Standard | AMS 5513 |
Grade | 304 , 304L |
Thickness | 0.15mm-4mm for cold rolled |
Width | 4.6-1200mm |
Technique | Cold Rolled ,hot rolled |
Application | Construction,Industry,Tube,decoration,Automotive |
Condition | Annealed ,2B |
Forms | strip ,foil ,wire , plate ,sheet |
Product name | stainless steel strip |
Edge | slit edge ,round edge ,Deburred edge |
Brand Name | xinzheng |
Model Number | Stainless steel strip |
Certification | ISO, EN, MTC |
Place of Origin | CHINA |
View Detail Information
Explore similar products
Astm 301 1/2 Hard Tempered 2B Surface Stainless Steel Strap Coil For Automobile
Astm A240 AISI 201 Stainless Steel Strip Coil 2B / BA Surface For Kitchen
Strip, Coil, Foil and Wire, ASTM A313 204CU stainless steel strip , 2B or BA ,
301 stainless steel strip Cold rolled BA Full hard Slit edge For washers
Product Specification
Payment Terms | L/C, D/P, T/T, Western Union, MoneyGram | Supply Ability | 4000 MT PER week |
Delivery Time | 5-25 Days | Packaging Details | Standard seaworthy export package |
Standard | AMS 5513 | Grade | 304 , 304L |
Thickness | 0.15mm-4mm for cold rolled | Width | 4.6-1200mm |
Technique | Cold Rolled ,hot rolled | Application | Construction,Industry,Tube,decoration,Automotive |
Condition | Annealed ,2B | Forms | strip ,foil ,wire , plate ,sheet |
Product name | stainless steel strip | Edge | slit edge ,round edge ,Deburred edge |
Brand Name | xinzheng | Model Number | Stainless steel strip |
Certification | ISO, EN, MTC | Place of Origin | CHINA |
High Light | AMS 5513 Precision Stainless Steel Strip ,AMS 5513 Precision Stainless Steel trim ,1200mm width Precision Stainless Steel trim |
AMS 5513 304 Stainless steel strips coil Annealed No.1 2B Annealed For general industry overview
304L has oxidation resistance to a maximum temperature of 1650° F (899° C) continuously without appreciable scaling. The maximum temperature for intermittent exposure is 1500° F (816° C). Since 304L is an extra low-carbon variation of 304 it can often be used in the "as-welded" condition (without annealing), even in severe corrosive conditions, except for applications specifying stress relief. 304L has good welding characteristics and can be welded by all standard methods but attention needs to be paid to avoid weld "hot cracking". Welding may be followed by annealing to relieve stresses during severe forming or spinning.
PRODUCT FORMS:
Sheet, plate , Strip, pipe ,tube ,bar ,profiles
Equivalent Materials
AISI 304 equivalents | ||
ASTM A887 Grade S30460 | EN X5CrNi18-10 | ASTM F594 Grade S30500 |
ASTM A887 Grade S30461 | EN 1.4301 | ASTM F594 Grade Alloy Group 1 |
ASTM A887 Grade S30462 | ISO A2 | ASTM F738M Grade S30500 |
ASTM A887 Grade S30463 | GOST 08Ch18N10 | ASTM F738M Grade Alloy Group A1 |
ASTM A887 Grade S30464 | GB 0Cr18Ni9 | ASTM F836M Grade S30500 |
ASTM A887 Grade S30465 | UNS S30400 | ASTM F836M Grade Alloy Group A1 |
ASTM A887 Grade S30466 | ASTM A193 Grade B8P Class 1D | ASTM F837 Grade S30500 |
ASTM A887 Grade S30467 | ASTM A193 Grade B8P Class 1 | ASTM F837 Grade Property Class A1 |
DIN 1.4301 | ASTM A193 Grade B8P Class 2 | ASTM F879 Grade S30500 |
DIN X 5 CrNi 18 9 | ASTM A193 Grade B8PA Class 1A | ASTM F880 Grade S30500 |
