Manufacturer of a wide range of products which include High Temperature Unshaped Refractories A600 Ca60 Ca80 High Alumina Refractory Cement For Furnace Construction,Furnace Kiln Oven Phosphate Bonded Unshape Refractory Material Hi...
MOQ:
Price:
| Usage | industrial furnace |
| Origin | China |
| Service Temperature | 900~1700℃ |
| Maximum Service Temperature | 1800°C |
| Corrosion Resistance | Excellent |
| Size | 0-3mm,5%/3-5mm,35%/5-8mm,40%/8-15mm,20% |
| Shape | powder |
| Transport Package | 25kg/bag |
| Made | Henan |
| Country Of Origin | Henan China |
| Product | Low Cement Castable |
| Thermal Shock Resistence | 50 |
| Water Content | ≤ 5% |
| Package | 25kgs/50kgs bag |
| Refractoriness | ≥ 1700°C |
| Brand Name | RONGSHENG |
| Model Number | 10101-52-7 |
| Certification | ISO9001 |
| Place of Origin | Henan, China |
MOQ: 1 Ton
Price:
| Feature | Thermal Shock Resistance |
| Permanent Linear Change | 1400℃*3h |
| Firing Linear Change | ±0.5 |
| Water Content | ≤0.5% |
| Type | Ceramic Raw Materials |
| Thermal Conductivity | 2.5 W/m·K |
| Initial Setting Time | ≥60% |
| Compressive Strength | 100 MPa |
| Transport Package | 25kg/bag |
| Abrasion Resistance | Excellent |
| Refractoriness | ≥1750°C |
| Sample | Freely |
| Raw Material | Al2O3 powder |
| Application Temperature | ≥1200℃ |
| Curing Time | 24 hours |
| Brand Name | RONGSHENG |
| Certification | ISO9001 |
| Place of Origin | Henan, China |
MOQ: 1 Ton
Price:
| Installation Method | Vibration Casting |
| Abrasion Resistance | Excellent |
| Water Addition | 6-8% |
| Compressive Strength | 20 Mpa |
| Volume Density | 2.6 |
| Curing Method | Air Setting |
| Type | Low Cement Castable |
| Appliction | tundish lining |
| Bending Strength Mpa | 8~20 |
| Origin | China |
| Oem | Yes |
| Working Temperature | 1800℃ |
| Thermal Conductivity | 3 W/mK |
| Castable Color | Gray |
| Color | Light Grey |
| Brand Name | RONGSHENG |
| Certification | ISO9001 |
MOQ:
Price:
| Initial Setting | ＞1 hour |
| Raw Material | High Alumina Bauxite |
| Max Service Temp | ≥1550 |
| Refractoriness | 1750℃ |
| Shape | Power |
| Raw Materials | Bauxite Particle |
| Curing Method | Air Setting |
| Application | Furnace lining, kiln lining, incinerator lining |
| Feature | Thermal Shock Resistance |
| Bulk Density | 2.5 g/cm3 |
| Construction Method | Vibration and Self flow castable |
| Maximum Service Temp | 1500 |
| Calcium Oxide Content | ≤15% |
| Usage | Refractoy |
| Product | Acid-Resistant Castable |
| Brand Name | RONGSHENG |
| Model Number | 10101-52-7 |
| Certification | ISO9001 |
| Place of Origin | Henan, China |
MOQ:
Price:
| Final Setting Time | ≤6h |
| Apparent Porosity | ≤18% |
| Port | Tianji / Shang hai/qingdao/ningbo |
| Usage | furnace bottom |
| Abrasion Resistance | Excellent |
| Appliction | tundish lining |
| Bulk Density | 2.5 g/cm3 |
| Calcium Oxide Content | ≤15% |
| Origin | China |
| Sample | Avaliable |
| Mgo | 10% |
| Working Temperature | max1650 |
| Maximum Service Temperature | 1800°C |
| Max Service Temp | ≥1550 |
| Compressive Strength | ≥80 MPa |
| Brand Name | RONGSHENG |
| Place of Origin | Henan, China |
MOQ:
Price:
| Country Of Origin | China |
| Color | Gray,Brown,Light yellow |
| Water Content | ≤0.5% |
| Rupture Strength Mpa | 4.0 |
| Oem | Yes |
| Type | High Alumina Castable |
| Working Temperature | 1300-1600C |
| Feature | High refractoriness under load |
| Processing Service | mixing |
| Size | Customized |
| Mgo | ≥80 |
| Product | High Alumina Castable |
| Maximum Service Temperature | 1800°C |
| Temperature | 1350℃ |
| Maximum Service Temp | 1500 |
| Brand Name | RONGSHENG |
| Place of Origin | Henan, China |
MOQ:
Price:
| Imax Servce Temperature | 700℃~1400℃ |
| Raw Material | Corundum |
| Advantage | Operate convinniently |
| Curing Time | 24 hours |
| Refractoriness | ≥ 1700°C |
| Made | Henan |
| Color | Gray |
| Type | Factory |
| Shape | Particle |
| Bulkdensity | 1.8 - 2.5 g/cm³ |
| Shrinkage | ≤ 1.5% after firing |
| Settingtime | Initial set 2-6 hours, final set 12-24 hours |
| Mgo | 10% |
| Package | Woven Bags |
| Flexural Strength | 1d ≥5.0MPa |
| Place of Origin | Henan, China |
| Brand Name | RONGSHENG |
| Certification | ISO9001 |
MOQ:
Price:
| Type | manufacturer |
| Usage | Furnace Liner |
| Final Setting | ＞8 hourS |
| Packing | bag |
| Installationmethod | Casting or gunning |
| Mixingratio | Water to castable ratio typically 5-7% |
| Country Of Origin | China |
| Product | High Alumina Castable |
| Thermalshockresistance | Good |
| Material Strength | High material strength |
| Compressivestrength | ≥ 50 MPa |
| Origin | China |
| Ph Value | 9 - 11 |
| Bulk Density | 1.8 - 2.5 g/cm³ |
| Cao | 30% |
| Certification | ISO9001 |
| Place of Origin | Henan, China |
| Brand Name | RONGSHENG |
MOQ:
Price:
| Working Temperature | 1800℃ |
| Packing | Fumigated Wooden Pallet |
| Phvalue | Neutral to slightly alkaline |
| Appliction | tundish lining |
| Strength | High |
| Permanent Linear Change | ±0.4 |
| Thermal Shock Resistence | 50 |
| Package | Wooden Pallet |
| Water Content | ≤ 5% |
| Firing Linear Change | ±0.5/0 ~ +1.5/±1.0 |
| Raw Material | High Alumina Bauxite |
| Final Setting Time | ≤6h |
| Sample | Sample Provided |
| Product | Low Cement Castable |
| Curingtime | 24 to 72 hours depending on temperature |
| Certification | ISO9001 |
| Place of Origin | Henan, China |
| Brand Name | RONGSHENG |
MOQ: 5 Ton
Price: US $500-1,000 / Ton
| Supply Ability | 3000 Ton/ Month |
| Delivery Time | 15 days after payment |
| Packaging Details | 25kg in a woven bags,then 40 bags in a ton bag or in a wooden pallet. Customized is also ok |
| Payment Terms | T/T, Western Union, |
| Material | Steel fibre |
| Color | gray |
| Made | Henan |
| Al2O3 | ≥75 |
| Bulk density | 2.7 |
| Shape | powder |
| Brand Name | Rongsheng |
| Model Number | YH-F16K |
| Certification | ISO9001、CE |
| Place of Origin | Henan |
Explore more categories
Get in touch with us
Leave a Message, we will call you back quickly!