Chongqing Leomed Technology Co., Ltd.
| Productn Name | PEEK |
| Color | Natural/White/Yellow/Red |
| Density(g/cm3) | 1.32/1.48/1.51/1.35 |
| Bending Strength(MPa) | 163/152/154/158 |
| Bending ModulusBending ModulusBending Modulus(GPa) | 4/5.3/5.6/4.8 |
| Bending Modulus(KJ/m2) | 199/145/162/176 |
| Brand Name | Leomed |
View Detail Information
Explore similar products
Class II All-in-One Stain Glaze Paste for Zirconia Crowns 4 Main 18 Effect
Mixable Shade System Paste Cervical / Incisal Zone Formulas For PFM & Glass
3 :1 Glaze-Blue Ratio Dental Aesthetic Paste with Diluting Liquid Class II and
No Separate Glazing Dental Paste 12-38°C Storage Stability Manual Power Source
Product Specification
| Productn Name | PEEK | Color | Natural/White/Yellow/Red |
| Density(g/cm3) | 1.32/1.48/1.51/1.35 | Bending Strength(MPa) | 163/152/154/158 |
| Bending ModulusBending ModulusBending Modulus(GPa) | 4/5.3/5.6/4.8 | Bending Modulus(KJ/m2) | 199/145/162/176 |
| Brand Name | Leomed | ||
| High Light | Zirkonzahn Compatible Dental Discs ，160MPa+ Strength Dental Discs ，CAD CAM Dental Discs | ||
PEEK Dental Discs 160MPa+ Strength, Zirkonzahn & Amann Girrbach Compatible CAD/CAM
Medical-Grade PEEK Dental Discs
Engineered as the ultimate bone-mimetic solution for permanent implant prosthetics, these semi-crystalline PEEK discs deliver revolutionary biomechanical performance. With an elastic modulus (4-5.6 GPa) mirroring cortical bone and flexural strength exceeding 160MPa, they eliminate stress-shielding risks while enabling precision CAD/CAM fabrication at 260°C.
Stress-Shielding Elimination – 4.0-5.6 GPa modulus matches human bone for load distribution
Fatigue-Resistant Architecture – >160MPa flexural strength supports multi-unit bridges
Bioinert Certification – ISO 10993-compliant surface inhibits bacterial colonization
Imaging Compatibility – Zero CT/MRI artifacts for accurate diagnostics
| Property | PEEK Discs | Titanium | PMMA |
|---|---|---|---|
| Elastic Modulus (GPa) | 4.0-5.6 | 110-120 | 2.0-3.0 |
| Density (g/cm³) | 1.32-1.51 | 4.4-4.5 | 1.15-1.19 |
| Allergy Incidence | 0% | >8% | <0.1% |
| Aesthetic Adaptability | Tintable (★★★★☆) | Non-adaptable | High (★★★★★) |
Tooling Requirements
Diamond-coated carbide burs
18,000-25,000 RPM spindle speed
≥0.75 MPa vacuum pressure
Post-Processing
Sandblasting – 50μm alumina oxide
Staining – PEEK-specific dyes (80°C/10min)
Healing Abutments – 37% ↑ osteoblast proliferation vs titanium
Removable Dentures – 60% lighter than cobalt-chrome
Surgical Guides – Withstands 200+ autoclave cycles (134°C)
| Grade | Density (g/cm³) | Flex Strength (MPa) | Modulus (GPa) |
|---|---|---|---|
| Natural | 1.32 | 163 | 4.0 |
| White | 1.48 | 152 | 5.3 |
| Yellow | 1.51 | 154 | 5.6 |
| Red | 1.35 | 158 | 4.8 |
Company Details
Business Type:
Manufacturer,Trading Company
Year Established:
2019
Total Annual:
1000000-1500000
Employee Number:
100~150
Ecer Certification：
Verified Supplier
Chongqing Leomed Technology Co., Ltd. is a rapidly growing and professional company that specializes in providing dental CAD/CAM solutions to customers worldwide. With a strong focus on “innovation, precision, validation, and customer satisfaction”, we invest significant efforts in resea... Chongqing Leomed Technology Co., Ltd. is a rapidly growing and professional company that specializes in providing dental CAD/CAM solutions to customers worldwide. With a strong focus on “innovation, precision, validation, and customer satisfaction”, we invest significant efforts in resea...
Get in touch with us
Leave a Message, we will call you back quickly!