Hastelloy X 2.4665 N06002 Alloy Steel Round Bar with Corrosion Resistance High

 Hastelloy is a nickel-based corrosion-resistant alloy, which is mainly divided into nickel-chromium alloy and nickel-chromium-molybdenum alloy. Hastelloy has good corrosion resistance and thermal stability, and is used in aviation and chemical fields. Hastelloy is the general name for the commercial grades of nickel-based corrosion-resistant alloys produced by Hastelloy International. 

 Hastelloy X (N06002) Hastelloy Overview:
 Hastelloy X (N06002) Hastelloy is a nickel-based superalloy with high iron content, which is mainly solidified by chromium and molybdenum. It has good resistance to oxidation and corrosion. High temperature alloy HastelloyX is a kind of alloy. A nickel-chromium-molybdenum alloy of cobalt and tungsten is added. With moderate durability and creep strength below 900 °C, cold and hot formability and weldability are good. Used in the manufacture of aero-engine combustor components and other high-temperature components, long-term use below 900 ° C, short-term operating temperature up to 1080 ° C. The main varieties supplied are plates, strips, pipes, bars, forgings, ring parts and precision castings. HastelloyX alloy has excellent oxidation resistance at temperatures up to 1200 ° C and can also be used in neutral and reducing atmospheres. At the same time, HastelloyX alloy is resistant to carbonization and nitriding.
HastelloyX Hastelloy grades and standards:

HastelloyX GH3536, GH536 (China), NC22FeD (France), 2.4665, NiCr22Fe18Mo (Germany), HastelloyX, UNS N06002 (USA) NiCr21Fe18Mo9 (ISO)

Complete specifications, stock in stock   

Strip, sheet (thick plate, medium plate, sheet, steel plate), bar (black bar, light bar, grinding bar, round bar, square bar, steel bar), pipe (capillary, seamless pipe, steel pipe), Forgings (flanges, elbows, bolts, nuts, tees), welding consumables (welding rods, welding wire, welded pipes), wire and other materials.

Chemical Composition Of Hastelloy X 

 Hastelloy X (N06002) Hastelloy heat treatment system:

sheet and pipe: 1130 ~ 1170 ° C, rapid air or water cooling; bar and ring test sample: 1175 ° C ± 15 ° C, air cooling or faster cooling; strip: 1065 ~1105 ° C, rapid cooling.
Hastelloy X (N06002) Hastelloy variety specifications and supply status:

supply δ0.5 ~ 4.0mm sheet, δ0.05 ~ 0.8mm strip, outer diameter 4 ~ 20mm, wall thickness 1.0 ~ 2.0mm pipe, diameter A welding wire of 0.2 to 10.0 mm, a bar of diameter ≤ 300 mm and a ring of various diameters and wall thicknesses, and precision castings of different shapes and sizes. Plates, strips and pipes are supplied after solution treatment and pickling, and the strips can also be supplied in cold-rolled state; the wire is delivered in a hard, semi-hard, solid-melt, pickling, bright solution treatment state. It can also be delivered in straight line; bars and rings are delivered without heat treatment. Precision castings are supplied in the cast state.
Hastelloy X (N06002) Hastelloy smelting and casting process:

using electric arc furnace charging slag or non-vacuum induction furnace charging slag remelting process. The castings are produced by re-melting the master alloy in an induction furnace and then pouring into the heated mold shell, and the pouring speed is preferably as fast as possible.
Hastelloy X (N06002) Hastelloy application overview and special requirements:

The alloy has been widely used in foreign aerospace engines and civil industries, China is mainly used to manufacture combustion chamber components and other hot end components and honeycomb structures. The alloy has a certain age hardening phenomenon after long-term use at high temperatures.

Specifications