SHANGHAI UNITE STEEL
| Supply Ability | 2000/pieces |
| Delivery Time | Within 5-35 days |
| Packaging Details | Wooden case or according to customers' requirement |
| Production Technique | hot forged |
| Quality Standard | ISO, GB, ASTM, DIN, JIS |
| Surface | Black, Bright, Smooth |
| Testing | Eddy test |
| Inspection | The third party is acceptable |
| Delivery time | Within 5-35 days |
| Brand Name | UST |
| Model Number | OD80-1200MM |
| Certification | ISO9001 |
| Place of Origin | CHINA |
View Detail Information
Explore similar products
4140 / 42CrMo4 / SCM440 Carbon Steel Shaft , OD 80-1200 Mm Rotor Shaft
OD 80-1200 Mm Forged Steel Shaft S45C / 1045/CK45 Grade Carbon Steel
817M40 / SAE4340 Forged Steel Shaft For Mechnical Purpose OD 80-1200 Mm
DIN X20Cr13 / 1.4021 / 420 Steel Shaft , Hot Forged Alloy Steel Shaft
Product Specification
| Supply Ability | 2000/pieces | Delivery Time | Within 5-35 days |
| Packaging Details | Wooden case or according to customers' requirement | Production Technique | hot forged |
| Quality Standard | ISO, GB, ASTM, DIN, JIS | Surface | Black, Bright, Smooth |
| Testing | Eddy test | Inspection | The third party is acceptable |
| Delivery time | Within 5-35 days | Brand Name | UST |
| Model Number | OD80-1200MM | Certification | ISO9001 |
| Place of Origin | CHINA | ||
| High Light | Alloy Steel Shaft ，Carbon Steel Shaft | ||
30CrNiMo8/1.6580 alloy forged steel shaft, OD80-1200mm'
Application: 30CrNiMo8/ DIN 1.6580 steel is widely used in the manufacture of the camshaft and connecting rod of engine parts, poor processability. 30CrNiMo8 is suitable for permanently stressed components with large cross sections for automotive and mechanical engineering.For economic performance under severe dynamic stress, parts must be designed for optimum strength or toughness.
Chemical composition: Carbon:0.26/0.34; Silicon:Max0.40; Manganese:0.50/0.80;
Chromium:1.80/2.20; Molybdenum:0.30/0.50; Nickel:1.80/2.20;
Forging:
1)Preheat 1.6580 forged alloy steel carefully.
2)Raise the forging temperature up to 1150-1200°C.
3)Keep the forging temperature above 850°C.
9. Heat Treatment: Hardening&Tempering(quenched and tempered and after stress relieved)
1)Heating 30CrNiMo8 steel uniformly to 850°C;
2)W-Nr 1.6580 alloy steel should be quenched in the oil;
3)Heat the material to the temperature 550°C;
4)Soak at this temperature for at least 2 hours;
5)1.6580 alloy steel should be cooled in the furnace.
(In case after QT a straightening process is necessary then the products should be tempered and distorsion-poor annealed with at least more than 625°C.)
Pakage& shipping
Company Details
Business Type:
Manufacturer,Distributor/Wholesaler,Agent,Exporter,Trading Company,Seller
Year Established:
2010
Total Annual:
10000000-25000000
Employee Number:
50~110
Ecer Certification：
Active Member
We, Shanghai Unite Steel are committed to integrate engineering steel resources in china and serve the global engineering steel market. Our company has more than 15 years of experience in steel researching, production, managing and sales. And our team mostly are based on and worked in national... We, Shanghai Unite Steel are committed to integrate engineering steel resources in china and serve the global engineering steel market. Our company has more than 15 years of experience in steel researching, production, managing and sales. And our team mostly are based on and worked in national...
Get in touch with us
Leave a Message, we will call you back quickly!