Hainan Chenxiang New Material Technology Co., Ltd.
| Packaging Details | 25kg~300kg fine round package; 200kg and 250kg large iron or wood plate package; 25kg/pallet basket package. |
| Warranty | 3 years |
| Customized Support | ODM, OBM, OEM |
| Material | Low Carbon Steel |
| Diameter | 2.5mm/3.2mm/4.0mm/5.0mm |
| Melting Point | As Standard |
| Weight | 25/50/100/200/250/500/1000KG |
| Sample | For Free |
| Delivery | 5-10 days |
| C | 0.07 |
| Mn | 1.61 |
| Si | 0.03 |
| P | 0.12 |
| S | 0.011 |
| Ni | 0.008 |
| Cr | 0.012 |
| Brand Name | CHENXIANG |
| Model Number | WES EH14 |
| Place of Origin | Shandong, China |
View Detail Information
Explore similar products
H10Mn2 Submerged Arc Wire Copper Plated For Carbon Structural Steel
High Strength 3.2mm EH14 Saw Welding Wire For Welding Low Alloy High Strength
Submerged Arc Welding Wire EH14 H10Mn2 2.5mm/3.2mm/4.0mm/5.0mm Diameter
AWS A 5.17 EH14 Submerged Arc Welding Wire / 25KG-300KG Subarc Wire
Product Specification
| Packaging Details | 25kg~300kg fine round package; 200kg and 250kg large iron or wood plate package; 25kg/pallet basket package. | Warranty | 3 years |
| Customized Support | ODM, OBM, OEM | Material | Low Carbon Steel |
| Diameter | 2.5mm/3.2mm/4.0mm/5.0mm | Melting Point | As Standard |
| Weight | 25/50/100/200/250/500/1000KG | Sample | For Free |
| Delivery | 5-10 days | C | 0.07 |
| Mn | 1.61 | Si | 0.03 |
| P | 0.12 | S | 0.011 |
| Ni | 0.008 | Cr | 0.012 |
| Brand Name | CHENXIANG | Model Number | WES EH14 |
| Place of Origin | Shandong, China | ||
| High Light | eh14 submerged arc welding wire ，h10mn2 submerged arc welding wire ，customized saw welding wire | ||
Product Description
H10Mn2 submerged arc welding wire is a non-alloy fine-grained steel submerged arc welding wire with excellent welding processability, easy slag removal, and beautiful weld formation. It is mainly used in conjunction with sintered flux JQ·SJ101, and is suitable for welding base materials with a tensile strength level of 490MPa, such as Q345. Common application areas include ships, pressure vessels, bridges, engineering machinery, construction machinery, and steel structures.
Features
H10Mn2 submerged arc welding wire has high low-temperature toughness and strength, and is suitable for various structural welding that requires high strength and good toughness.
Notes
Welding wire storage: Keep dry and avoid moisture.
Flux selection: Select appropriate flux according to welding materials and process requirements.
Welding environment: Avoid welding in humid or windy environments to avoid affecting welding quality.
Welding process
Welding method: Submerged arc welding (SAW).
Flux matching: Common fluxes such as SJ101, SJ301, etc.
Welding parameters: Select appropriate current, voltage and welding speed according to workpiece thickness, welding position and process requirements.
Preheating and interlayer temperature: For thick plates or low temperature environments, preheating and control of interlayer temperature are required.
Post-weld heat treatment: Post-weld heat treatment is performed when necessary to eliminate residual stress.