D700mm JS700 Aluminum casting impregnation Vacuum Impregnation Plant

Product Specification

D700mm JS700 Aluminum casting impregnation Vacuum Impregnation Plant 

Introduction
Vacuum impregnation is a specialized process used to eliminate porosity and leakage in aluminum castings. This technique involves pressurizing a resin into the pores of the casting and curing it to create a permanent, leak-proof seal. The process is widely used across industries such as automotive, electronics, aerospace, and defense to improve the integrity and performance of aluminum castings. The vacuum impregnation plant includes several key stages, each designed to ensure optimal sealing and minimal resin wastage.

Overall Impregnation Process

1. Hot Water Washing Tank
   The hot water washing tank utilizes water heated to 60-65°C to effectively remove surface contaminants from aluminum castings. This step prepares the parts for subsequent drying and impregnation.

2. Vacuum Drying Tank
   The vacuum drying tank ensures efficient moisture removal from the castings using low energy. The drying process typically lasts for at least 10 minutes, making it ideal for removing any residual moisture before impregnation.

3. Vacuum Impregnation Tank
   This tank uses both dry and wet vacuum processes to impregnate the castings with resin. The vacuum pressure reaches -0.098 to -0.100 Mpa, and the basket can move up and down automatically with a speed of 10-15 seconds per cycle. The impregnation tank is integrated with both the impregnation and resin storage systems.

4. Resin Removal Tank
   After the impregnation process, excess resin is removed using centrifugal force. The basket undergoes a 90° rotation to ensure all sides of the casting are treated, which is particularly useful for deep or blind holes in the parts.

5. Cold Wash Tank
   The cold wash tank is equipped with rotating nozzles that spray clean water onto the castings. This ensures that the parts are thoroughly rinsed after the resin removal process.

6. Hot Curing Tank
   The hot curing tank uses steam suction to control steam accumulation in the workshop. The castings are cured at a temperature of 90-93°C for 15 minutes to ensure the resin hardens, providing a durable and leak-proof seal.

Pretreatment Line

1. Hot Water Rotation Cleaning Tank
   Preheating and chemical residue removal are conducted in this tank, where hot water (60-70°C) is used to clean the products. The rotation mechanism enhances the removal of water from deep holes, improving drying efficiency for the next step.

Vacuum Impregnation Line

1. Vacuum Impregnation Tank
   This critical tank applies a dry vacuum followed by a wet vacuum to impregnate the aluminum castings. The process ensures uniform resin infiltration into the castings.

   • Key Features:

     • Vacuum degree: -0.098 Mpa

     • Up-down movement speed: 10-15 seconds

     • Temperature control: Resin temperature maintained between 0°C and 28°C

     • Observation window: Enables operators to monitor the impregnation process

2. Rotation Resin Removal Tank
   The resin removal tank uses centrifugal force to remove excess resin from the castings. The tank rotates both clockwise and anticlockwise, ensuring all surfaces of the casting are treated. The rotation speed is adjustable, and the resin is automatically returned to the impregnation tank for recycling.

   • Key Features:

     • Rotation speed: Adjustable from 0 to 10 rpm

     • Rotation time: 5-7 minutes for clockwise and anticlockwise rotation

     • Material: SUS304 stainless steel

3. Cold Wash Tank
   After resin removal, castings are transferred to the cold wash tank, where clean water is sprayed to remove any remaining impurities. The rotating nozzle ensures thorough cleaning.

4. Hot Water Curing Tank
   The hot water curing tank provides controlled curing at 90-93°C for 15 minutes. This curing step ensures that the resin fully hardens, providing a leak-proof finish.

Detailed Technical Parameters

Advantages of Vacuum Impregnation for Aluminum Castings

• Leak-proof Performance: The vacuum impregnation process effectively seals porous aluminum castings, ensuring they are resistant to leakage and suitable for high-pressure applications.

• Efficient Resin Use: With the advanced resin removal system, the process minimizes resin wastage and optimizes the material cost.

• Enhanced Durability: The resin curing process improves the mechanical properties of the castings, making them more durable and resistant to wear and corrosion.

• Fully Automated Process: The PLC-controlled system allows for automatic operation, ensuring precision, consistency, and reduced labor costs.

• Environmentally Friendly: The closed-loop resin system and efficient drying process reduce environmental impact by minimizing waste and energy consumption.

Conclusion

The vacuum impregnation plant for aluminum castings ensures high-quality, leak-proof products by effectively sealing porous areas through an optimized multi-stage process. With advanced features such as centrifugal resin removal, precise temperature control, and fully automated operation, this system provides a comprehensive solution for industries requiring durable aluminum castings. The plant's efficiency, reduced material waste, and energy-saving processes make it a valuable investment for companies looking to meet stringent quality standards while maintaining operational efficiency.