Product Name | CuNi23 Strip |
Thickness Range | 0.01mm - 2.0mm |
Width Range | 5mm - 600mm |
Temper Options | Soft (annealed), Half-hard, Hard (cold-rolled) |
Tensile Strength | Soft: 350-400 MPa; Half-hard: 450-500 MPa; Hard: 550-600 MPa |
Elongation (25°C) | Soft: ≥30%; Half-hard: 15-25%; Hard: ≤10% |
Hardness (HV) | Soft: 90-110; Half-hard: 130-150; Hard: 170-190 |
Resistivity (20°C) | 35-38 μΩ·cm |
Brand Name | Huona |
Model Number | CuNi23 |
Certification | ISO9001 |
Place of Origin | Shanghai |
View Detail Information
Explore similar products
Copper Nickel Zinc Strip C7521 C7701 C7541 Alloy
CuNi44 NC050 Foil High-Performance Nickel-Copper Alloy for Electrical &
CuNi44 Flat Wire (ASTM C71500/DIN CuNi44) Nickel-Copper Alloy for Electrical
Corrosion Resistant Copper Nickel Alloy Wire CuNi23 for Marine Applications
Product Specification
Payment Terms | L/C,T/T,Western Union,MoneyGram | Supply Ability | 500 tons per month |
Delivery Time | 5-21days | Packaging Details | Carton/Wooden Case |
Product Name | CuNi23 Strip | Thickness Range | 0.01mm - 2.0mm |
Width Range | 5mm - 600mm | Temper Options | Soft (annealed), Half-hard, Hard (cold-rolled) |
Tensile Strength | Soft: 350-400 MPa; Half-hard: 450-500 MPa; Hard: 550-600 MPa | Elongation (25°C) | Soft: ≥30%; Half-hard: 15-25%; Hard: ≤10% |
Hardness (HV) | Soft: 90-110; Half-hard: 130-150; Hard: 170-190 | Resistivity (20°C) | 35-38 μΩ·cm |
Brand Name | Huona | Model Number | CuNi23 |
Certification | ISO9001 | Place of Origin | Shanghai |
High Light | CuNi23 nickel copper alloy strip ,NC030 copper nickel alloy for electrical use ,industrial copper nickel alloy strip with warranty |
Attribute | Value (Typical) |
---|---|
Chemical Composition (wt%)
|
Cu: 76-78%; Ni: 22-24%; Fe: ≤0.5%; Mn: ≤0.8%; Si: ≤0.1%; C: ≤0.05%
|
Thickness Range
|
0.01mm - 2.0mm (tolerance: ±0.001mm for ≤0.1mm; ±0.005mm for >0.1mm)
|
Width Range
|
5mm - 600mm (tolerance: ±0.05mm for ≤100mm; ±0.1mm for >100mm)
|
Temper Options
|
Soft (annealed), Half-hard, Hard (cold-rolled)
|
Tensile Strength
|
Soft: 350-400 MPa; Half-hard: 450-500 MPa; Hard: 550-600 MPa
|
Yield Strength
|
Soft: 120-150 MPa; Half-hard: 300-350 MPa; Hard: 450-500 MPa
|
Elongation (25°C)
|
Soft: ≥30%; Half-hard: 15-25%; Hard: ≤10%
|
Hardness (HV)
|
Soft: 90-110; Half-hard: 130-150; Hard: 170-190
|
Resistivity (20°C)
|
35-38 μΩ·cm
|
Thermal Conductivity (20°C)
|
45 W/(m·K)
|
Operating Temperature Range
|
-50°C to 250°C (continuous use)
|
Item | Specification |
---|---|
Surface Finish
|
Bright annealed (Ra ≤0.2μm), matte (Ra ≤0.8μm), or polished (Ra ≤0.1μm)
|
Flatness
|
≤0.05mm/m (for thickness ≤0.5mm); ≤0.1mm/m (for thickness >0.5mm)
|
Machinability
|
Excellent (compatible with CNC cutting, stamping, and bending; minimal tool wear)
|
Weldability
|
Suitable for TIG/MIG welding and soldering (forms strong, corrosion-resistant joints)
|
Packaging
|
Vacuum-sealed in moisture-proof bags with desiccants; wooden spools (for rolls) or cartons (for cut sheets)
|
Customization
|
Slitting to narrow widths (≥5mm), cut-to-length pieces, special tempers, or anti-tarnish coating
|
Company Details
Business Type:
Manufacturer,Exporter
Year Established:
2008
Total Annual:
8000000-100000000
Employee Number:
100~120
Ecer Certification:
Verified Supplier
Huona (Shanghai) New Material Co., Ltd. Was established in 2008, currently have three divisions: Magnesium Division, Thermal Spray Division and Functional Material Division.Magnesium Division produces magnesium metal products. Various models of high-quality magnesium alloy plate, magnesium rods, hig... Huona (Shanghai) New Material Co., Ltd. Was established in 2008, currently have three divisions: Magnesium Division, Thermal Spray Division and Functional Material Division.Magnesium Division produces magnesium metal products. Various models of high-quality magnesium alloy plate, magnesium rods, hig...