Wuxi Zhongxin Special Steel Co.，Ltd
| Payment Terms | L/C, D/P, T/T, Western Union, MoneyGram |
| Supply Ability | 4000 MT PER week |
| Delivery Time | 5-25 Days |
| Packaging Details | Standard seaworthy export package |
| Standard | ASME ,AISI,ASTM, EN, ISO |
| Thickness | 0.15mm-4mm for cold rolled |
| Width | 4.6-700mm |
| Technique | Cold Rolled |
| Application | Construction,Industry,Tube,decoration,Automotive |
| Grade | 301 stainless steel |
| Length | strip ,foil ,wire , plate ,sheet ,tube ,pipe |
| Product name | stainless steel strip |
| Edge | Mill edge ,slit edge ,round edge ,Deburred edge |
| Brand Name | xinzheng |
| Model Number | Stainless steel strip |
| Certification | ISO,SGS,ISO & SGS,ISO/CE/SGS |
| Place of Origin | CHINA |
View Detail Information
Explore similar products
ISO BV Austenitic 1mm Aluminium Strip N08020 Duplex Steel Coil
UNS S20400 Precision Stainless Steel Strip Flat Metal Trim Nitronic 30
ASTM A666 Thin Stainless Steel Perforated Metal Strip 410 Martensitic
A580 Precision Stainless Steel Strip nickel plated 13-8 PH
Product Specification
| Payment Terms | L/C, D/P, T/T, Western Union, MoneyGram | Supply Ability | 4000 MT PER week |
| Delivery Time | 5-25 Days | Packaging Details | Standard seaworthy export package |
| Standard | ASME ,AISI,ASTM, EN, ISO | Thickness | 0.15mm-4mm for cold rolled |
| Width | 4.6-700mm | Technique | Cold Rolled |
| Application | Construction,Industry,Tube,decoration,Automotive | Grade | 301 stainless steel |
| Length | strip ,foil ,wire , plate ,sheet ,tube ,pipe | Product name | stainless steel strip |
| Edge | Mill edge ,slit edge ,round edge ,Deburred edge | Brand Name | xinzheng |
| Model Number | Stainless steel strip | Certification | ISO,SGS,ISO & SGS,ISO/CE/SGS |
| Place of Origin | CHINA |
Type 301 is an austenitic stainless steel capable of attaining high strengths and ductility by cold working. Type 301 Stainless Steel is non-magnetic in the annealed condition, but becomes magnetic through cold work. The high strength and corrosion resistance of this grade of stainless steel makes it useful for a variety of applications.
Type 301 is a chromium nickel austenitic stainless steel capable of attaining high strengths and ductility by cold working. It is not hardenable by heat treatment. Type 301 is non-magnetic in the annealed condition and becomes increasingly magnetic with cold working. This chromium nickel stainless steel alloy provides high strength and good ductility when cold worked. 301 stainless steel is a modification of stainless steel grade 304 with lower chromium and nickel to increase the work hardening range. Type 301 steel exhibits corrosion resistance comparable to type 302 and 304. In the cold worked and annealed condition, type 301 achieves its most optimal resistance to corrosion. It is preferable over types 302 and 304 in the tempered condition because the higher enlongations (which are attainable at a given strength level) facilitate fabrication.
