Zhengzhou Rongsheng Refractory Co., Ltd.
| Transport Package | 25kg/bag |
| Corrosion Resistance | Good |
| Bending Strength Mpa | 8~20 |
| Bulk Density | 0.6-1.0g/cm3 |
| Resistance To Abrasion | High |
| Cold Crushing Strength | 2-5MPa |
| Firing Linear Change | ±0.5 |
| Features | High Temperature Resistant |
| Compressive Strength | customizable |
| Maximum Service Temp | 1500 |
| Curingtime | 24 - 72 hours depending on formulation |
| Maximumservicetemperature | Up to 1800°C |
| Castable Color | Gray |
| Service Temperature | 1000℃-1800℃ |
| Compressivestrength | ≥ 50 MPa at 1100°C |
| Brand Name | RONGSHENG |
| Certification | ISO9001 |
| Place of Origin | Henan, China |
View Detail Information
Explore similar products
High Temperature Unshaped Refractories A600 Ca60 Ca80 High Alumina Refractory
Furnace Kiln Oven Phosphate Bonded Unshape Refractory Material High Alumina
High Temperature Kiln Castable Refractory Cement Quick-Drying Explosion-Proof
High Performance Low Cement Castable Refractory Mullite Castable For High
Product Specification
| Transport Package | 25kg/bag | Corrosion Resistance | Good |
| Bending Strength Mpa | 8~20 | Bulk Density | 0.6-1.0g/cm3 |
| Resistance To Abrasion | High | Cold Crushing Strength | 2-5MPa |
| Firing Linear Change | ±0.5 | Features | High Temperature Resistant |
| Compressive Strength | customizable | Maximum Service Temp | 1500 |
| Curingtime | 24 - 72 hours depending on formulation | Maximumservicetemperature | Up to 1800°C |
| Castable Color | Gray | Service Temperature | 1000℃-1800℃ |
| Compressivestrength | ≥ 50 MPa at 1100°C | Brand Name | RONGSHENG |
| Certification | ISO9001 | Place of Origin | Henan, China |
| High Light | low cement refractory castable ，high alumina castable for furnace ，refractory casting for boiler lining | ||
High Alumina Castable Introduction
High alumina refractory castable is an unshape material made by mixing high alumina bauxite as the main refractory aggregate, adding additives, binders, and other materials. Mixing with water can be directly used, using vibration casting for molding. Generally speaking, the operating temperature range is between 1400 ° C and 1600 ° C. High alumina castable can be directly cast into an integral lining on industrial furnaces or prefabricated into fire-resistant prefabricated blocks, which can be used for masonry in industrial furnaces.
Characteristic of High Alumina Castable
1.Has a certain degree of corrosion resistance;
2.High refractory temperature and high load softening temperature;
3.High compressive strength and excellent thermal shock resistance;
4.High density, low porosity.
5. Good resistance to flake performance.
| Item | Specification | |||
| Clay | High Alumina | Corundum | ||
| Al2O3 % | ≥45 | ≥75 | ≥98 | |
| CaO % | <1.8 | <1.5 | <1.0 | |
| Bulk Density, g/cm3 | 110℃×24h | ≥2.3 | ≥2.6 | ≥3.1 |
| 1350℃×3h | ≥2.26 | ≥2.61 | / | |
| 1550℃×3h | / | / | ≥3.00 | |
| CCS, MPa | 110℃×24h | ≥70 | ≥75 | ≥85 |
| 1350℃×3h | ≥85 | ≥90 | / | |
| 1550℃×3h | / | / | ≥100 | |
| CMOR, MPa | 110℃×24h | ≥6 | ≥8 | ≥9 |
| 1350℃×3h | ≥8 | ≥9 | / | |
| 1550℃×3h | / | / | ≥11 | |
| PLC, % | 1000℃×3h | -0.3 | -0.2 | -0.2 |
| 1350℃×3h | ±0.3 | ±0.5 | / | |
| 1550℃×3h | / | / | ±0.5 | |
| Max Working Temperature, ℃ | 1450 | 1600 | 1800 | |
Company Details
Business Type:
Manufacturer
Year Established:
2011
Total Annual:
20000000-50000000
Employee Number:
101~150
Ecer Certification：
Verified Supplier
Our company can provide not only the domestic and foreign customers excellent quality of high-temperature thermal insulation material, but also the first-rate service including professional furnace lining design, installation supervision, engineering construction etc. <p style="... Our company can provide not only the domestic and foreign customers excellent quality of high-temperature thermal insulation material, but also the first-rate service including professional furnace lining design, installation supervision, engineering construction etc. <p style="...