Changzhou DLX Alloy Co., Ltd.
| Payment Terms | L/C, T/T, Western Union, MoneyGram |
| Supply Ability | 500 tons per month |
| Delivery Time | 7-20 days |
| Packaging Details | Spool package with Carton box, Coil package with polybag |
| Material | Ferrous Chromium Aluminum |
| Resistivity | 1.25+/-0.05 |
| Tensile Strength | 580-680MPA |
| Elongtation | ≥12% |
| Application | Heating, Resistivity |
| Condition | Hard / Soft |
| Sureface | Bright, Oxided, Acide |
| Maximum Temperature | 950℃ |
| Melting Point | 1450℃ |
| Brand Name | DLX |
| Model Number | 1Cr13Al4 |
| Place of Origin | China Jiangsu |
| Certification | CE,ROHS |
View Detail Information
Explore similar products
8mm Bright 830 MPA 0Cr27Al7Mo2 Resistance Wire FeCrAl Alloy
0.03mm 600 MPA 0Cr21Al4 Iron Chromium Aluminum Alloy
Bead Insulated Coils 0Cr25Al5FeCrAl 8mm Heating Wire FeCrAl Alloy
2.5mmx5mm Industrial Electric Furnace 0Cr21Al6Nb Strip FeCrAl Alloy
Product Specification
| Payment Terms | L/C, T/T, Western Union, MoneyGram | Supply Ability | 500 tons per month |
| Delivery Time | 7-20 days | Packaging Details | Spool package with Carton box, Coil package with polybag |
| Material | Ferrous Chromium Aluminum | Resistivity | 1.25+/-0.05 |
| Tensile Strength | 580-680MPA | Elongtation | ≥12% |
| Application | Heating, Resistivity | Condition | Hard / Soft |
| Sureface | Bright, Oxided, Acide | Maximum Temperature | 950℃ |
| Melting Point | 1450℃ | Brand Name | DLX |
| Model Number | 1Cr13Al4 | Place of Origin | China Jiangsu |
| Certification | CE,ROHS | ||
| High Light | Fecral Heating Resistance Wire ，1.6mm SWG16 Heating Resistance Wire ，1Cr13Al4 Heating Resistance Wire | ||
1Cr13Al4 alloy is a high resistance electric heating alloy, known for its excellent corrosion resistance and high-temperature strength. It has a high electrical resistivity and a low resistance temperature coefficient. The main components of 1Cr13Al4 include chromium, aluminum, nickel, etc., which endow the alloy with good electrical resistivity, high-temperature oxidation resistance, and corrosion resistance.
The 1Cr13Al4 resistance wire plays an important role in resistance performance testing. When conducting resistance performance tests, 1Cr13Al4 resistance wire is often used as one of the test samples to evaluate its resistance characteristics and stability. This type of testing typically involves measuring the resistance value of the wire and testing it under different temperatures, humidities, or other environmental conditions to determine its performance under various operating conditions.
The resistance characteristics of 1Cr13Al4 resistance wire are determined based on its material composition and manufacturing process. Therefore, in resistance performance testing, it is compared to standard specifications to ensure that it meets the expected resistance values and performance requirements. Various measuring devices and instruments such as multimeters, bridges, etc., may be used during the testing process to ensure accurate measurement of the resistance wire.
Additionally, durability testing may also be conducted in resistance performance testing to assess the stability and durability of 1Cr13Al4 resistance wire under long-term use and different operating conditions. This type of testing can help determine the reliability and lifespan of the resistance wire and provide reference for its performance in practical applications.
Overall, the application of 1Cr13Al4 resistance wire in resistance performance testing aims to evaluate its resistance characteristics and stability under different conditions to ensure that it meets the expected performance requirements and supports its reliability in various industrial applications.
| Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
| Nb0.5 | Mo1.8-2.2 | |||||||
| Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
| Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | ||
| Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
| Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
| Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
| Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | |
| ||
| ||
| ||
| ||
| ||
Company Details
Business Type:
Manufacturer,Seller
Year Established:
2002
Total Annual:
1000000-120000000+
Employee Number:
100~150
Ecer Certification：
Verified Supplier
Changzhou DLX Alloy Co., Ltd. was established in 2002 and has passed ISO9001 international quality management system certification and SGS certification.We initially focused on the production of resistance alloys. Over the past 20 years, we have continued to conduct research and development and now ... Changzhou DLX Alloy Co., Ltd. was established in 2002 and has passed ISO9001 international quality management system certification and SGS certification.We initially focused on the production of resistance alloys. Over the past 20 years, we have continued to conduct research and development and now ...
Get in touch with us
Leave a Message, we will call you back quickly!