| Product name | Stainless Steel Welding Wire |
| Grade | ER310 |
| Wire Weight | 1kg / 5kg / 15kg / 150kg / 250kg |
| Wire Size(mm) | 0.8mm / 0.9mm / 1.0mm / 1.2mm/ 1.6mm/ 2.0mm |
| Wire Size(in) | 0.25 / 0.30 /0.35 / 0.40 / 0.45 / 0.030 |
| Package | spool - drum |
| Certification | ISO9001, CE |
| Place of Origin | Jiangsu, China |
View Detail Information
Explore similar products
0.8mm Stainless Steel Welding Wire In Spool ER308LSi
Alloy ER 2209 Stainless Steel TIG MIG And SUB - ARC Wire Used For Welding 1.0mm
Alloy Stainless Steel Welding Wire ER304 1.6mm
ER347 Stainless Steel TIG Welding Rods Wires 1.2mm
Product Specification
| Payment Terms | L/C, T/T | Supply Ability | 5000 Ton/Tons per Month |
| Delivery Time | 7~10working days | Product name | Stainless Steel Welding Wire |
| Grade | ER310 | Wire Weight | 1kg / 5kg / 15kg / 150kg / 250kg |
| Wire Size(mm) | 0.8mm / 0.9mm / 1.0mm / 1.2mm/ 1.6mm/ 2.0mm | Wire Size(in) | 0.25 / 0.30 /0.35 / 0.40 / 0.45 / 0.030 |
| Package | spool - drum | Certification | ISO9001, CE |
| Place of Origin | Jiangsu, China | ||
| High Light | AWS Class Welding Stainless Steel Wire ，ER310 Stainless Steel MIG Wire ，MIG 0.35" Welding Stainless Steel Wire | ||
ER310 Stainless Steel Welding Wire
ER310 Stainless Steel Welding Wire is also known as H12Cr26Ni21Si.The melting gold contains 25Cr-20Ni. it is mostly used in the welding ratio KMS of 310S stainless steel. 309 is more suitable for dissimilar metal welding and high self-hardening alloy steel and high carbon steel welding; It can be used for welding stainless steel and stainless steel lining, as well as dissimilar steel, high chromium steel, high manganese steel and so on.
STAINLESS STEEL SPRING WIRE GRADE
|
European Standards EN 10088-3 |
Designation USA | Japan | |||
| Grades | Designation | AISI-ASTM-SAE | UNS | ||
| AUSTENITIC GRADES | 1.4301 | X5CrNi8-10 | 304 | S30400 | 304 |
| 1.431 | X10CrNi18-8 | 302 | S30200 | 302 | |
| 1.4305 | X8CrNiS18-9 | 303 | S30300S | 303 | |
| 1.4306 | X2CrNi19-11 | 304L | - | - | |
| 1.4303 | X4CrNi18-9 | 305 | S30600 | 305 | |
| 1.4307 | X2CrNi18-9 | 304L | S30403 | 304L | |
| 1.4401 | X5CrNiMo17-12-2 | 316 | S31600 | 316 | |
| 1.4404 | X2CrNiMo17-12-2 | 316L | S31603 | 316L | |
| 1.4541 | X5CrNiTi18-10 | 321 | S32100 | 321 | |
| 1.4567 | X3CrNiCu18-9-4 | 302HQ-304Cu | S30430 | XM7 | |
| 1.457 | X6CrNiCuS18-9-2 | - | - | - | |
| 1.4571 | X6CrNiMoTi17-12-2 | 316Ti | S31635 | 316Ti | |
| 1.4597 | X8CrMnCuNB17-8-3 | 204Cu | - | - | |
| 1.4539 | X1NiCrMoCu25-20-5 | 904L | NO8904 | - | |
| REFRACTORY GRADES | 1.4841 | X15CrNiSi25-21 | 314 | S31400 | - |
