| Model NO. | 301 |
| Shape | Flat |
| Technique | Cold Rolled |
| Surface Treatment | Bright |
| Thickness | 0.1 - 3.0mm |
| Width | 10 - 1219mm |
| Hardness | 1/4H 1/2H 3/4H FH |
| Tensile Strength | 758 - 1276 MPa |
| Yield Strength | 276 - 965 MPa |
| Elongation | 9 - 60% |
| Density | 7880 kg/m3 |
| Elastic Modulus | 193 GPa |
| Thermal Conductivity | 16.2 - 21.4 W/m.K |
| Electrical Resistivity | 695 nΩ.m |
| Thermal Expansion | 16.9 - 18.2 μm/m/°C |
| Certification | AISI, ASTM, EN, DIN |
View Detail Information
Explore similar products
Cold Rolled Stainless Steel Strip with Polished Surface and Width 10-1800mm SS
Cold Rolled Stainless Steel Strip with Polished Surface and Width 10-1800mm SS
ASTM A240 SS316L Strip Cold Rolled Stainless Steel Coil with Polished Surface
AISI 304L 316L 310S Stainless Steel Coil with No. 4 Finish and Width 10-1800mm
Product Specification
| Model NO. | 301 | Shape | Flat |
| Technique | Cold Rolled | Surface Treatment | Bright |
| Thickness | 0.1 - 3.0mm | Width | 10 - 1219mm |
| Hardness | 1/4H 1/2H 3/4H FH | Tensile Strength | 758 - 1276 MPa |
| Yield Strength | 276 - 965 MPa | Elongation | 9 - 60% |
| Density | 7880 kg/m3 | Elastic Modulus | 193 GPa |
| Thermal Conductivity | 16.2 - 21.4 W/m.K | Electrical Resistivity | 695 nΩ.m |
| Thermal Expansion | 16.9 - 18.2 μm/m/°C | Certification | AISI, ASTM, EN, DIN |
| High Light | Cold Rolled 301 Stainless Steel Strip ，Width 10-2000mm 301 Stainless Steel Coil ，Bright Surface 301 Stainless Steel | ||
301 stainless steel is available in strip and wire forms with tensile strength up to 1800 MPa, offering tempers ranging from 1/16 Hard to Full Hard. This grade maintains sufficient ductility even in ½ hard conditions, making it suitable for aircraft components, rail car parts, and architectural structures.
| Product Name | 301 Stainless Steel Strips |
|---|---|
| Thickness | 0.1 - 3.0mm |
| Surface | 2B, Bright, Hairline |
| Width | 10 - 1219mm |
| Standard | ASTM A240 / JIS G4305 / EN 10088 |
| Hardness | 1/4H, 1/2H, 3/4H, FH or as requested |
| Other Grades | 201, 202, 301, 304, 304L, 309S, 310S, 316L, 410, 420, 430, 440, etc. |
| MOQ | 300 Kgs |
301L: Low carbon version ideal for applications requiring good ductility, specified in JIS G4305.
301LN: Contains higher nitrogen content with increased work hardening rate, specified in EN10088-2 as grade 1.4318.
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N |
|---|---|---|---|---|---|---|---|---|---|
| 301 ASTM A666 | - 0.15 | - 2.0 | - 1.0 | - 0.045 | - 0.030 | 16.0-18.0 | - | 6.0-8.0 | - 0.10 |
| 301L JIS G4305 | - 0.03 | - 2.0 | - 1.0 | - 0.045 | - 0.030 | 16.0-18.0 | - | 6.0-8.0 | - 0.20 |
| 1.4318/301LN EN 10088-2 | - 0.03 | - 2.0 | - 1.0 | - 0.045 | - 0.015 | 16.5-18.5 | - | 6.0-8.0 | 0.10-0.20 |
| Grade 301 Temper ASTM A666 | Tensile Strength (MPa) min. | Yield Strength 0.2% Proof (MPa) min. | Elongation (% in 50mm) min. | Bend Angle (°) | Bend Factor |
|---|---|---|---|---|---|
| Annealed | 758 | 276 | 60 | - | - |
| 1/16 Hard | 620 | 310 | 40 | 180 | 1 |
| 1/8 Hard | 690 | 380 | 40 | 180 | 1 |
| 1/4 Hard | 862 | 514 | 25 | 90 | 2 |
| 1/2 Hard | 1034 | 758 | 18 | 90 | 2 |
| 3/4 Hard | 1205 | 930 | 12 | 90 | 3 |
| Full Hard | 1276 | 965 | 9 | 90 | 5 |
| Property | 301 Grade |
|---|---|
| Density (kg/m³) | 7880 |
| Elastic Modulus (GPa) | 193 |
| Mean Coefficient of Thermal Expansion (μm/m/°C) 0-100°C | 16.9 |
| Mean Coefficient of Thermal Expansion (μm/m/°C) 0-315°C | 17.2 |
| Mean Coefficient of Thermal Expansion (μm/m/°C) 0-538°C | 18.2 |
| Thermal Conductivity (W/m.K) at 100°C | 16.2 |
| Thermal Conductivity (W/m.K) at 500°C | 21.4 |
| Specific Heat 0-100°C (J/kg.K) | 500 |
| Electrical Resistivity (nΩ.m) | 695 |
Similar to 304 stainless steel, grade 301 offers good resistance to corrosion in mildly corrosive environments at ambient temperatures.
Exhibits good oxidation resistance for intermittent service up to 840°C and continuous service up to 900°C.
Solution treatment annealing at 1010°C to 1120°C followed by rapid cooling. Thermal hardening is not suitable for this grade.
High work hardening rate (14MPa increase per 1% reduction in area). Achieves high strength through cold rolling and roll forming. Non-magnetic when annealed, becomes magnetic when cold worked.
Suitable for all standard welding methods. Grade 308L recommended as filler metal. Annealing required after welding for maximum corrosion resistance (not necessary for 301L and 301LN).
Company Details
Business Type:
Manufacturer,Distributor/Wholesaler,Exporter
Total Annual:
>1000000
Employee Number:
>100
Ecer Certification：
Verified Supplier
Our company is located in Wuxi City, China, we are a stainless steel plate, seamless steel pipe, round steel, steel belt, decorative pipe and other products distribution wholesale private enterprise. Our company operates stainless steel plate, seamless steel pipe, round steel, steel belt, decorative... Our company is located in Wuxi City, China, we are a stainless steel plate, seamless steel pipe, round steel, steel belt, decorative pipe and other products distribution wholesale private enterprise. Our company operates stainless steel plate, seamless steel pipe, round steel, steel belt, decorative...
Get in touch with us
Leave a Message, we will call you back quickly!