Zhengzhou Rongsheng Refractory Co., Ltd.
Products
Manufacturer of a wide range of products which include Jm23 Jm26 Mullite Refractory Bricks K23 K26 Mullite Insulating Fire Brick For Hot Blast Furnace,Glass Furnace Lining Mullite Insulation Brick 1700C Insulating Fire Bricks Jm26...
MOQ: 400 rolls
Price:
| Compressive Strength | ≥70MPa |
| Rervice Temperature | 1550 |
| Refractoriness | ≥1790℃ |
| Origin | Xinmi |
| Usage | Glass furnace,steel converter .etc |
| Thermal Shock Resistance | ≥20 times |
| Product | Mullite Insulation Brick |
| Chemical Composition | Al2O3≥70%, SiO2≤30% |
| Water Absorption | ≤1% |
| Certificates | ISO9001 CE |
| Service | Customized service |
| Cold Compressive | 1.2-2.5 Mpa |
| Acid Resistance | Excellent |
| Application | High Temperature Furnace Lining |
| Thermal Expansion | 0.5-0.9% under 1000 ℃ |
| Brand Name | RONGSHENG |
| Certification | ISO9001 |
| Place of Origin | Henan, China |
MOQ: 1 Ton
Price:
| Thermal Conductivity | ≤1.5W/m·K |
| Apparent Porosity | ≥62% |
| Color | White |
| Size | 230x114x65mm |
| Material | Mullite |
| Compressive Strength | ≥70MPa |
| Thermal Expansion | 0.5-0.9% under 1000 ℃ |
| Certificates | ISO9001 CE |
| Performance | Insulation |
| Chemical Composition | Al2O3: 70-80%, SiO2: 20-30% |
| Application | High temperature furnace lining, kiln lining, etc. |
| Refractoriness | ≥1790℃ |
| Origin | Xinmi |
| Density | 2.5-2.7g/cm3 |
| Usage | Glass furnace,steel converter .etc |
| Brand Name | RONGSHENG |
| Certification | ISO9001 |
| Place of Origin | Henan, China |
MOQ:
Price:
| SiO2 Content (%) | 25% max |
| Al2O3 Content (%) | 55% min |
| MgO Content (%) | little |
| CaO Content (%) | little |
| CrO Content (%) | little |
| SiC Content (%) | 1.2-1.4 |
| Brand Name | RONGSHENG |
| Certification | ISO9001 |
| Place of Origin | Henan, China |
MOQ: 1 TON
Price: $150.00 - $500.00 / Ton
| Payment Terms | L/C, T/T, Western Union |
| Supply Ability | 6000 Ton/Tons per Month Insulating refractory mullite fire brick for sale price |
| Delivery Time | 5-8 days |
| Packaging Details | 1.On wooden pallets with plastic cover 2.According to customer's demands Port Qingdao,Tianjin,Dalian,Shanghai |
| Place of Origin: | Henan, China |
| Shape: | Brick |
| Material: | fused mullite or sintered mullite |
| SiO2 Content (%): | max 23% |
| Al2O3 Content (%): | 45-82% |
| MgO Content (%): | little |
| CaO Content (%): | 0.34% |
| SiC Content (%): | 1.2-1.4 |
| Model Number: | Mullite brick, JM mullite Insulating brick |
| Product name: | Insulating refractory mullite fire brick for sale price |
| Brand Name | Rongsheng |
| Model Number | Refractory Brick |
| Certification | ISO9001 |
| Place of Origin | China |
MOQ: 10 Ton
Price: US $ 1000-3000 /Ton
| Supply Ability | 3000Ton/ Month |
| Delivery Time | within 35 working days after receipt T/T advance. |
| Packaging Details | Pallet in size 960*960*1020mm, with cardboard and corner protection,waterproof film. |
| Payment Terms | T/T, Western Union, |
| Product Name | Mullite brick |
| Material | high purity corundum |
| Shape | 230x114x65mm |
| Color | White |
| Apparent Porosity | 18 |
| Efractoriness | 1790 |
| Brand Name | Rongsheng |
| Model Number | RS |
| Certification | ISO9001、CE |
| Place of Origin | Henan |
MOQ:
Price:
| SiO2 Content (%) | 25% max |
| Al2O3 Content (%) | 55% min |
| MgO Content (%) | little |
| CaO Content (%) | little |
| CrO Content (%) | little |
| SiC Content (%) | 1.2-1.4 |
MOQ: 1 piece of brick
Price: USD 568 MT Per Month
| Payment Terms | Western Union, L/C, T/T |
| Delivery Time | 25 Days After Payment |
| Packaging Details | Fumigation Pallet in size 920*920*1030mm with cardboard and corner protection,waterproof film |
| Supply Ability | 1000 Ton Per Month |
| Bulk density | 1.0g/cm3 |
| Cold Crushing Strength | 2.0 |
| Thermal conductivity | 0.25(W/m.k) |
| Al2O3 | 50 |
| Fe2O3 | 0.9 |
| Original | China |
| Brand Name | ZZRS |
| Model Number | JM |
| Certification | CE ISO 9001 |
| Place of Origin | China |
MOQ:
Price: 200-800USD
| AL2O3%≥ | 40 |
| CCS MPA≥ | 2 |
| Packaging Details | packed on wooden pallets, with water-proof cover, and tightened with plastic/steel bandages |
| Delivery Time | 20-30DAYS |
| Payment Terms | TT； L/C |
| Supply Ability | 2000tons /month |
| Place of Origin | Zhengzhou ,China |
| Brand Name | Rongsheng |
| Certification | ISO9001 |
| Model Number | JM23/JM26/JM28 |
MOQ:
Price:
| Cold Compressive | 1.2-2.5 Mpa |
| Original | China |
| Thermal Shock Resistance | ≥300 ℃ |
| Material | bauxite chamotte |
| Bulk Density | 0.6 - 1.0 |
| Apparent Porosity | 18 |
| Rervice Temperature | 1550 |
| Thermalexpansion | 4.5-5.5 x 10^-6 /°C |
| Operatingtemperature | Up to 1750°C |
| Size | 230x114x65mm |
| Thermalshockresistance | Good |
| Max Service Temperature | 1600-1700°C |
| Acid Resistance | Excellent |
| Modulus Of Rupture | ≥15 MPa |
| Thermalconductivity | 1.5-2.0 W/m·K |
| Place of Origin | Henan, China |
| Certification | ISO9001 |
| Brand Name | RONGSHENG |
MOQ:
Price:
| Cold Crushing Strength | ≥70 MPa |
| Rervice Temperature | 1550 |
| Shape | Rectangular brick |
| Flexural Strength | 20-40 MPa |
| Productname | Mullite Brick |
| Thermal Shock Resistance | ≥300 ℃ |
| Certificates | ISO9001 CE |
| Bulk Density | 0.55-1.03 g/cm3 |
| Usage | Glass furnace,steel converter .etc |
| Porosity | 15-20% |
| Material | Mullite |
| Performance | Insulation |
| Product | Mullite Insulation Brick |
| Chemical Composition | Al2O3 70-80%, SiO2 20-30% |
| Density | 2.6-2.8 g/cm³ |
| Certification | ISO9001 |
| Place of Origin | Henan, China |
| Brand Name | RONGSHENG |
Explore more categories
Get in touch with us
Leave a Message, we will call you back quickly!