Product Specification

3 Strands Twisted PE/PP/Nylon Packaging Rope for Secure Fastening

Production Process

Step 1: Raw Material Preparation & Drying

• Material Selection: High-quality granular resins are chosen based on the rope’s intended use:
  • PE resin (low-density or high-density): For cost-effectiveness, chemical resistance, and flexibility.
  • PP resin: For higher tensile strength, heat resistance, and low water absorption.
  • Nylon resin (e.g., Nylon 6, Nylon 66): For exceptional abrasion resistance, impact strength, and elasticity.
• Drying (for Nylon/PP): Nylon and PP resins are hygroscopic (absorb moisture from air), which can cause bubbles or weak points in the final rope. They are dried in a dehumidifying dryer at 80–120°C for 2–4 hours until moisture content drops below 0.1%. PE resin typically skips this step due to low moisture absorption.

Step 2: Extrusion (Filament Formation)

• The dried resin granules are fed into a single-screw extruder, where they are heated to a molten state (temperature varies by material: PE 160–220°C, PP 180–240°C, Nylon 220–260°C).
• The molten polymer is pushed through a spinneret (a metal plate with hundreds of tiny holes, 0.5–2mm in diameter) to form continuous, thin filaments (called "monofilaments").
• The extruded monofilaments are immediately cooled in a water bath (20–40°C) to solidify their shape, preventing deformation and ensuring uniform thickness.

Step 3: Drawing (Strengthening Filaments)

• The cooled monofilaments are pulled through a drawing machine (equipped with heated rollers) at a speed faster than the extrusion speed. This "stretching" process aligns the polymer molecules in the filament, significantly increasing tensile strength (by 2–3x) and reducing elongation (preventing the rope from stretching excessively during use).
• The drawing temperature is controlled (PE 60–80°C, PP 80–100°C, Nylon 120–160°C) to avoid filament breakage while maximizing strength.

Step 4: Twisting (Forming Single Strands)

• Multiple drawn monofilaments (quantity depends on the desired rope thickness, e.g., 20–50 filaments per strand) are gathered into a bundle and fed into a single-strand twisting machine.
• The machine twists the bundle at a controlled speed (500–1,500 twists per meter) to form a tight, uniform "single strand." Twisting direction (S-twist or Z-twist) is pre-determined to ensure compatibility with the final 3-strand twisting step.

Step 5: 3-Strand Twisting (Final Rope Formation)

• Three pre-twisted single strands are loaded onto a 3-strand twisting machine (also called a "rope making machine") with three separate bobbins.
• The machine rotates the three strands in the opposite direction of their individual twists (e.g., if single strands are S-twisted, the final twist is Z-twisted) to create a balanced, stable 3-strand rope. This "counter-twisting" prevents the rope from unraveling and enhances its load-bearing capacity.
• The twisting speed is adjusted based on the rope’s diameter (typically 100–500 rpm) to ensure consistent twist density.

Step 6: Heat Setting (Stabilization)

• The newly twisted rope is passed through a heat-setting oven (temperature: PE 70–90°C, PP 90–110°C, Nylon 120–150°C) for 1–3 minutes. This process relieves internal stress in the polymer structure, reducing "rope memory" (the tendency to untwist) and ensuring dimensional stability—even when exposed to temperature changes or moisture.

Step 7: Winding, Cutting & Quality Inspection

• The heat-set rope is wound onto large spools or reels using an automated winding machine, with tension controlled to avoid stretching or deformation.
• Based on customer requirements, the rope is cut into fixed lengths (e.g., 50m, 100m, 500m) or left as continuous spools.
• Quality Checks: Each batch undergoes testing for:
  • Tensile strength (via a tensile testing machine)
  • Twist uniformity (visual inspection and caliper measurement)
  • Thickness consistency (digital caliper)
  • Abrasion resistance (abrasion tester)
  • Chemical resistance (for PE/PP/Nylon, tested against oils, acids, or alkalis).
  • 

2. Application Scope

2.1 Logistics & Transportation

• Cargo Securement: Used to tie down packages, cartons, or pallets on trucks, trailers, or shipping containers. PP and Nylon variants are preferred for heavy loads (e.g., machinery parts, bulk goods) due to high tensile strength; PE is ideal for lighter packages (e.g., consumer goods, textiles).
• Pallet Wrapping Complement: Works with stretch film to reinforce palletized loads, preventing shifting during transit (especially for uneven or irregularly shaped items).
• Container Fastening: Secures door flaps of shipping containers or covers (e.g., tarps) over open-top trucks, resisting wind and rain damage.

2.2 Warehousing & Storage

• Inventory Organization: Bundles small items (e.g., pipes, rods, boxes) for neat storage, reducing clutter and minimizing damage.
• Shelf Stabilization: Ties down stacked goods on high shelves to prevent tipping, especially in warehouses with frequent forklift movement.
• Temporary Enclosures: Creates temporary barriers or dividers in warehouses to separate different product categories.

2.3 Agriculture & Horticulture

• Crop Support: Nylon and PP ropes (weather-resistant) tie up climbing plants (e.g., tomatoes, grapes, beans) to trellises, ensuring proper growth and preventing stem breakage.
• Baling Small Crops: Bundles hay, straw, or dried herbs for storage or transport (PE rope is cost-effective for this purpose).
• Greenhouse Use: Secures greenhouse films or shade nets to frames, withstanding temperature fluctuations and mild wind loads.

2.4 Construction & Building

• Lightweight Fastening: Ties construction materials (e.g., lumber, pipes, scaffolding accessories) to transport carts or hoists (not for heavy structural loads—reserved for non-critical, temporary fastening).
• Debris Management: Bundles construction waste (e.g., wood scraps, metal pieces) for efficient disposal or recycling.
• Temporary Safety Barriers: Marks off construction zones or hazardous areas when paired with warning tapes.

2.5 Consumer & Household Use

• Moving & Packing: Secures boxes, suitcases, or furniture in moving vans, preventing damage from sliding.
• Outdoor Activities: PE/PP ropes (waterproof) are used for camping (tying tents, hanging gear) or gardening (tying plants, organizing tools). Nylon variants are suitable for lightweight DIY projects (e.g., crafting, hanging decorations).
• Waste Management: Ties trash bags, compost bags, or recycling bundles to prevent spillage.

2.6 Industrial Packaging

• Heavy-Duty Bundling: Secures industrial components (e.g., metal rods, plastic pipes, rubber hoses) during packaging and shipping. PP and Nylon ropes handle higher weights than PE, making them ideal for industrial-grade goods.
• Machinery Protection: Wraps around machinery parts (e.g., gears, valves) to hold protective covers in place during storage or transit, shielding against dust and scratches.

1.PHOTOS

2. Main performance

3.Technology Comparison

Coil length: 220m

Spliced strength:± 10% lower

Weight and length tolerance:± 5%

MBL=Minimum Breaking Load conform ISO 2307

Other sizes available upon request

4.Parameter Table