TORICH INTERNATIONAL LIMITED
| Payment Terms | D/A, L/C, D/P, T/T, Western Union, MoneyGram |
| Supply Ability | 60000Ton Per Year |
| Delivery Time | 30 Work days |
| Packaging Details | packing in wooden boxes or in hexagonal bundles |
| Product name | GB9948 10#20# 12CrMo 15CrMo 12Cr1MoV 07Cr19Ni10 Petroleum Cracking Seamless Steel Tubes |
| Standard | GB EN ASTM JIS DIN |
| Surface | oiled |
| Material | 10#20#12CrMo15CrMo12Cr5Mo-NT022Cr17Ni12Mo2 |
| Usage | Petroleum Cracking |
| Shape | Round |
| OD | 5-600mm |
| WT | 0.5-50mm |
| Brand Name | Torich |
| Model Number | GB 9948 |
| Certification | ISO9001:2008,ISO14001:2008 |
| Place of Origin | Zhejiang,China |
View Detail Information
Explore similar products
JIS G4105 SCM440 Alloy Steel Seamless Pipes for High Temperature Applications
ASTM A501 Gr.A Gr.B Seamless Carbon Steel Tube for Construction
ASTM A501 Seamless Carbon Steel Tube for Construction
20MnG High Pressure Boiler Tube Alloy Seamless Pipe For Boilers Heat Exchangers
Product Specification
| Payment Terms | D/A, L/C, D/P, T/T, Western Union, MoneyGram | Supply Ability | 60000Ton Per Year |
| Delivery Time | 30 Work days | Packaging Details | packing in wooden boxes or in hexagonal bundles |
| Product name | GB9948 10#20# 12CrMo 15CrMo 12Cr1MoV 07Cr19Ni10 Petroleum Cracking Seamless Steel Tubes | Standard | GB EN ASTM JIS DIN |
| Surface | oiled | Material | 10#20#12CrMo15CrMo12Cr5Mo-NT022Cr17Ni12Mo2 |
| Usage | Petroleum Cracking | Shape | Round |
| OD | 5-600mm | WT | 0.5-50mm |
| Brand Name | Torich | Model Number | GB 9948 |
| Certification | ISO9001:2008,ISO14001:2008 | Place of Origin | Zhejiang,China |
| High Light | seamless steel pipe ，precision stainless steel tubing | ||
Product name: GB 9948 Material10#20# 12CrMo 15CrMo 12Cr1MoV Petroleum Cracking Seamless Steel Tubes
Out Diameter: 3~500mm
Wall Thickness: 0.5~50mm
Application: It is used for the seamless steel tubes for furnace,heat exchangers, Petroleum Cracking etc.
Table1 The Tolerances of Outer Diameter and Wall Thickness Unit:mm
| Sort Code | Manufacuring Method | Nominal Size | Tolerances | ||
| Common Level | High Level | ||||
| W-H | Hot Rolling (Extrusion) | Outer Diameter D | ≤54 | ±0.50 | ±0.30 |
| ＞54~325 | ±1%D | ±0.75%D | |||
| ＞325 | ±1%D | - | |||
| Wall Thicknass S | ≤20 | +15%S -10%S | ±10%S | ||
| ＞20 | +12.5%S -10%S | ±10%S | |||
| Hot Expand | Outer Diameter D | All | ±1%D | ||
| Wall Thicknass S | All | ±15%S | |||
| W-C | Cold Drawn(Rolling) | Outer Diameter D | ≤25.4 | ±0.15 | |
| ＞25.4~40 | ±0.20 | ||||
| ＞40~50 | ±0.25 | ||||
| ＞50~60 | ±0.30 | ||||
| ＞60 | ±0.75%D | ±0.5%D | |||
| Wall Thicknass S | ≤3.0 | ±0.3 | ±0.2 | ||
| ＞3.0 | ±10%S | ±7.5%S | |||
Table2 The Tolerance of Minimum Wall Thickness Unit :mm