ASTM A240 for annealed condition
ASTM A666 for tempered material
Hot Rolled Strip Available Size
Width: 16.0~609.6 mm
Thickness: 2.5~10.0 mm
Available Steel Grade:
Cold Rolled Strip Available Size
Width: 4.0~609.6 mm
Thickness: 0.1~3.0 mm
2B, 2D, BA, No.3, No.4, No.5, SB, HL, etc
| Surface finish | Characteristics and application |
| NO.2B | The surface brightness and flatness of no2B is better than no2D. then through a special surface treatment to improve its mechanical properties,No2B could nearly satisfy compreh ensive uses. |
| NO.1 | The surface is finished by heat treatment and pickling or processes corresponding thereto after hot rolling. |
| NO.4 | Polished with abrasive belt of grit #150-#180,have better brightness with discontinuous coarse stria,but thinner than No3, are used as bathtub buildings inner and external ornaments electrical appliances kitchen utensils and food processing equipment etc. |
| HL | Polished with abrasive belt of grit #150#320 on the NO.4 finish and has continuous streaks,mainly used as buildingsornaments elevators,door of building,frontal plate etc. |
| BA | Cold rolled, bright annealed and skin-passed, the product have excellent brightness and good reflexivity like mirror,kitchen apparatus,ornament etc. |
| 8K | The product have excellent brightness and prefer reflexivity can to be the mirror. |
ANNEALED CONDITION
Ultimate Tensile Strength: 95 KSI min (655 MPA min) Yield Strength (0.2% Offset): 38 KSI min (260 MPA min) Elongation: 40%min Hardness: B95 max
TEMPERED 1/16 HARD
Ultimate Tensile Strength: 95 KSI min (655 MPA min) Yield Strength (0.2% Offset): 45 KSI min (310 MPA min) Elongation: 40% min
Tempered 1/8 Hard Ultimate Tensile Strength: 100 KSI min (690 MPA min) Yield Strength (0.2% Offset): 55 KSI min (380 MPA min) Elongation: 45% min
TEMPERED 1/4 HARD
Ultimate Tensile Strength: 125 KSI min (860 MPA min) Yield Strength (0.2% Offset): 75 KSI min (515 MPA min) Elongation: 25% min
TEMPERED 1/2 HARD
Ultimate Tensile Strength: 150 KSI min (1035 MPA min) Yield Strength (0.2% Offset): 110 KSI min (760 MPA min) Elongation: 15% < 0.15" 18% > 0.15"
TEMPERED 3/4 HARD
Ultimate Tensile Strength: 175 KSI min (1205 MPA min) Yield Strength (0.2% Offset): 135 KSI min (930 MPA min) Elongation: 10% < 0.15" 12% > 0.15"
TEMPERED FULL HARD
Ultimate Tensile Strength: 185 KSI min (1275 MPA min) Yield Strength (0.2% Offset): 140 KSI min (965 MPA min) Elongation: 8% < 0.15" 9% > 0.15"
Stainless steel : Type 201, 202, 205, 301, 302, 302B, 303, 303Se, 304, 304L, 302HQ, 304N, 305, 308, 309, 309S, 310, 310S, 314, 316, 316L, 316F, 316N, 317, 317L, 317LMN, 321, 330, 347, 348, 384, 405, 409, 429, 430, 430F, 430FSe, 434, 436, 442, 446, 403, 410, 414, 416, 416Se, 420, 420F, 422, 431, 440A, 440B, 440C, 630 , 13-8 PH ,15-5 PH , 17-7 PH ,17-4 ph , 904L , A286 ,VG-10 , SAE 316 , SAE 316L , SAE 440 , SAE 420
Duplex stainless steel : 2205 , 2304 , 2507
Nickel alloy :
Titanium and titanium alloys
| Element | Min | Max |
|---|---|---|
| Carbon | 0.15 | 0.15 |
| Manganese | 2.00 | 2.00 |
| Silicon | 1.00 | 1.00 |
| Chromium | 16.00 | 18.00 |
| Nickel | 6.00 | 8.00 |
| Aluminum | 0.75 | 0.75 |
| Phosphorus | 0.040 | 0.040 |
| Sulphur | 0.030 | 0.030 |
| Copper | 0.75 | 0.75 |
| Nitrogen | 0.10 | 0.10 |
| Iron | Balance | Balance |
Density: 0.285 lbs/in 3 7 .88 g/cm3
Electrical Resistivity: microhm-in (microhm-cm): 68 °F (20 °C): 27.4 (69.5)
Specific Heat: BTU/lb/° F (kJ/kg•K): 32 -212 °F (0 -100 °C): 0.12 (0.50)
Thermal Conductivity: BTU/hr/ft2/ft/° F (W/m•K)
At 212 ° F (100 °C)-9.4 (16.2),
At 932 ° F (500 °C)-12.4 (21.4)
Mean Coefficient of Thermal Expansion: in/in/° F (µm/m•K)
32-212 °F (0-100 °C)-9.4 x 10·6 (16.9)
32-600 °F (0-315 °C)-9.9 x 10·6 (17.8)
32 -1000 °F (0 -538 °C)-10.2 x 10·6 (18.4)
32 -1200 °F (0 -649 °C)-10.4 x 10·6 (18.7)
Modulus of Elasticity: ksi (MPa)
28.0 x 103 (193 x 103) in tension
11.2 x 103 (78 x 103) In torsion
Magnetic Permeability: H = 200 Oersteds: Annealed < 1.02 max.
