Huona (Shanghai) New Material Co., Ltd.
| Payment Terms | L/C,T/T,Western Union, |
| Supply Ability | 500 tons per month |
| Delivery Time | 5-21days |
| Packaging Details | Carton/Wooden Case |
| Product Name | AZ31 Magnesium Rod |
| Yield strength (MPa) | 165 |
| Tensile strength, (MPa) | 245 |
| Elongation (percent) | 12 |
| Composition (wt. percent) | Mg: Balance; Al: 2.5-3.5%; Zn: 0.7-1.3%; Mn: 0.2-1.0%; Si: ≤0.08%; Fe: ≤0.005% |
| Thermal Conductivity (25°C) | 156 W/(m·K) |
| Operating Temperature Range | -50°C to 120°C (continuous use) |
| Temper Options | F (as-fabricated), T4 (solution-treated), T6 (solution-treated + aged) |
| Brand Name | Huona |
| Model Number | AZ31 |
| Certification | ISO9001 |
| Place of Origin | Shanghai |
View Detail Information
Explore similar products
Silver Coated Copper Wire for Electronics High Conductivity Stable Signal
Silver Coated Copper Tape for Electrical Shielding & Connections
Thermocouple Type K Mini Size Connector Flat Chromel Alumel Pin Thermometer Plug
To46-06A Optical Communication Sealing Material For Civil Use
Product Specification
| Payment Terms | L/C,T/T,Western Union, | Supply Ability | 500 tons per month |
| Delivery Time | 5-21days | Packaging Details | Carton/Wooden Case |
| Product Name | AZ31 Magnesium Rod | Yield strength (MPa) | 165 |
| Tensile strength, (MPa) | 245 | Elongation (percent) | 12 |
| Composition (wt. percent) | Mg: Balance; Al: 2.5-3.5%; Zn: 0.7-1.3%; Mn: 0.2-1.0%; Si: ≤0.08%; Fe: ≤0.005% | Thermal Conductivity (25°C) | 156 W/(m·K) |
| Operating Temperature Range | -50°C to 120°C (continuous use) | Temper Options | F (as-fabricated), T4 (solution-treated), T6 (solution-treated + aged) |
| Brand Name | Huona | Model Number | AZ31 |
| Certification | ISO9001 | Place of Origin | Shanghai |
| High Light | AZ31 magnesium rod sacrificial anode ，ASTM B80 magnesium rod industrial ，DIN EN 1753 magnesium anode | ||
AZ31 magnesium alloy bar, a flagship product of Huona New Material, is a high-performance wrought magnesium alloy rod engineered for lightweight structural applications. Composed of magnesium (Mg) as the base metal, with aluminum (Al) and zinc (Zn) as key alloying elements, it balances excellent mechanical strength, good ductility, and ultra-low density (only ~1.78 g/cm³--about 35% lighter than aluminum alloys). This combination makes it an ideal alternative to heavier metals in industries prioritizing weight reduction, while Huona's advanced extrusion and heat-treatment processes ensure consistent quality and dimensional precision across all batches.
AZ31 magnesium alloy bar outperforms traditional structural materials in critical lightweight scenarios:
| Attribute | Value (Typical) |
|---|---|
| Chemical Composition (wt%) | Mg: Balance; Al: 2.5-3.5%; Zn: 0.7-1.3%; Mn: 0.2-1.0%; Si: ≤0.08%; Fe: ≤0.005% |
| Diameter Range (Round Bar) | 5mm - 200mm (tolerance: h8/h9 for precision applications) |
| Length | 1000mm - 6000mm (custom cut-to-length available) |
| Temper Options | F (as-fabricated), T4 (solution-treated), T6 (solution-treated + aged) |
| Tensile Strength | F: 220-250 MPa; T4: 240-260 MPa; T6: 260-280 MPa |
| Yield Strength | F: 150-180 MPa; T4: 160-190 MPa; T6: 180-210 MPa |
| Elongation (25°C) | F: 8-12%; T4: 12-15%; T6: 8-10% |
| Hardness (HV) | F: 60-70; T4: 65-75; T6: 75-85 |
| Thermal Conductivity (25°C) | 156 W/(m*K) |
| Operating Temperature Range | -50°C to 120°C (continuous use) |
| Alloy | Temper | Composition (wt. percent) | Tensile properties |
|---|---|---|---|
| AZ31 | F | Al: 3.0 Zn: 1.0 Mn: 0.20 Zr: - |
Yield strength: 165 MPa Tensile strength: 245 MPa Elongation: 12% |
| AZ61 | F | Al: 6.5 Zn: 1.0 Mn: 0.15 Zr: - |
Yield strength: 165 MPa Tensile strength: 280 MPa Elongation: 14% |
| AZ80 | T5 | Al: 8.0 Zn: 0.6 Mn: 0.30 Zr: - |
Yield strength: 275 MPa Tensile strength: 380 MPa Elongation: 7% |
| ZK60 | F | Al: - Zn: 5.5 Mn: - Zr: 0.45 |
Yield strength: 240 MPa Tensile strength: 325 MPa Elongation: 13% |
| ZK60 | T5 | Al: - Zn: 5.5 Mn: - Zr: 0.45 |
Yield strength: 268 MPa Tensile strength: 330 MPa Elongation: 12% |
| AM30 | F | Al: 3.0 Zn: - Mn: 0.40 Zr: - |
Yield strength: 171 MPa Tensile strength: 232 MPa Elongation: 12% |
Huona New Material ensures strict quality control for AZ31 magnesium alloy bars, with each batch undergoing chemical composition analysis, mechanical property testing, and dimensional inspection. Free samples (100mm-300mm lengths) and material test reports (MTR) are available upon request. Our technical team also provides application-specific support--including machining guidelines and corrosion protection recommendations--to help customers maximize the performance of AZ31 in their projects.
Company Details
Business Type:
Manufacturer,Exporter
Year Established:
2008
Total Annual:
8000000-100000000
Employee Number:
100~120
Ecer Certification：
Verified Supplier
Huona (Shanghai) New Material Co., Ltd. Was established in 2008, currently have three divisions: Magnesium Division, Thermal Spray Division and Functional Material Division.Magnesium Division produces magnesium metal products. Various models of high-quality magnesium alloy plate, magnesium rods, hig... Huona (Shanghai) New Material Co., Ltd. Was established in 2008, currently have three divisions: Magnesium Division, Thermal Spray Division and Functional Material Division.Magnesium Division produces magnesium metal products. Various models of high-quality magnesium alloy plate, magnesium rods, hig...