| 1.4845 | X8CrNi25-21 | 310-310S | S31000 | SUH310 | |
| FERRITIC GRADES | 1.4016 | X6Cr 17 | 430 | S43000 | 430 |
| 1.4104 | X14CrMoS17 | 430F | S43020 | 430F | |
| 1.4509 | X2CrTiNb18 | 441 | S44100 | 441 | |
| 1.451 | X3CrTi17 | 439/XM8 | S43035 | - | |
| 1.4511 | X3CrNb17 | 430Cb | - | - | |
| 1.4512 | X2CrTi12 | 409 | S40920 | - | |
| MARTENSITIC GRADES | 1.4005 | X12CrS13 | 416 | S41600 | 416 |
| 1.4034 | X46Cr13 | 420C | - | - | |
| 1.4021 | X20Cr13 | 420A | S4200 | - | |
| 1.4035 | X46CrS13 | - | - | - | |
ER310 CHEMICAL COMPOSITION--Standard:AWS A 5.9 YB/T5092
| Element | C | Mn | Si | P | S | Cr | Ni | Mo | Cu | Ti | Nb |
| ER308LSi | ≤0.03% | 1.0~2.5% | 0.65~1.00% | ≤0.03% | ≤0.03% | 19.5~22% | 9~11% | ≤0.75% | ≤0.75% | - | - |
| ER304 | ≤0.08% | 1.0~2.5% | ≤0.06% | ≤0.03% | ≤0.03% | 17~19% | 8~11% | - | - | - | - |
| ER321 | ≤0.08% | 1.0~2.5% | 0.3~0.65% | ≤0.03% | ≤0.03% | 18.5~20.5% | 9~10.5% | ≤0.75% | - | 9×C–1.00 | - |
| ER309L | ≤0.03% | 1.0~2.5% | 0.3~0.65% | ≤0.03% | ≤0.03% | 23~25% | 12~14% | ≤0.75% | ≤0.75% | - | - |
| ER307Si | 0.04~0.14% | 6.5~8.0% | 0.65~1.0% | ≤0.03% | ≤0.03% | 18.5~22% | 8~10.75% | ≤0.75% | ≤0.75% | - | - |
| ER347 | ≤0.08% | 1.0~2.5% | 0.3~0.65% | ≤0.03% | ≤0.03% | 19~21.5% | 9~11% | ≤0.75% | - | - | 10×C–1.0 |
| ER316LSi | ≤0.03% | 1.0~2.5% | 0.65~1.0% | ≤0.03% | ≤0.03% | 18~20% | 11~14% | 2~3% | ≤0.75% | - | - |
| ER410 | ≤0.12% | ≤0.6% | ≤0.5% | ≤0.03% | ≤0.03% | 11.5~13.5% | ≤0.6% | ≤0.75% | ≤0.75% | - | - |
| ER430 | ≤0.10% | ≤0.6% | ≤0.5% | ≤0.03% | ≤0.03% | 15.5~17% | ≤0.6% | ≤0.75% | ≤0.75% | - | - |
| ER310 | 0.08~0.15% | 1.0~2.5% | 0.3~0.65% | ≤0.03% | ≤0.03% | 25~28% | 20~22.5% | ≤0.75% | ≤0.75% | - | - |
| ER2209 | ≤0.03% | 0.5~2.0% | ≤0.9% | ≤0.03% | ≤0.03% | 21.5~23.5% | 7.5~9.5% | ≤0.75% | - | - | - |
ER310 Stainless Steel Welding Wire Specifications
| Type | Spool (MIG) | Tube (TIG) | ||||||
|
Specification ( MM ) |
0.8,0.9,1.0,1.2,1.6,2.0 | 1.6,2.0,2.4,3.2,4.0,5.0 | ||||||
| Package |
S100/1kg S200/5kg S270,S300/15kg-20kg |
5kg/box 10kg/box length :1000MM | ||||||
| Mechanical Properties | Tensile Strength Mpa | Elongation after fracture A(%) | ||||||
| ≥ 550 | ≥ 30 | |||||||
| Diameter(MM) | 0.8 | 1.0 | 1.2 | 1.6 | 2.0 | 2.5 | 3.2 | |
| Current(A) | 70 ~ 150 | 100 ~ 200 | 140 ~ 220 | 50 ~ 100 | 100 ~ 200 | 200 ~ 300 | 300 ~ 400 | |
Stainless Steel MIG welding wire have how many types?
ER304,ER307Si,ER308,ER308L,ER308LSi,ER309,ER309L,ER309LSi,ER310,ER316,ER316L,ER316LSi,ER321,ER347,ER410,
ER430,ER2209,317l
How to choose a suitable gasless mig welding stainless steel wire?or what type of filler wire is best for wire feed welding stainless steel?
