| Density before sintering (g/cm3) | 3.1±0.5 g/cm3 |
| Density after sintering (g/cm3) | 6.08±0.01 g/cm3 |
| CTE after sintering (25-200℃) | (10.5±1.0)x10-6K-1 |
| 3-point bending strength after sintering (MPa) | 1100Mpa |
| Average transmittance | 25~39% |
| Chemical solubility after sintering (μg/cm2) | < 100 |
| Radioactivity after sintering (Bq/g) | <0.1 |
| Sintering temperature (℃) | 1450-1550℃Recommended 1530℃ |
| Brand Name | UPCERA |
| Model Number | ST-Color |
| Certification | CE、 FDA 、CFDA、KFDA |
| Place of Origin | China |
View Detail Information
Explore similar products
Super Translucent Zirconia Based Ceramics With 16 shades Coloring Liquids
Pre Sintered Zirconia Blocks Dental , Full Zirconia Crowns Blanks With C2
Milling Zirconia Based Ceramics Top Translucent , Multilayer Zirconia Sintering
Colored Dental Zirconia Blank Compatible Milling Zirconium with B2
Product Specification
| Payment Terms | T/T | Supply Ability | 10 working days after received your payment |
| Packaging Details | Carton | Density before sintering (g/cm3) | 3.1±0.5 g/cm3 |
| Density after sintering (g/cm3) | 6.08±0.01 g/cm3 | CTE after sintering (25-200℃) | (10.5±1.0)x10-6K-1 |
| 3-point bending strength after sintering (MPa) | 1100Mpa | Average transmittance | 25~39% |
| Chemical solubility after sintering (μg/cm2) | < 100 | Radioactivity after sintering (Bq/g) | <0.1 |
| Sintering temperature (℃) | 1450-1550℃Recommended 1530℃ | Brand Name | UPCERA |
| Model Number | ST-Color | Certification | CE、 FDA 、CFDA、KFDA |
| Place of Origin | China | ||
| High Light | zirconium dioxide ceramic ，dental ceramic materials | ||
Dental Laboratory Milling Supplies Core Dental Ceramics ST 16 Pre - shaded
Specifications:
ST COLOR block: suitable for single shaded crown and bridge with VITA classic 16 shades(A1/A2/A3/A3.5/A4/B1/B2/B3/B4/C1/C2/C3/C4/D2/D3/D4)
| ZZ CAD/CAM | D95-10 | |
| D95-12 | ||
| D95-14 | ||
| D95-16 | ||
| D95-18 | ||
| D95-20 | ||
| D95-22 | ||
| D95-25 | ||
| D95-30 |
Indications:
| ST Color |
crown | √ |
Bridge | √ |
3-4 units bridge | √ |
5-6 units bridge | √ |
Bridges over 7 units | √ |
Cantilever bridge | √ |
Inlay bridge | √ |
Maryland bridge | √ |
Telescopic crown | √ |
Personalized abutment | √ |
Operation Guide:
1 .Place a zirconia block in your CAD/CAM machine and machine it following the manufacturer’s instructions.
2 .After machining is completed, remove the zirconia block from the CAD/CAM machine first. Then remove the framework from the zirconia block with a diamond disc. Subsequently, place the framework on a sintering tray with zirconia beads and put them in the oven for sintering.
3 .Program the furnace according to its instruction manual and zirconia block’s sintering chart, and then start sintering.
4 .Do not remove the sintered framework until it is fully cooled down. Examine the sintered framework for wall thickness, margin fit and seat fit. If necessary, make minor adjustments with a water cooled diamond tool.
5 .Make sure no wall thickness is less than 0.5mm and no connector is thinner than 9mm2.
6 .Rinse the sintered framework with water and dry completely.
Company Details
Business Type:
Manufacturer,Seller
Year Established:
2014
Total Annual:
1000000-10000000
Employee Number:
800~1000
Ecer Certification：
Active Member
Shenzhen Upcera Co., Ltd and Liaoning Upcera Co., Ltd are comprehensive manufacturing and trading company, specializing in R & D, sales & services of dental zirconia, lithium disilicate, hyramic and other dental consumables. Our products are qualified with C E, F D A, I S O 1 3 4 8 5, C F D ... Shenzhen Upcera Co., Ltd and Liaoning Upcera Co., Ltd are comprehensive manufacturing and trading company, specializing in R & D, sales & services of dental zirconia, lithium disilicate, hyramic and other dental consumables. Our products are qualified with C E, F D A, I S O 1 3 4 8 5, C F D ...
Get in touch with us
Leave a Message, we will call you back quickly!