| Appliction | tundish lining |
| Packing | Fumigated Wooden Pallet |
| Abrasion Resistance | Good |
| Customized | yes |
| Settingtime | Initial set 2-4 hours, final set 24 hours |
| Compressivestrength | ≥ 50 MPa (after firing) |
| Strength | High |
| Calcium Oxide Content | ≤15% |
| Imax Servce Temperature | 700℃~1400℃ |
| Color | Gray or off-white |
| Bulk Density | 2.0g/cm3 |
| Materialtype | High alumina, silica, magnesia, or other refractory aggregates |
| Raw Materials | Bauxite Particle |
| Operatingtemperature | Up to 1800°C |
| Thermalconductivity | 0.7 - 1.5 W/m·K |
| Place of Origin | Henan, China |
| Certification | ISO9001 |
| Brand Name | RONGSHENG |
View Detail Information
Explore similar products
High Temperature Unshaped Refractories A600 Ca60 Ca80 High Alumina Refractory
Furnace Kiln Oven Phosphate Bonded Unshape Refractory Material High Alumina
High Temperature Kiln Castable Refractory Cement Quick-Drying Explosion-Proof
High Performance Low Cement Castable Refractory Mullite Castable For High
Product Specification
| Appliction | tundish lining | Packing | Fumigated Wooden Pallet |
| Abrasion Resistance | Good | Customized | yes |
| Settingtime | Initial set 2-4 hours, final set 24 hours | Compressivestrength | ≥ 50 MPa (after firing) |
| Strength | High | Calcium Oxide Content | ≤15% |
| Imax Servce Temperature | 700℃~1400℃ | Color | Gray or off-white |
| Bulk Density | 2.0g/cm3 | Materialtype | High alumina, silica, magnesia, or other refractory aggregates |
| Raw Materials | Bauxite Particle | Operatingtemperature | Up to 1800°C |
| Thermalconductivity | 0.7 - 1.5 W/m·K | Place of Origin | Henan, China |
| Certification | ISO9001 | Brand Name | RONGSHENG |
| High Light | refractory castable non-metallic material ，inorganic chemicals refractory products ，high-temperature refractory castable | ||
Features and Advantages of Refractory Gunning Mix
refractory gunning mix has the characteristics of high adhesive rate,less resilience,high strength and easy gunning etc.scour resistance,impact resistance,erosion resistance.anti-scouring, wear resistance and excellent performances.
Application of Refractory Gunning Mix
Steel Industry,Energy Industry,Building Materials.It serves as a protective layer on the inner surface of blast furnace and hot blast furnace shells, as well as a working lining for blast furnace heads, coal gas outlet pipe, and dust collectors.
Refractory Material Gunning Mix Technique Data
| Item | Specification | |||
| LGP0.8 | LGP1.0 | LGP1.3 | ||
| Al2O3 % | ≥30 | ≥35 | ≥40 | |
| Bulk Density,g/cm3 110℃×24h | ≤0.8 | ≤1.0 | ≤1.3 | |
| CCS, MPa | 110℃×24h | ≥4 | ≥5 | ≥7 |
| Test Temperature, ×3h | ≥3 800℃ | ≥4 1000℃ | ≥5 1200℃ | |
| PLC, % Test Temperature, ×3h |
±0.8 800℃ |
±0.8 1000℃ |
±0.8 1200℃ |
|
| Thermal Conductivity, W/(m·K) 350℃±25℃ | ≤0.21 | ≤0.25 | ≤0.35 | |
| Test Temperature, ℃ | 800 | 1000 | 1200 | |
| Item | Specification | |||
| LGP1.5 | LGP1.8 | LGP1.8T | ||
| Al2O3 % | ≥42 | ≥45 | ≥55 | |
| Bulk Density,g/cm3 110℃×24h | ≤1.5 | ≤1.8 | ≤1.8 | |
| CCS, MPa | 100℃×24h | ≥12 | ≥15 | ≥12 |
| Test Temperature, ×3h | ≥10 1300℃ | ≥13 1300℃ | ≥10 1400℃ | |
| PLC, % Test Temperature×3h |
±0.8 1300℃ |
±0.8 1300℃ |
±1.0 1400℃ |
|
| Thermal Conductivity, W/(m·K) 350℃±25℃ | ≤0.4 | ≤0.7 | ≤0.75 | |
| Max Working Temperature, ℃ | 1300 | 1300 | 1500 | |
Company Details
Business Type:
Manufacturer
Year Established:
2011
Total Annual:
20000000-50000000
Employee Number:
101~150
Ecer Certification：
Verified Supplier
Our company can provide not only the domestic and foreign customers excellent quality of high-temperature thermal insulation material, but also the first-rate service including professional furnace lining design, installation supervision, engineering construction etc. <p style="... Our company can provide not only the domestic and foreign customers excellent quality of high-temperature thermal insulation material, but also the first-rate service including professional furnace lining design, installation supervision, engineering construction etc. <p style="...
Get in touch with us
Leave a Message, we will call you back quickly!