond and a zirconia ceramic has been measured at 1500 ºC. If the temperature of zirconia ceramic rises above 1000 ºC, a phase change can occur that will induce cracking and surface defects, lowering the strength of the coping.
Q: Is preparation design of a zirconia coping important since the zirconia ceramic is so strong?
A: Preparation design of the zirconia coping is very important. The thickness of unsupported porcelain should not exceed 2 mm. The zirconia coping should be as thick as needed to avoid unsupported porcelain.
Company Details
Business Type:
Manufacturer,Seller
Year Established:
2014
Total Annual:
1000000-10000000
Employee Number:
800~1000
Ecer Certification：
Active Member
Shenzhen Upcera Co., Ltd and Liaoning Upcera Co., Ltd are comprehensive manufacturing and trading company, specializing in R & D, sales & services of dental zirconia, lithium disilicate, hyramic and other dental consumables. Our products are qualified with C E, F D A, I S O 1 3 4 8 5, C F D ... Shenzhen Upcera Co., Ltd and Liaoning Upcera Co., Ltd are comprehensive manufacturing and trading company, specializing in R & D, sales & services of dental zirconia, lithium disilicate, hyramic and other dental consumables. Our products are qualified with C E, F D A, I S O 1 3 4 8 5, C F D ...
Get in touch with us
Leave a Message, we will call you back quickly!