DIN X5CrNi18-10 | ASTM A194 Grade 8P | DIN 1.4314 |
AFNOR Z6CN18-09 | ASTM A194 Grade 8PA | AFNOR 9160/C 109 |
AFNOR Z7CN18-09 | ASTM A240 Grade S30500 | AFNOR 9160C411 |
BS 304S15 | ASTM A249 Grade TP305 | AFNOR Z 12 CN 18-10 |
BS 304S31 | ASTM A276 Grade S30500 | AISI 305 |
UNI X5CrNi1810 | ASTM A313 Grade S30500 | SAE 305 |
SS 2332 | ASTM A314 Grade S30500 | EN FE-PA 11 |
UNE F.3551 | ASTM A320 Grade B8P Class 1 | EN FE-PA 12 |
SAE 304 | ASTM A320 Grade B8P Class 2 | EN 1.4314 |
JIS SUS304 | ASTM A320 Grade B8PA Class 1A | DIN 1.4350 |
JIS SUS304TBS | ASTM A368 Grade 305 | DIN X5CrNi18-9 |
JIS SUS304TPD | ASTM A473 Grade 305 | AFNOR Z6CN18.09 |
JIS SUS304TP | ASTM A478 Grade 305 | SS 2333 |
JIS SUS304TPY | ASTM A492 Grade S30500 | EN 1.4350 |
JIS SUS304TB | ASTM A493 Grade S30500 | |
JIS SUS304TF | ASTM A511 Grade MT305 | |
JIS SUS304TKA | ASTM A554 Grade MT305 | |
JIS SUS304TKC | ASTM A580 Grade S30500 | |
JIS SUSF304 | ASTM A959 Grade S30500 | |
ASTM F593 Grade S30500 | ||
ASTM F593 Grade Alloy Group 1 |
Hot Rolled Strip Available Size
Width: 16.0~609.6 mm
Thickness: 2.5~10.0 mm
Available Steel Grade:
Cold Rolled Strip Available Size
Width: 4.0~609.6 mm
Thickness: 0.1~3.0 mm
Surface Finish:
2B, 2D, BA, No.3, No.4, No.5, SB, HL, etc
Surface finish | Characteristics and application |
NO.2B | The surface brightness and flatness of no2B is better than no2D. then through a specialsurface treatment to improve its mechanical properties,No2B could nearly satisfy comprehensive uses |
NO.1 | The surface is finished by heat treatment and pickling or processes corresponding thereto after hot rolling. |
NO.4 | Polished with abrasive belt of grit #150-#180,have better brightness with discontinuous coarse stria,but thinner than No3, are used as bathtub buildings inner and externalornaments electrical appliances kitchen utensils and food processing equipment etc. |
HL | Polished with abrasive belt of grit #150#320 on the NO.4 finish and has continuous streaks,mainly used as buildingsornaments elevators,door of building,frontal plate etc. |
BA | Cold rolled, bright annealed and skin-passed, the product have excellent brightness and good reflexivity like mirror,kitchen apparatus,ornament etc. |
8K | The product have excellent brightness and prefer reflexivity can to be the mirror. |
Condition :
ANNEALED CONDITION
Ultimate Tensile Strength: 95 KSI min (655 MPA min) Yield Strength (0.2% Offset): 38 KSI min (260 MPA min) Elongation: 40%min Hardness: B95 max
TEMPERED 1/16 HARD
Ultimate Tensile Strength: 95 KSI min (655 MPA min) Yield Strength (0.2% Offset): 45 KSI min (310 MPA min) Elongation: 40% min
Tempered 1/8 Hard Ultimate Tensile Strength: 100 KSI min (690 MPA min) Yield Strength (0.2% Offset): 55 KSI min (380 MPA min) Elongation: 45% min
TEMPERED 1/4 HARD
Ultimate Tensile Strength: 125 KSI min (860 MPA min) Yield Strength (0.2% Offset): 75 KSI min (515 MPA min) Elongation: 25% min
TEMPERED 1/2 HARD
Ultimate Tensile Strength: 150 KSI min (1035 MPA min) Yield Strength (0.2% Offset): 110 KSI min (760 MPA min) Elongation: 15% < 0.15" 18% > 0.15"
TEMPERED 3/4 HARD
Ultimate Tensile Strength: 175 KSI min (1205 MPA min) Yield Strength (0.2% Offset): 135 KSI min (930 MPA min) Elongation: 10% < 0.15" 12% > 0.15"
