Shenzhen KangLiBang Technology Co., Ltd
| Payment Terms | T/T |
| Delivery Time | 5-7days |
| Packaging Details | 1KG/BOTTLE |
| Hardness(ShoreA) | 50±5 |
| Tensile Strength (Mpa) | 10~12 |
| Elongation at Break(%) | 500~540 Compression Set %(100℃/22h): ＜5 |
| Specific Gravity | 1.1g/cm3 |
| C-100A | transparent paste, containing platinum and organic silicon polymer |
| C-100B | transparent organic silicon polymer, containing crosslinking agent and inhibitor |
| Brand Name | KangLiBang |
| Model Number | C-100AB |
| Certification | ROHS，SGS |
| Place of Origin | Guangdong, China |
View Detail Information
Explore similar products
Vulcanizing Silicone Rubber Curing Agent Neutral PH Food Grade OEM
Raw Elastomer Silicone Curing Agent Platinum Catalyzed Addition Cure In Bulk
ODM Inflammable Curing Agent Platinum Catalyst For Silicone Rubber C-15
Platinum Catalyst Rubber Silicone Curing Agent Transparent Medical Grade OEM
Product Specification
| Payment Terms | T/T | Delivery Time | 5-7days |
| Packaging Details | 1KG/BOTTLE | Hardness(ShoreA) | 50±5 |
| Tensile Strength (Mpa) | 10~12 | Elongation at Break(%) | 500~540 Compression Set %(100℃/22h): ＜5 |
| Specific Gravity | 1.1g/cm3 | C-100A | transparent paste, containing platinum and organic silicon polymer |
| C-100B | transparent organic silicon polymer, containing crosslinking agent and inhibitor | Brand Name | KangLiBang |
| Model Number | C-100AB | Certification | ROHS，SGS |
| Place of Origin | Guangdong, China | ||
| High Light | FDA Approved Silicone Curing Agent ，Silicone Curing Agent Paste ，FDA Approved sylgard 184 curing agent | ||
Two Component Platinum Addition Type Cross Linking Agent
C-100AB,two component platinum addition type cross linking agent which is added in the raw silicones for the cross linking of food and medical grade silicone rubber items ,The vulcanized products can pass the FDA test, ,it features with non-toxic, odourle
PRODUCT SPECIFICATION:
C-100A: transparent paste, containing platinum and organic silicon polymer
C-100B: transparent organic silicon polymer, containing crosslinking agent and inhibitor
Hardness(ShoreA) : 50±5
Tensile Strength (Mpa) : 10~12
Elongation at Break(%): 500~540 Compression Set %(100℃/22h): ＜5
Specific Gravity: 1.1g/cm3
PRODUCT DETAILS:
C-100AB,two component platinum addition type cross linking agent
Which is added in the raw silicones for the cross linking of food and medical grade silicone rubber items ,
The vulcanized products can pass the FDA test,
it features with non-toxic, odourless, high grade of transparency, well anti-yellowing and other properties.
PRODUCT ADVANTAGE:
Food Grade and Medical Grade,No secondary curing
Anti-yellow,High penetration
Low addition rate
ATTENTION:
The raw material is easy poisoning once contact with nitrogen, phosphorus, sulfur and heavy metal materials.
C-100A and C-100B can not be added at the same time. First add C-100B into raw silicone and mixing evenly, then add C-100A into raw silicone. The addition order is important.
The temperature of mixing machine which used for mixing silicone with platinum curing agent can not be higher than 45℃. Please add this agent after being cold.
The mixed raw materials should be used up within two days
.Please choose the suitable raw materials for hot air vulcanization,unmatched raw material will cause bubbles in the process.
PROCESSING:
C-100B 2.0~2.5%
C-100A 0.5~0.6%
Curing condition: IR(6meters),constant temperature ±5℃. First curing: IR curing at 190~200℃ for 40~60 seconds.
Finished curing: After first curing, it should be cured again as below conditions.
| Curing temperature | 155~165℃ | 165~175℃ | Over 175℃ |
| Curing time | 3~5minutes | 3minutes | 2minutes |
Application weight ratio:
C-100B 1.5~2.0%
C-100A 0.5~0.6%
Curing condition:IR(6meters),constant temperature ±5℃.
First curing: IR(Infrared Radiation) curing at 140℃ for 40~50 seconds. Finished curing:After first curing, it should be cured again as below conditions.
|
Curing temperature |
80~90℃ |
95~110℃ |
115~135℃ |
|
Curing time |
7 minutes |
5 minutes |
4 minutes |
Type two: Compression Molding
Application weight ratio:
C-100B 1.0~1.5%
C-100A 0.5%
Curing temperature: 115~135℃(200~300seconds)
Curing time:Can be adjusted with the thickness and type of the silicone products
Company Details
Business Type:
Manufacturer
Year Established:
2010
Total Annual:
5000000-10000000
Employee Number:
50~100
Ecer Certification：
Verified Supplier
Shenzhen Kanglibang Science & Technology Co., Ltd was founded in 2010, focusing on the development of new adhesive materials. It is a national-level specialized and special "little giant" enterprise integrating the research and development, manufacturing, sales and service of adhesive ... Shenzhen Kanglibang Science & Technology Co., Ltd was founded in 2010, focusing on the development of new adhesive materials. It is a national-level specialized and special "little giant" enterprise integrating the research and development, manufacturing, sales and service of adhesive ...
Get in touch with us
Leave a Message, we will call you back quickly!