| Sort Code | Manufacturing Method | Minimum Wall Thickness Smin | Tolerance | |
| Common Level | High Level | |||
| W-H | Hot Rolling(Extrusion) | ≤4.0 | +0.90 0 | +0.70 0 |
| ＞4.0 | +25%Smin 0 | +22%Smin 0 | ||
| W-C | Cold Drawn(Rolling) | ≤3.0 | +0.6 0 | +0.4 0 |
| ＞3.0 | +20%Smin 0 | +15%Smin 0 | ||
Table3 Steel grade and chemical composition
| Steel grade | Chemical composition % | |||||||||||
| C | Si | Mn | Cr | Mo | Ni | Nb | Ti | V | Cu | P | S | |
| ≤ | ||||||||||||
| 10 | 0.07~ 0.13 | 0.17~ 0.37 | 0.35~ 0.65 | ≤0.15 | ≤0.15 | ≤ 0.25 | — | — | ≤0.08 | ≤0.20 | 0.025 | 0.015 |
| 20 | 0.17~ 0.23 | 0.17~ 0.37 | 0.35~ 0.65 | ≤0.25 | ≤0.15 | ≤ 0.25 | — | — | ≤0.08 | ≤0.20 | 0.025 | 0.015 |
| 12CrMo | 0.08~ 0.15 | 0.17~ 0.37 | 0.40~ 0.70 | 0.40~ 0.70 | 0.40~ 0.55 | ≤ 0.30 | — | — | — | ≤0.20 | 0.025 | 0.015 |
| 15CrMo | 0.12~ 0.018 | 0.17~ 0.37 | 0.40~ 0.70 | 0.80~ 1.10 | 0.40~ 0.55 | ≤ 0.30 | — | — | — | ≤0.20 | 0.025 | 0.015 |
| 12CrlMo | 0.08~ 0.15 | 0.50~ 1.00 | 0.30~ 0.60 | 1.00~ 1.50 | 0.45~ 0.65 | ≤ 0.30 | — | — | — | ≤0.20 | 0.025 | 0.015 |
| 12CrlMoV | 0.08~ 0.15 | 0.17~ 0.37 | 0.40~ 0.70 | 0.90~ 1.20 | 0.25~ 0.35 | ≤ 0.30 | — | — | 0.15~ 0.30 | ≤0.20 | 0.025 | 0.015 |
| 12Cr2Mo | 0.08~ 0.15 | ≤0.50 | 0.40~ 0.60 | 2.00~ 2.50 | 0.90~ 1.13 | ≤ 0.30 | — | — | — | ≤0.20 | 0.025 | 0.015 |
| 12Cr5MoI 12Cr5MoNT | ≤ 0.15 | ≤0.50 | 0.30~ 0.60 | 4.00~ 6.00 | 0.45~ 0.60 | ≤ 0.60 | — | — | — | ≤0.20 | 0.025 | 0.015 |
| 12Cr9MoI 12Cr9MoNT | ≤ 0.15 | 0.25~ 1.00 | 0.30~ 0.60 | 8.00~ 10.00 | 0.90~ 1.10 | ≤ 0.60 | — | — | — | ≤0.20 | 0.025 | 0.015 |
| 07Cr19Ni10 | 0.04~ 0.10 | ≤ 1.00 | ≤2.00 | 18.00~ 20.00 | — | 8.00~ 11.00 | — | — | — | — | 0.030 | 0.015 |
| 07Cr18Ni11Nb | 0.04~ 0.10 | ≤ 1.00 | ≤2.00 | 17.00~ 19.00 | — | 9.00~ 12.00 | 8C~ 1.10 | — | — | — | 0.030 | 0.015 |
| 07Cr19Ni11NTi | 0.04~ 0.10 | ≤0.75 | ≤2.00 | 17.00~ 20.00 | — | 9.00~ 13.00 | — | 4C~ 0.60 | — | — | 0.030 | 0.015 |
| 022Cr17Ni12Mo2 | ≤ 0.30 | ≤1.00 | ≤2.00 | 16.00~ 18.00 | 2.00~ 3.00 | 10.00~ 14.00 | — | — | — | — | 0.030 | 0.015 |
Table4 Heat Treatment Standard
| Steel Grade | Heat Treatment Standard |
| 10a | Normalizing；At Temperature 880℃~940℃ |
| 20a | Normalizing:At Temperature 880℃~940℃ |
| 12CrMob | Normalizing:At Temperature 900℃~960℃ Tempering:At Temperature 670℃~730℃ |
| 15CrMob | Normalizing:At Temperature 900℃~960℃ Tempering:At Temperature 680℃~730℃ |
| 12Cr1Mob | Normalizing:At Temperature 900℃~960℃ Tempering:At Temperature 680℃~750℃ |
| 12Cr1MoVb | S≤30mm:Normalizing:At Temperature 980℃~1020℃ Tempering:At Temperature 720℃~760℃ S＞30mm:Quenching:At Temperature 950℃~990℃ Tempering:At Temperature 720℃~760℃ Or Normalizing:At Temperature 980℃~1020℃ (rapid cooling after Normalizing) Tempering:At Temperature 720℃~760℃ |
