Beijing Chuangyuan Construction Engineering Co., Ltd.
| Material | 100% Fiberglass |
| Color | Golden |
| Flame Resistance | Non-combustible / Self-extinguishing |
| Technology | Dewaxed/Desized |
| Supply Ability | 50000 pieces per day |
| Delivery Time | Delivery within 15-30 days |
| Raw Material | Fiber Glass Roving |
| Dimensional Stability | ≤ 0.5% |
| Yarn Type | E-Glass |
| Packaging Details | Wooden frame or cardboard box packaging, customizable |
| Standing Temperature | 550℃ |
| Payment Terms | T/T, PayPal, Xtransfer |
| Application | High Temperature Insulation |
| Place of Origin | Hebei, China |
| Certification | ISO9001 |
View Detail Information
Explore similar products
Fireproof Blanket Heat Treated Fiberglass Cloth Golden For Welding Blanket
Flameproof Plain Weave Heat Treated Fiberglass Fabric Welding Fire Blanket
Heat Cleaned Reinforced Fireproof Fiberglass Fabric 80cm 100cm 127cm Width
Dewaxed Bulk Fiberglass Cloth Roll Heat Treated E Glass Woven Fabric Silicone
Product Specification
| Material | 100% Fiberglass | Color | Golden |
| Flame Resistance | Non-combustible / Self-extinguishing | Technology | Dewaxed/Desized |
| Supply Ability | 50000 pieces per day | Delivery Time | Delivery within 15-30 days |
| Raw Material | Fiber Glass Roving | Dimensional Stability | ≤ 0.5% |
| Yarn Type | E-Glass | Packaging Details | Wooden frame or cardboard box packaging, customizable |
| Standing Temperature | 550℃ | Payment Terms | T/T, PayPal, Xtransfer |
| Application | High Temperature Insulation | Place of Origin | Hebei, China |
| Certification | ISO9001 | ||
| High Light | dewaxed heat treated fiberglass fabric ，heat treated fiberglass fabric waxless ，dewaxed fireproof fiberglass fabric | ||
Asbestos-Free Dewaxed Fiberglass Cloth Heat Treated Waxless Insulation Fabric Welding For Industrial Pipe Boiler Wrapping
The production of hot cleaning fiberglass cloth generally includes the following main steps:
*Raw material preparation: The main raw materials are glass balls or broken glass, as well as other auxiliary materials used to adjust the properties of the glass.
*Melting and Drawing: The raw materials are melted into liquid glass in a high-temperature furnace, and then rapidly drawn into continuous glass fibers with extremely fine diameters through tiny holes on a platinum rhodium alloy plate.
*Wetting agent application: During the drawing process, a chemical coating called "wetting agent" is applied to the surface of the fiber. This layer of coating is crucial for protecting the fibers, enhancing the bonding strength between the fibers and subsequent resin materials.
*Spinning and spinning: Multiple single fiber glass fibers are combined into one strand of raw yarn, and multiple strands of raw yarn are combined into thicker and stronger yarns as needed.
*Weaving: Weaving glass fiber yarn into fabric on a weaving machine according to a set pattern (such as plain weave, diagonal weave).
*Post processing: The woven fabric needs to undergo heat treatment (desizing) to remove the lubricating slurry applied during weaving, and sometimes surface chemical treatment (such as coating with coupling agents) is also carried out according to the purpose to improve its compatibility with materials such as resins.
| Parameter | Specification Range |
|---|---|
| Product Name | Heat Cleaned Fiberglass Fabric |
| Process Type | Heat Cleaning / Thermal Desizing / Heat Treatment |
| Heat Treatment Temperature | 350°C – 650°C (660°F – 1200°F) |
| Weave Structure | Plain Weave / Twill Weave / Satin Weave / Lenor Weave |
| Weight (g/m²) | 50 – 900 g/m² |
| Thickness (mm) | 0.05 – 1.2 mm |
| Width (cm/in) | 80cm / 100cm / 127cm / 150cm / 200cm (31" / 39" / 50" / 59" / 79") |
| Residual Sizing Content | < 0.2% (typically < 0.1%) |
| Tensile Strength (Warp) – After | ≥ 600 – 3500 N/50mm |
| Tensile Strength (Weft) – Before | ≥ 600 – 3500 N/50mm |
| Tensile Strength (Weft) – After | ≥ 450 – 3000 N/50mm |
| Strength Retention Rate | 85% – 92% |
| Elongation at Break | ≤ 3% – 5% |
| Temperature Resistance (Substrate) | 550°C – 800°C (1022°F – 1472°F) |
| Continuous Service Temperature | Up to 550°C (1022°F) |
| Resin Compatibility | Epoxy / Polyester / Vinyl Ester / Phenolic / Silicone / PTFE |
| Coating Compatibility | Silicone / PTFE / Acrylic / Polyurethane / Aluminum |
| Flame Resistance | Non-combustible / Self-extinguishing |
| Moisture Absorption | ≤ 0.5% |
Q. 1: How long is the sample time ? Does the sample fee can be returned?
Company Details
Business Type:
Manufacturer,Exporter,Seller
Year Established:
2018
Total Annual:
180000000-200000000
Employee Number:
260~280
Ecer Certification：
Verified Supplier
Beijing Chuangyuan Construction Engineering Co., Ltd is a specialized manufacturer of high-performance fiberglass textiles based in Beijing, China. With years of industry experience, we focus on the research, development, production, and global distribution of premium glass fiber products for i... Beijing Chuangyuan Construction Engineering Co., Ltd is a specialized manufacturer of high-performance fiberglass textiles based in Beijing, China. With years of industry experience, we focus on the research, development, production, and global distribution of premium glass fiber products for i...
Get in touch with us
Leave a Message, we will call you back quickly!