Melting Range: 2250-2590 ° F (1399-1421 ° C)
Ultimate Tensile Strength: 75 KSI min (515 MPA min) Yield Strength: (0.2% offset): 30 KSI min (205 MPA min) Elongation: 40% Min Hardness: B92 or Equiv. Max
1/16 Hard Ultimate Tensile Strength: 90 KSI min (629 MPA min) Yield Strength: (0.2% Offset) 45 KSI min (310 MPA min) Elongation: 40% Min 1/8 Hard Ultimate Tensile Strength: 100 KSI min (690 MPA) Yield Strength: (0.2% Offset) 55 KSI min/380 MPA min Elongation: 40% Min1/4 Hard Ultimate Tensile Strength: 125 KSI min (860 MPA) Yield Strength: (0.2% Offset) 75 KSI min/515 MPA min Elongation: 25% Min
1/2 Hard Ultimate Tensile Strength: 150 KSI min (1035 MPA min) Yield Strength: (0.2% Offset) 110 KSI min (760 MPA min) Elongation: 15%<.015" 18%>.015" 3/4 Hard Ultimate Tensile Strength: 175 KSI min (1205 MPA min) Yield Strength: (0.2% Offset) 135 KSI MIN/515 MPA MIN Elongation: 10%< .015" 12%> .015" Full Hard Ultimate Tensile Strength: 185 KSI min (1275 MPA min) Yield Strength: (0.2% Offset) 140 KSI min (965 MPA min) Elongation: 8% < .015" 9% > .015" Extra Full Hard Ultimate Tensile Strength: 270 KSI min< .014" (1860 MPA min) 250 KSI min .015" to 017" (1720 MPA min) 225 KSI min .0171" to .019" (1552 MPA min) 205 KSI min .0191 to .021 (1435 MPA min) 185 KSI min >.0211 (1275 MPA min) Spring Tempered Ultimate Tensile Strength: 185 KSI min (1275 MPA min) Yield Strength: (0.2% Offset) 140 KSI min (965 MPA min) Elongation: 8% < .015" 9% > .045"
301 has good to excellent corrosion resistance and is used in many food service applications, similar to grade 304.
Q: Would you provide samples For free?
A: Yes . with on stock specification We provide samples For Free . Freight charge collect
SAE 301 JIS SUS301 ASTM MT301 ASTM 301 UNS S30100 DIN 1.4310 DIN X12CrNi-17-7 DIN O DIN 14 DIN X10CrNi18-8 DIN X12CrNi17-7 DIN X 12 CrNi 17 7 AFNOR X10CrNi18-8 AFNOR Z12CN17-07 BS 301S21 BS X10CrNi18-8 UNI X2CrNi1807 SS 2331 UNE F.3517 AISI S30100 AISI 30301 SAE S30100 SAE 30301 JIS SUS302 EN X10CrNi18-8 EN 1.4310 ISO X10CrNi18-8 GOST 12Ch18N9 GB 1Cr17Ni7 ASTM S30151 ASTM 30302 UNS S30200 UNS S30151 IS X07Cr18Ni9 DIN 1.4324 AISI 302 SAE 302 JIS SUS301J1 EN FE-PA 18 EN 1.4324 302 ASTM MT302
Company Details
Business Type:
Manufacturer,Distributor/Wholesaler,Agent,Exporter,Trading Company,Seller
Year Established:
2016
Total Annual:
10000000-20000000
Employee Number:
100~200
Ecer Certification：
Active Member
Wuxi Zhongxin Special Steel Co.，Ltd is located in Wuxi City, Wuxi is close to Shanghai (BAO STEEL) ,Zhangjiagang (ZPSS),Ningbo (BAO XIN),KUN SHAN (DKSS), enjoy excellent geographic location and convenient water, land and air transportation. , Wuxi become the biggest stainless steel shee... Wuxi Zhongxin Special Steel Co.，Ltd is located in Wuxi City, Wuxi is close to Shanghai (BAO STEEL) ,Zhangjiagang (ZPSS),Ningbo (BAO XIN),KUN SHAN (DKSS), enjoy excellent geographic location and convenient water, land and air transportation. , Wuxi become the biggest stainless steel shee...