| 12Cr2Mob | S≤30mm:Normalizing:At Temperature 900℃~960℃ Tempering:At Temperature 700℃~750℃ S＞30mm:Quenching:At Temperature ≥ 900℃ Tempering:At Temperature 700℃~750℃ Or Normalizing:At Temperature 900℃~960℃ (rapid cooling after Normalizing) Tempering:At Temperature 700℃~750℃ |
| 12Cr5MoI | Full Annealing or isothermal annealing |
| 12Cr5MoNT | Normalizing:At Temperature 930℃~980℃ Tempering:At Temperature 730℃~770℃ |
| 12Cr9MoI | Full Annealing or isothermal annealing |
| 12Cr9MoNT | Normalizing:At Temperature 890℃~950℃ Tempering:At Temperature 720℃~800℃ |
| 07Cr19Ni10 | Treatment with solid solving:At Temperature ≥ 1040℃ (rapid cooling after Treatment)
|
| 07Cr18Ni11Nb | Treatment with solid solving: For Hot Rolled Tube At Temperature ≥ 1050℃ For Cold Drawn(rolled)Tube At Temperature ≥ 1100℃ (rapid cooling after Treatment)
|
| 07Cr19Ni11Ti | Treatment with solid solving: For Hot Rolled Tube At Temperature ≥ 1050℃ For Cold Drawn(rolled)Tube At Temperature ≥ 1100℃ (rapid cooling after Treatment)
|
Table5 Mechanical Property
| Steel Grade | Tensile Strength Rm/MPa | Lower yield strength Rp0.2/MPa | Elongation A/％ | Shock absorption KV2/J | Brinell hardness | ||
| Longitudinal direction | Transverse | Longitudinal direction | Transverse | ||||
| ≥ | ≤ | ||||||
| 10 | 335~475 | 205 | 25 | 23 | 40 | 27 | - |
| 20 | 410~550 | 245 | 24 | 22 | 40 | 27 | - |
| 12CrMo | 410~560 | 205 | 21 | 19 | 40 | 27 | 156HBW |
| 15CrMo | 440~640 | 295 | 21 | 19 | 40 | 27 | 170HBW |
| 12Cr1Mo | 415~560 | 205 | 22 | 20 | 40 | 27 | 163HBW |
| 12Cr2MoV | 470~640 | 255 | 21 | 19 | 40 | 27 | 179HBW |
| 12Cr2Mo | 450~600 | 280 | 22 | 20 | 40 | 27 | 163HBW |
| 12Cr5MoI | 415~590 | 205 | 22 | 20 | 40 | 27 | 163HBW |
| 12Cr5MoNT | 480~640 | 280 | 20 | 18 | 40 | 27 | - |
| 12Cr9MoI | 460~640 | 210 | 20 | 18 | 40 | 27 | 179HBW |
| 12Cr9MoNT | 590~740 | 390 | 18 | 16 | 40 | 27 | - |
| 07Cr19Ni10 | ≥520 | 205 | 35 | - | - | 187HBW | |
| 07Cr18Ni11Nb | ≥520 | 205 | 35 | - | - | 187HBW | |
| 07Cr19Ni11Ti | ≥520 | 205 | 35 | - | - | 187HBW | |
| 022Cr17Ni12Mo2 | ≥485 | 170 | 35 | - | - | 187HBW | |
| If the wall thickness of the tube is less than 5mm, doesn’t have to do the hardness test | |||||||
Table6 Impact energy absorption attenuation factor of small sample
| Specimen | Specimen size(heightXwidth)mm | Attenuation factor |
| Standard sample | 10X10 | 1.00 |
| Small sample | 10X7.5 | 0.75 |
| Small sample | 10X5 | 0.50 |
Table7 Diameter flaring rate of steel tubes
| Steel | Diameter flaring rate of steel tubes/% | ||
| ID/OD | |||
| ≤0.6 | ＞0.6~0.8 | ＞0.8 | |
| Carbon structural steel | 10 | 12 | 17 |
| Alloy structural steel | 8 | 10 | 15 |
| Stainless(heat resistance)steel | 12 | 15 | 20 |
Table8 Testing items and sampling quantity of steel tubes