The first two designators may be“ER”for solid wires that may be used as electrodes or rodsor they may be“EC’for composite cored or stranded wires;or they may be“EQ”for strip electrodes.
The three- or four-digit number,such as 308 in ER308,designates the nominal chemical composition of the filler metal.
ER307.The nominal composition(wt.%)of this classification is 21 Cr.9.5Ni.4 Mn.1 Mo.Filler metals .
ER308The nominal composition(wt.%)of this classification is 21 Cr10 Ni.Commercial specifications is most often used to weld base metals of similar composition, in particular, Type 304.
ER308Si.This classification is the same asER308except for the higher silicon content.
ER308H.This classification is the same as ER308.except that the allowable carbon content is used for welding 304H base metal.
ER308L.This classification is the same as ER308,except for the carbon content.Low carbon,is less than that of the niobium-stabilized alloys or Type 308H at elevated temperatures.
ER308LMo.This classification is used for welding ASTM CF3M stainless steel castings and matches the base metal with ER316L is desired.
ER309.The nominal composition(wt.%)of this classification is 24 Cr13 Ni.Filler metals.
304 and similar base metals where severe corrosion conditions exist requiring higher alloy weld metal.
ER309Si.This classification is the same as ER309,except for higher silicon content.
ER309L.This classification is the same as ER39,except for the carbon content.
ER309LS.This classification is the same as ER309Lexcent for higher sillicon content.
ER309Mo.This classification is the same as ER309except for the addition of 2.0 percent to 3.0 percent.
ER310.The nominal composition(wt.%)of this classification is 26.5 Cr,21 Ni.Filler metal of this classification is most often used to weld base metals of similar composition
ER312.The nominal composition(wt.%) of this classification is 30 Cr, 9 Ni.Filler metal of this classification was originally designed to weld cast alloys of similar composition.
ER316 weld metal may occur when the following three factors co-exist:
The presence of a continuous or semicontinuous network of ferrite in the weld metal microstructurel
ER316Si.This classification is the same as ER316,except for the higher silicon content.
ER316H.This filler metal is the same as ER316,except that the allowable carbon .
ER316L.This classification is the same as ER316.except for the carbon content.
ER316LSi.This classification is the same as ER316L except for the higher silicon content.
ER317.The nominal composition(wt.%) of this classification is 19.5 Cr14 Ni3.5 Mo, higher than ER316.
ER317LThis classification is the same as ER317except for the carbon content.
ER318This composition is identical to ER316,except for the addition of niobium.
ER321Thenominal composition(wt.%)of this classification is 19.5 Cr.9.5 Niwith titanium added.The titanium acts in the same way as niobium in Type 347.
ER347.The nominalcomposition(wt.%) of this classification is 20 Cr,10 Ni,with Nb added as a stabilizer.
ER347Si.This classification is the same as ER347,except for the higher silicon content.
ER409.This 12 Cr alloy(wt.%) differs from Tvpe 410 material because it has a ferritic microstructure.
ER410.This 12 Cralloy(wt.%) is an air-hardening steel.
ER410NiMo.The nominal composition(wt.%)of this classification is 12 Cr4.5 Ni.0.55 Mo.
ER430.This is a 16 Cr(wt.%) alloy.The composition is balanced by providing sufficient chromium to give adequate corrosion resistance for the usual applications.
ER439.This is an 18 Cr(wt.%) alloy that is stabilized with titanium.
Company Details
Business Type:
Manufacturer,Exporter,Trading Company,Seller
Year Established:
2018
Total Annual:
15000000-20000000
Employee Number:
100~120
Ecer Certification：
Verified Supplier
Qingdao Teste Metal Products Co., Ltd. is a professional manufacturer with more than 20 years of experience in manufacturing stainless steel and carbon steel establised in 2018. Our location is in Wuxi - the largest stainless-steel processing center in China. We have our own factory and... Qingdao Teste Metal Products Co., Ltd. is a professional manufacturer with more than 20 years of experience in manufacturing stainless steel and carbon steel establised in 2018. Our location is in Wuxi - the largest stainless-steel processing center in China. We have our own factory and...
Get in touch with us
Leave a Message, we will call you back quickly!