| Standard | ASTM B637, AMS 5662, AMS 5663, NACE MR0175 / ISO 15156 |
| Tensile Strength | ≥ 1275 MPa (185 ksi) at Room Temperature |
| Diameter Range | customization |
| Payment Terms | T/T |
| Product Form | Round Bar / Rod |
| Melting Point | 1260-1336°C (2300-2437°F) |
| Elongation | ≥ 12% in 4D |
| Density | 8.19 g/cm³ |
| Hardness | 331-400 HBW (Aged Condition) |
| Condition | Solution Annealed, Aged (Precipitation Hardened), Hot Rolled, Cold Drawn, Forged |
| Surface Finish | Black, Bright, Peeled, Polished, Machined |
| Application | Gas Turbine Blades, Aerospace Engine Shafts, Nuclear Reactor Components, Oil and Gas Downhole Tools |
| Supply Ability | 50000 Kilograms per Month |
| Delivery Time | 7 working days for stock, 15-30 days for production |
| Length | Custom Cut Available |
| Packaging Details | wooden case |
| Material Grade | Inconel 718 (UNS N07718 / 2.4668) |
| Yield Strength (0.2% Offset) | ≥ 1034 MPa (150 ksi) at Room Temperature |
| Certification | ISO 9001:2015, ASTM B637, AMS 5662, NACE MR0175 |
| Model Number | IN718-RB |
| Place of Origin | Shanghai, China |
| Brand Name | ECER |
View Detail Information
Explore similar products
Diameter 1.2mm Inconel 600 Welding Wire
815 MPA Lncoloy 925 UNS N09925 Corrosion Strip Alloy
Polish Surface Nickel Alloy Inconel 600 Round Bar
150mm Thickness Heat Corrosion Alloy 600 Round Bar Inconel 600 Tubing
Product Specification
| Standard | ASTM B637, AMS 5662, AMS 5663, NACE MR0175 / ISO 15156 | Tensile Strength | ≥ 1275 MPa (185 ksi) at Room Temperature |
| Diameter Range | customization | Payment Terms | T/T |
| Product Form | Round Bar / Rod | Melting Point | 1260-1336°C (2300-2437°F) |
| Elongation | ≥ 12% in 4D | Density | 8.19 g/cm³ |
| Hardness | 331-400 HBW (Aged Condition) | Condition | Solution Annealed, Aged (Precipitation Hardened), Hot Rolled, Cold Drawn, Forged |
| Surface Finish | Black, Bright, Peeled, Polished, Machined | Application | Gas Turbine Blades, Aerospace Engine Shafts, Nuclear Reactor Components, Oil and Gas Downhole Tools |
| Supply Ability | 50000 Kilograms per Month | Delivery Time | 7 working days for stock, 15-30 days for production |
| Length | Custom Cut Available | Packaging Details | wooden case |
| Material Grade | Inconel 718 (UNS N07718 / 2.4668) | Yield Strength (0.2% Offset) | ≥ 1034 MPa (150 ksi) at Room Temperature |
| Certification | ISO 9001:2015, ASTM B637, AMS 5662, NACE MR0175 | Model Number | IN718-RB |
| Place of Origin | Shanghai, China | Brand Name | ECER |
| High Light | AMS 5662 ASTM B637 Certified ，Solution Annealed Aged Condition ，Aerospace Turbine Engine Grade | ||
| Condition | Description | Typical Hardness |
|---|---|---|
| Solution Annealed | Heated to 927-1010°C, air cooled or faster. Optimal for subsequent machining and forming. | 240-300 HBW |
| Aged (Precipitation Hardened) | Solution annealed + 718°C/8h furnace cool to 621°C + 621°C/8h air cool. Maximum strength condition per AMS 5662. | 331-400 HBW |
| Hot Rolled | Rolled above recrystallization temperature. Suitable for general structural applications. | As rolled |
| Cold Drawn | Drawn at room temperature for enhanced surface finish and dimensional tolerance (h9/h10). | Work hardened |
| Element | Ni | Cr | Fe | Nb+Ta | Mo | Ti | Al | Co | C |
|---|---|---|---|---|---|---|---|---|---|
| Spec | 50.0-55.0 | 17.0-21.0 | Balance | 4.75-5.50 | 2.80-3.30 | 0.65-1.15 | 0.20-0.80 | ≤1.0 | ≤0.08 |
| Property | Minimum Value | Typical Value |
|---|---|---|
| Tensile Strength | 1275 MPa (185 ksi) | 1380 MPa (200 ksi) |
| Yield Strength (0.2% Offset) | 1034 MPa (150 ksi) | 1138 MPa (165 ksi) |
| Elongation in 4D | 12% | 18% |
| Reduction of Area | 15% | 25% |
| Hardness | 331 HBW | 370 HBW |
Company Details
Business Type:
Manufacturer,Exporter
Year Established:
2008
Total Annual:
8000000-100000000
Employee Number:
100~120
Ecer Certification：
Verified Supplier
Huona (Shanghai) New Material Co., Ltd. Was established in 2008, currently have three divisions: Magnesium Division, Thermal Spray Division and Functional Material Division.Magnesium Division produces magnesium metal products. Various models of high-quality magnesium alloy plate, magnesium rods, hig... Huona (Shanghai) New Material Co., Ltd. Was established in 2008, currently have three divisions: Magnesium Division, Thermal Spray Division and Functional Material Division.Magnesium Division produces magnesium metal products. Various models of high-quality magnesium alloy plate, magnesium rods, hig...
Get in touch with us
Leave a Message, we will call you back quickly!