AISI 420 Sheet TISCO 20Cr13 SUS420J1 430J2 DIN 1.4021 Stainless Steel Plate 10

AISI 420 Stainless Steel (SS420), UNS S42000

AISI 420 stainless steel (SS420) is a straight chromium martensitic stainless steel grade with certain wear resistance, corrosion resistance and high hardness.

SS420 Datasheet

The tables below give 420 stainless steel (SS420) datasheet and specification including chemical composition, properties, heat treatment, etc.

Chemical Composition

Datasheet 1, The table below shows ASTM AISI 420 stainless steel composition.

AISI 420 Stainless Steel Properties

The datasheets below list type 420 stainless steel (SS420) properties including physical properties and mechanical properties.

Physical Properties

SS 420 stainless steel physical properties are listed in the table below such as density, melting point, specific heat, electrical resistivity, elastic modulus, thermal conductivity, and coefficient of thermal expansion (CTE).

Datasheet 2, 420 stainless steel properties – 1.

Mechanical Properties

AISI 420 stainless steel mechanical properties are given in the datasheet below including tensile strength, yield strength, elongation, reduction in area, Brinell and Rockwell hardness, Charpy impact test, etc.

Datasheet 3, Type 420 stainless steel properties – 2.

Type 420 Stainless Steel Heat Treatment

Type 420 stainless steel heat treatment includes annealing, hardening, tempering and stress relief. Preparation for heat treatment includes precleaning, preheating, atmosphere protection, salt bath, and hydrogen embrittlement.

• Precleaning: All workpieces of SS420 and fixtures must be thoroughly cleaned, such as oil, sweat and other stains on the surface of the workpiece.
• Preheating: The thermal conductivity of type 420 stainless steel is usually lower than that of carbon steel. When heating rapidly, the workpiece is easily deformed and cracked. Therefore, preheating is recommended. The preheating temperature is generally 760-790 °C (1400-1450 °F). Heavy-duty parts can be preheated in two stages: Preheat at 540 °C (1000 °F) firstly, and then heat to 790 °C (1450 °F).
• Atmosphere protection: Austenitizing temperature 1010 °C (1850 °F), dew-point temperature: 10-12 °C (50-54 °F) for AISI 420 wrought martensitic stainless steel.
• Salt bath: Bath salts give 420 grade stainless steel (SS 420) parts a better result.
• Hydrogen embrittlement: Hydrogen embrittlement is a serious problem with 420 steel.

Annealing

Annealing for ASTM AISI 420 wrought stainless steel.

• Subcritical annealing (Recommended) temperature for AISI 420 stainless steel: from 675-760 °C (1245-1400 °F); Air cool from the temperature range, use the upper heating temperature range to minimize hardness. The corresponding Rockwell hardness is 94-97 HRB.
• Full annealing temperature for type 420 steel: 830-885 °C (1525-1625 °F), and then soak thoroughly, furnace cool to 790 °C (1455 °F), continue cooling at 15-25 °C/h (27-45 °F/h) to 595 °C (1100 °F); Air cool to room temperature. The corresponding Rockwell hardness is 86-95 HRB.
• Isothermal annealing temperature for AISI 420 grade stainless steel: Heat to 830-885 °C (1525-1625 °F); keep 2h at 705 °C (1300 °F), the corresponding Rockwell hardness is 95 HRB. (Preheat at subcritical annealing temperature range is very important.)

Hardening

Hardening for 420 grade stainless steel: Heating to austenitizing temperature 980-1065 °C (1800-1950 °F), quenching medium is air or oil, if the part thickness is > 0.25 in. (6.4 mm), oil quenching should be used. After quenching to room temperature, immediate cold treatment is recommended and the recommended cold treatment temperature is -75±10 °C (-100±20 °F), which can reduce austenite and keep maximum dimensional stability.

Tempering

AISI 420 steel (SS420) is very brittle under just hardened conditions and usually must be tempered to achieve useful toughness.

The tempering temperature for 420 grade stainless steel after austenitizing: 205-370 °C (400-700 °F). The corresponding tensile strength and Rockwell hardness are 1550-1930 MPa (225-280 ksi) and 48-56 HRC.

Stress Relieving

If the quenched SS420 does not temper immediately, the stress relief should be carried out quickly.

Forging

Straight chrome AISI type 420 steel is very easy to forge into complex shapes.

Welding

Filler metal for ARC welding of AISI 420 steel: E/ER420, E/ER308, E/ER309.

To obtain a good weld, it’s better to preheat it to a minimum of 200 °C (390 °F) before welding, and then set the post weld heat treatment to 675-750 °C (1250-1380 °F).

Applications

ASTM AISI 420 grade stainless steel (SS 420) is mostly used to manufacture parts resistant to atmospheric, water vapor, water and oxidizing acids.

AISI 420 material (SS420) is used in all kinds of precision machinery, bearings, electrical equipment, instruments, meters, transportation tools, knives, scissors, household appliances, valves, valve components, plunger rods, fittings, guides, parts for chemical plants, shafts, spindles, plastic mold, pumper plunger, cutlery, gears, and rollers.

AISI 420 Equivalent

Type 420 stainless steel equivalent materials are listed in the table below, including Chinese GB, ISO, Japanese JIS, and European EN standard (Germany DIN EN, British BSI…).