| Number | Testing items | Sampling quantity |
| 1 | Chemical composition | 1 sample from each furnace |
| 2 | Tensile test | 1 sample from each of two steel tubes on each batch |
| 3 | Hardness test | 3 samples taken on 2 steel tubes on each batch |
| 4 | Impact test | All |
| 5 | Hydraulic test | 1 sample from each of two steel tubes on each batch |
| 6 | Flattening test | 2 samples taken on 2 steel tubes on each batch |
| 7 | Bending test | 1 sample taken on 2 steel tubes on each furnace |
| 8 | Flaring test | 2 samples taken on 2 steel tubes on each batch |
| 9 | Macroscopic examination | 1 sample taken on 2 steel tubes on each furnace |
| 10 | Non-metallic inclusions | 1 sample taken on 2 steel tubes on each furnace |
| 11 | Eddy current testing | All |
| 12 | Magnetic flux leakage detection | All |
| 13 | Ultrasonic testing | All |
| 14 | Intergranular corrosion test | 1 sample from each of two steel tubes on each batch |
Table A.1 Comparison Table of Similar Steel Grade
| No. | GB | Similar Steel Grade | |||
| ISO | EN | ASTM/ASME | JIS | ||
| 1 | 10 | - | P195GH | A | STB 340 |
| 2 | 20 | PH26 | P235GH | A-1,B | STB 410 |
| 3 | 12CrMo | - | - | T2/P2 | STBA 20 |
| 4 | 15CrMo | 13CrMo4-5 | 13CrMo4-5 | T12/P12 | STBA 22 |
| 5 | 12Cr1Mo | - | 10CrMo5-5 | T11/P11 | STBA 23 |
| 6 | 12Cr1MoV | - | - | - | - |
| 7 | 12Cr2Mo | 10CrMo9-10 | 10CrMo9-10 | T22/P22 | STBA 24 |
| 8 | 12Cr5Mo-I | X11CrMo9-1TA | X11CrMo5+I | T5/P5 | STBA 25 |
| 9 | 12Cr5Mo-NT | - | X11CrMo5+NT | T5/P5 | STBA 25 |
| 10 | 12Cr9Mo-I | X11CrMo9-1TA | X11CrMo9-1+I | T9/P9 | STBA 26 |
| 11 | 12Cr9Mo-NT | - | X11CrMo9-1+NT | T9/P9 | STBA 26 |
| 12 | 07Cr19Ni10 | X7CrNi18-9 | X6CrNi18-10 | TP304H | SUS 304H TB |
| 13 | 07Cr18Ni11Nb | X7CrNiNb18-10 | X7CrNiNb18-10 | TP347H | SUS 347H TB |
| 14 | 07Cr19Ni11Ti | - | X6CrNiTi18-10 | TP321H | SUS 321H TB |
| 15 | 022Cr17Ni12Mo2 | - | X2CrNiMo17-12-2 | TP316L | SUS 316L TB |
Company Details
Business Type:
Manufacturer,Distributor/Wholesaler,Importer,Exporter,Trading Company,Seller
Year Established:
1997
Total Annual:
25000000-30000000
Employee Number:
100~200
Ecer Certification：
Verified Supplier
#torich-about-brief, #torich-about-brief * { box-sizing: border-box; } #torich-about-brief { --torich-red: #d71920; --torich-dark: #222a31; --torich-text: #4f5962; --torich-muted: #77818a; --torich-line: #e7eaed; --torich-soft: #f6f7f8; width: 100%; color: var(--torich-text); ... #torich-about-brief, #torich-about-brief * { box-sizing: border-box; } #torich-about-brief { --torich-red: #d71920; --torich-dark: #222a31; --torich-text: #4f5962; --torich-muted: #77818a; --torich-line: #e7eaed; --torich-soft: #f6f7f8; width: 100%; color: var(--torich-text); ...
Get in touch with us
Leave a Message, we will call you back quickly!