WUXI WANLI ADHESION MATERIALS CO., LTD.
Products
Manufacturer of a wide range of products which include Ivory Solid Hot Melt Glue For Woodworking Aluminum Polyurethane Glue Sticks PUR,Yellow Block Woodworking Hot Melt Adhesive PSA Industrial TPR-2005AC,Distinctive 2KPU-802 Polyu...
MOQ: 20 KG
Price:
| Payment Terms | L/C, T/T |
| Delivery Time | 5-8 work days |
| Packaging Details | 500~2000g/Bag, 20Kg/Barrel, 200Kg/Barrel |
| Product | PUR Hot Melt Adhesive |
| Component | Polyurethane(PUR) |
| Appearance | Ivory Solid |
| Solid Content | 100% |
| Shelf Life | 6·Months |
| Melt Viscosity | About 75000mPa·s at 120℃ |
| Operating Temperature | 120~140℃ |
| Open Time | 8~15s at 25℃ |
| Useage Scope | Edge Bonding of Wood Material s- Chip Board |
| Application Industry | Woodworking Edgebanding |
| Brand Name | WANLI-ADHESION |
| Model Number | PUR-7562.1 |
| Certification | ISO9001 ISO14001 IATF16949 |
| Place of Origin | CHINA |
MOQ: 20 KG
Price:
| Payment Terms | L/C, T/T |
| Delivery Time | 5-8 work days |
| Packaging Details | 20Kg/Carton |
| Product | PSA Hot Melt Adhesive |
| Component | TPR |
| Appearance | Yellow Block |
| Solid Content | 100% |
| Shelf Life | 12 Months |
| Melt Viscosity | Around 12500mpa·s (@160℃) |
| Softening Temperature | Around 100℃ |
| Operating Temperature | 150℃～180℃ |
| Peeling @180˚ | About 27.0N/2.5cm*45μm on Stainless Steel Plate |
| Lasting Adhesive | ≥72 Hours |
| Usage Scope | Floor Mute Pad Flat Lamination Bonding |
| Application Industry | PSA Hot Melt Glue for Woodworking Flat Lamination Bonding |
| Brand Name | WANLI-ADHESION |
| Model Number | TPR-2005AC |
| Certification | ISO9001 ISO14001 IATF16949 |
| Place of Origin | CHINA |
MOQ: 18KG
Price: Negotiation
| Payment Terms | L/C, T/T |
| Supply Ability | 10000KGS/week |
| Delivery Time | 5-8 work days |
| Packaging Details | 18/18kg Barrel |
| Appearance | A: Dark amber liquid/B: Light to colorless liquid |
| Density | A: 0.97(g/cm3)/B: 1.13(g/cm3) |
| Smell | Distinctive |
| Solid Content | 100% |
| Viscosity | A: 1600±300(mPa.s)/B:200±100(mPa.s) |
| Weight Mixing Ratio | A: 100/B: 100 |
| Mixed Viscosity | 400-700 (mPa.s) |
| Application Period | 4~6(minutes) |
| Hardness | 90-99 (Shore A) |
| Shear Strength | ABS: 2.22 (MPa), UPVC: 2.72 (MPa) |
| Application temperature | 25℃-30℃ |
| Brand Name | WANLI-ADHESION |
| Model Number | 2KPU-802 |
| Certification | ISO9001 ISO14001 IATF16949 |
| Place of Origin | CHINA |
MOQ: 400 ml
Price:
| Payment Terms | L/C, T/T |
| Delivery Time | 5-8 work days |
| Packaging Details | 400 ml/Tube, 23L/Barrel, 195L/Barrel |
| performance | Component A: UH®-3005 A/ Component B:UH®-3005 B |
| Fundamentals of Chemistry | Component A: Polyol/ Component B: Isocyanate |
| colour(Before mixing） | Component A: black / Component B: canary yellow |
| colour(After mixing） | black |
| Curing mechanism | Addition polymerization |
| Density（ kg/l）(Before mixing） | Component A: 1.44 / Component B: 1.33 |
| Density（ kg/l）(After mixing） | 1.385 |
| Mixing ratio (A: B volume ratio) | 100 : 100 |
| Mixing ratio (A: B weight ratio) | 100 : 92.5 |
| Viscosity (brookfleld 7# rotor 10rpm25 ℃) | Component A: about 30000CPS / Component B: about 20000CPS |
| Applicable period (min) | 35A |
| Shore D hardness (ASTM D2240) | 60 |
| Tensile strength (ASTM D638 MPa) | 10 |
| Thermal conductivity (ASTM e1461 w/ (m · K)) | 0.5 |
| Elongation at break (ASTM D638) | 5-10 % |
| Shear strength (ASTM d1002 aluminum 3003- aluminum 3003 MPa) | 14.6 |
| working temperature | -40 – 80 °C |
| Brand Name | WANLI-ADHESION |
| Model Number | UH®-3005 |
| Certification | ISO9001 ISO14001 IATF16949 |
| Place of Origin | CHINA |