Product Name | Spalling Resistance High Alumina Bricks |
Al2O3 Content | ≥70% |
Bulk Density | ≥2.55 g/cm³ |
Apparent Porosity | ≤22% |
C.C.S | ≥60 Mpa |
RUL T0.6 | ≥1470℃ |
Thermal Shock Resistance | ≥20 times (1100℃, water cooling) |
Application | Cement kiln |
Use Zone | Transition zone in rotary kiln |
Fe2O3 | ≤1.5% |
Brand Name | Jansincere |
Model Number | GKBL-70, KBL-70 |
Certification | ISO9001:2015 |
Place of Origin | Xinmi City, Henan, China |
View Detail Information
Explore similar products
Regeneration Baking Fire Rated Bricks , Heat Resistant Bricks For Fire Pit
Heat Insulation Furnace Refractory Bricks Industrial High Temperature Strength
High Refractoriness Blast Furnace Brick , Acid Proof Wood Stove Fire Bricks
Chrome Mullite Basic Refractory Bricks , High Heat Fire Resistant Bricks
Product Specification
Payment Terms | L/C, T/T, Western Union | Supply Ability | 45000 ton of silicon mullite bricks per year |
Delivery Time | 30-45 days | Packaging Details | Wooden pallet, plastic shrink film, paper corner protection and straps protected outside. Pallet size: 95*95cm, 100*100cm or as request. |
Product Name | Spalling Resistance High Alumina Bricks | Al2O3 Content | ≥70% |
Bulk Density | ≥2.55 g/cm³ | Apparent Porosity | ≤22% |
C.C.S | ≥60 Mpa | RUL T0.6 | ≥1470℃ |
Thermal Shock Resistance | ≥20 times (1100℃, water cooling) | Application | Cement kiln |
Use Zone | Transition zone in rotary kiln | Fe2O3 | ≤1.5% |
Brand Name | Jansincere | Model Number | GKBL-70, KBL-70 |
Certification | ISO9001:2015 | Place of Origin | Xinmi City, Henan, China |
High Light | blast furnace brick ,fire safe bricks |
Introduction:
High-Alumina Brick is made of special grade high-bauxite chamotte and compound material of ZrO2 in a proportion by high pressure shaping and burning.
Features:
strong anti-stripping capacity, erosion proof of potassium, sodium, sulfur, chlorine and basic salt, low heat conductivity.
Application:
is an ideal material used as the transition band and decomposition zone, also can be used at the door cover and cooler for cement kiln.
Technical Index:
Item | Index | ||
GKBL-70 | KBL-70 | ||
Chemical Composition | Al2O3/% ≥ | 70.0 | 70.0 |
ZrO2/% ≥ | 6.0 | -- | |
*Fe2O3/% ≤ | 1.5 | 1.5 | |
Physical Property | Bulk Density /g/cm3 ≥ | 2.55 | 2.55 |
Apparent Porosity /% ≤ | 22 | 20 | |
Cold Crushing Strength /Mpa ≥ | 60 | 60 | |
Refractoriness Under Load T0.6/℃ ≥ | 1470 | 1470 | |
Thermal Shock Resistance (1100℃~Water Cooling) Times ≥ | 20 | 15 | |
*this is only as the optional index. |
Company Details
Business Type:
Manufacturer,Distributor/Wholesaler,Exporter,Seller
Year Established:
1986
Total Annual:
15000000-20000000
Employee Number:
400~500
Ecer Certification:
Active Member
Zhengzhou Jansincere Refractory Co., Ltd was founded in 1986. With continuous effort, now Jansincere has three branches. We are focused on providing professional refractory design, manufacturing, installation and maintenance services for carbon industry, non-ferrous metallurgy industry, construction... Zhengzhou Jansincere Refractory Co., Ltd was founded in 1986. With continuous effort, now Jansincere has three branches. We are focused on providing professional refractory design, manufacturing, installation and maintenance services for carbon industry, non-ferrous metallurgy industry, construction...
Get in touch with us
Leave a Message, we will call you back quickly!