TEMPERED FULL HARD
Ultimate Tensile Strength: 185 KSI min (1275 MPA min) Yield Strength (0.2% Offset): 140 KSI min (965 MPA min) Elongation: 8% < 0.15" 9% > 0.15"
Available Steel Grade:
Stainless steel : Type 201, 202, 205, 301, 302, 302B, 303, 303Se, 304, 304L, 302HQ, 304N, 305, 308, 309, 309S, 310, 310S, 314, 316, 316L, 316F, 316N, 317, 317L, 317LMN, 321, 330, 347, 348, 384, 405, 409, 429, 430, 430F, 430FSe, 434, 436, 442, 446, 403, 410, 414, 416, 416Se, 420, 420F, 422, 431, 440A, 440B, 440C, 630 , 13-8 PH ,15-5 PH , 17-7 PH ,17-4 ph , 904L , A286 ,VG-10 , SAE 316 , SAE 316L , SAE 440 , SAE 420
Duplex stainless steel : 2205 , 2304 , 2507
Nickel alloy :
Titanium and titanium alloys
Composition per ASTM A240 | |
Carbon | .030 Max |
Manganese | 2.00 Max |
Phosphorus | .045 Max |
Sulfur | .030 Max |
Silicon | .75 Max |
Chromium | 17.50 – 19.50 |
Nickel | 8.00 – 12.00 |
Nitrogen | .10 Max |
Molybdenum | |
Mechanical Properties (Annealed, Per ASTM A240) | |
UTS | 70,000 ksi Min |
Elongation % in 2″ | 40.00 Min |
Rockwell Hardness | RB92.00 Max |
ADDITIONAL PROPERTIES
FINISHES
# 1 - Hot rolled annealed and descaled. It is available in strip, foil and ribbon. It is used for applications where a smooth decorative finish is not required.
# 2D - Dull finish produced by cold rolling, annealing and descaling. Used for deep drawn parts and those parts that need to retain lubricants in the forming process.
# 2B - Smooth finish produced by cold rolling, annealing and descaling. A light cold rolling pass is added after anneal with polished rolls giving it a brighter finish than 2D. #BA- Bright annealed cold rolled and bright annealed #CBA- Course bright annealed cold rolled matte finish and bright anneal
#2 - Cold Rolled
# 2BA- Smooth finish produced by cold rolling and bright annealing. A light pass using highly polished rolls produces a glossy finish.
2BA finish may be used for lightly formed applications where a glossy finish is desired in the formed part. Polished - Various grit finish for specific polish finished requirements. * Special finishes are available for all alloys - Contact US for more information
.
Q: Would you provide samples For free?
A: Yes . with on stock specification We provide samples For Free . Freight charge collect
Company Details
Business Type:
Manufacturer,Distributor/Wholesaler,Agent,Exporter,Trading Company,Seller
Year Established:
2016
Total Annual:
10000000-20000000
Employee Number:
100~200
Ecer Certification:
Active Member
Wuxi Zhongxin Special Steel Co.,Ltd is located in Wuxi City, Wuxi is close to Shanghai (BAO STEEL) ,Zhangjiagang (ZPSS),Ningbo (BAO XIN),KUN SHAN (DKSS), enjoy excellent geographic location and convenient water, land and air transportation. , Wuxi become the biggest stainless steel shee... Wuxi Zhongxin Special Steel Co.,Ltd is located in Wuxi City, Wuxi is close to Shanghai (BAO STEEL) ,Zhangjiagang (ZPSS),Ningbo (BAO XIN),KUN SHAN (DKSS), enjoy excellent geographic location and convenient water, land and air transportation. , Wuxi become the biggest stainless steel shee...
Get in touch with us
Leave a Message, we will call you back quickly!