Weifang Shihua Chemical Building Material Co., Ltd.
| Supply Ability | 500000㎡per Month |
| water impermeability | 0.3 megapascals, 2 hours, impermeable |
| regular thickness | 1.2mm/1.5mm/2.0mm |
| regular width | 2.0m |
| elongation at break | ≥500% |
| tensile strength | ≥12.0MPa |
| low temperature bending property | -40℃ no crack |
| Packaging Details | Plastic woven bags / Customizable |
| impact resistance | 0.5 kg·m, waterproof |
| normal length | 20m，custom length |
| Brand Name | shhous |
| Model Number | 1.2mm，1.5mm，2.0mm |
| Place of Origin | shandong,china |
| Certification | ISO |
View Detail Information
Explore similar products
Traffic Engineering TPO Waterproofing Membrane -40℃ No Crack
Custom Length 20m TPO Waterproofing Membrane For Building Roofs
White Tpo Waterproof Membrane Fireresistance For Underground Engineering
Non Asphalt TPO Waterproofing Membrane For Water Conservancy Projects
Product Specification
| Supply Ability | 500000㎡per Month | water impermeability | 0.3 megapascals, 2 hours, impermeable |
| regular thickness | 1.2mm/1.5mm/2.0mm | regular width | 2.0m |
| elongation at break | ≥500% | tensile strength | ≥12.0MPa |
| low temperature bending property | -40℃ no crack | Packaging Details | Plastic woven bags / Customizable |
| impact resistance | 0.5 kg·m, waterproof | normal length | 20m，custom length |
| Brand Name | shhous | Model Number | 1.2mm，1.5mm，2.0mm |
| Place of Origin | shandong,china | Certification | ISO |
| High Light | industrial thermoplastic polyolefin membrane ，industrial thermoplastic polyolefin roofing membrane ，buildings thermoplastic polyolefin membrane | ||
Tpo Waterproofing Membrane Suitable For Industrial Plants, Public Buildings, Etc
Product Features
The most core advantage of this type of coil is its outstanding weathering resistance. After the 7200-hour artificial climate accelerated aging test, its appearance and physical properties remain stable, and its expected outdoor service life reach more than 25 years. The solar reflectance of white and light-colored surfaces can reach more than 80%, which significantly reduce the roof temperature in summer, reduce building air conditioning cooling energy consumption, and achieve the energy-saving effect ofcool roof". The coil does not contain chlorine elements and plasticizers, and it will not become brittle due to plasticizer migration during long-term use. No gases are released during welding and use, and the material is recyclable, fully meeting the environmental protection requirements of green buildings and LEED certification. At the same time, its resistance range covers from -50℃ to high-temperature environments, and it can maintain flexibility even under extremely cold conditions in northern winters without low-temperature cracking.
performance metric
| No. | Item | Standard Requirement |
| 1 | Thermal aging (115°C × 672 h) | No abnormal appearance, tensile/elongation retention rate ≥90% |
| 2 | Heat treatment dimensional change rate | ≤2.0% |
| 3 | Seam peel strength | ≥4.0N/mm or roll material failure |
| 4 | right angle tear strength | ≥60N/mm |
Construction Steps
1.Base Treatment: Remove debris and protruding sharp objects from roof base, fill the uneven areas with cement mortar to ensure the base is flat and dry without obvious water accumulation risks.
2. Pre-laying Marking Draw reference lines according to the roof dimensions and the width of TPO membrane rolls, lay the TPO membrane rolls naturally and loosely on base, and let them stand for 30 minutes to release the internal stress of the material, so as to avoid the membrane wrinkling caused by temperature changes in the later stage.
3. Mechanical Fixing Fix the membrane rolls to the roof base with matching galvanized pressure bars and self-tapping screws. The spacing of fixing points shall be strictly set according to the calculation results of load to ensure that the overall wind uplift resistance performance meets the standards.
4. Hot Air Welding: Treat the lap edges of the membrane rolls an automatic hot air welding machine. Control the lap width to be above 10mm. Adjust the welding temperature according to the ambient temperature to ensure that the lap edges fully fused together without soldering defects such as cold joints or missed welds.
5. Detail Treatment: For detail positions such as and external roof corners, pipe roots, ventilation openings, and pipes extending from the roof, cut homogeneous TPO membrane rolls into adapted shapes heat and shape them with a hot air gun, then weld and seal them. Fix all head parts with U-shaped pressure bars and apply sealant to seal edges.
Acceptance Inspection: Conduct an air inflation test on all double-weld lap edges. If the pressure remains stable for minutes after reaching 0.15MPa, it is qualified. At the same time, the overall membrane surface for no damage or curling edges to complete the construction acceptance.
Company Details
Business Type:
Manufacturer,Exporter
Year Established:
2000
Total Annual:
17790000-17790000
Employee Number:
150~200
Ecer Certification：
Verified Supplier
Weifang Shihua Chemical Building Materials Co., Ltd. Founded in 1994, the company has a registered capital of RMB 100.86 million and covers a plant area of over 30,000 square meters. It mainly manufactures more than 100 types of products across five major series, including Shihua‑brand po... Weifang Shihua Chemical Building Materials Co., Ltd. Founded in 1994, the company has a registered capital of RMB 100.86 million and covers a plant area of over 30,000 square meters. It mainly manufactures more than 100 types of products across five major series, including Shihua‑brand po...