| Packaging Details | 1kg,5kg,10kg,20kg |
| Delivery Time | 7-10days |
| Payment Terms | T/T,LC |
| Supply Ability | 100000kgs/month |
| Color | Blue |
| Fineness | ≤8µm |
| Mix ratio | Base/Hardener=3:1 |
| Solid content after mixing | 75±3% |
| Viscosity after mixing (25℃) | 200±30 dPa﹒s |
| Density after mixing (25℃) | 1.30 ~1.50 g/ml |
| Pot life after mixing | 24 hour |
| Environment standard | In compliance with RoHS directives |
| Halogen content | ≤600ppm |
| Pre-baking limit | 75℃ , 70 min |
| Exposure energy | 300 ~600 mJ/cm2 |
| Shelf life | 6 months since the date of manufacture |
| Place of Origin | China |
| Brand Name | NUOJINSEN |
| Certification | ROHS,SGS |
| Model Number | 1801 |
View Detail Information
Explore similar products
Self Dry UV Curable Solder Mask , Anti Alkai Etching And Plating Resist Ink
Blue White Liquid Photoimageable Solder Mask , PCB Printing Ink For Multilayer
Liquid Photosensitive Solder Mask Etch Resist Red Solder Mask
Self Dry UV Curable Solder Mask , Anti Alkai Etching And Plating Resist Ink
Product Specification
| Packaging Details | 1kg,5kg,10kg,20kg | Delivery Time | 7-10days |
| Payment Terms | T/T,LC | Supply Ability | 100000kgs/month |
| Color | Blue | Fineness | ≤8µm |
| Mix ratio | Base/Hardener=3:1 | Solid content after mixing | 75±3% |
| Viscosity after mixing (25℃) | 200±30 dPa﹒s | Density after mixing (25℃) | 1.30 ~1.50 g/ml |
| Pot life after mixing | 24 hour | Environment standard | In compliance with RoHS directives |
| Halogen content | ≤600ppm | Pre-baking limit | 75℃ , 70 min |
| Exposure energy | 300 ~600 mJ/cm2 | Shelf life | 6 months since the date of manufacture |
| Place of Origin | China | Brand Name | NUOJINSEN |
| Certification | ROHS,SGS | Model Number | 1801 |
| High Light | solder resist ink ，white solder mask | ||
Blue color pcb printing use,photo image curing,pcb ink with hardener
| Items | Technical features | Notes |
| Color | Blue | |
| Viscosity (25℃) | 10±2dPa﹒s | VT-04F |
| Fineness | ≤5µm | 0 ~25µm Fineness gauge |
| Solid content | 50±5% | |
| Density (25℃) | 1.10 ~1.20 g/ml | |
| Resolution | 50µm (2.0mil) | |
| Adhesion | 100/100 | Laceration experiment |
| Plating resistance | Copper ,Tin ,Nickle and Aurum | Normal plating technics |
| Hardness | ≥2H | Pencil harder |
| Etching | Acidic/Alkaline etching solution | |
| Pre-baking limit | 75℃, 60min | |
| Package | 5.0kg/bucket , 20kg/box | According to customer requirements |
| Shelf time | 6 months since the date of manufacture | Store below 25℃ in dark |
Working procedure
1. Mixing
Mixing a small amount main agent with hardener and stirring thoroughly,then mixing the mixture above with the remanent main agent,add appropriate diluent and stirring 5-10 minutes. The viscosity of ink is adjusted to 120 PS if printed by hand. And it is adjusted to 180 PS if printed by machine.It is adjusted to 200 PS if it is aluminum tamponade .The viscosity of ink mixed above is measured at 25 degrees. Please use the special diluent of our company if the viscosity of ink needs to adjust.
10-15 minutes after stiring uniformly
1) Single side printing separately
First side:72-76 degrees,15-18 min
Second side:72-76 degrees,30-35 min
300-500mJ/cm2,Black ink:600-750mJ/cm2,exposure step:10-12 steps
Developing solution:0.8-1.2wt% Na2CO3 or K2CO3 aqueous solution
Developing solution temperature:28-32 degrees
Spray pressure:1.5-2.5kg/cm2
Developing time:40-90 seconds
Spray Tin board:150 degrees*(60-120min)
Chemical-plating Aurum board:150 degrees*(50-60min)
Thick copper plate,boards printed with black ink should be post-black in subsection:75 degrees*(60-120min)+100 degrees*30 min+150 degrees*(60-90min)
6 months since the date of manufacture,store below 25 degree in dark
1) Mixing the ink fully before using
2) We will offer you special diluent or PMA if the ink need dilute
3) The values above are based on experiments in our lab.Experiments need to be carried out in order to get proper using condition.
Company Details
Business Type:
Manufacturer,Importer,Exporter,Trading Company,Seller
Year Established:
2011
Total Annual:
5000000-6000000
Employee Number:
50~100
Ecer Certification：
Active Member
Hubei Nuojinsen Technology Co.,Ltd ,after years of unremitting efforts，Combined with foreign advanced technology and process,Production of PCB ink has reached the technical level, conforms to the requirement of RoHS environmental protection directive, with excellent quality and excellent service i... Hubei Nuojinsen Technology Co.,Ltd ,after years of unremitting efforts，Combined with foreign advanced technology and process,Production of PCB ink has reached the technical level, conforms to the requirement of RoHS environmental protection directive, with excellent quality and excellent service i...
Get in touch with us
Leave a Message, we will call you back quickly!