Shenzhen KangLiBang Technology Co., Ltd
| Payment Terms | T/T,Western Union |
| Delivery Time | 5-8 work days |
| Packaging Details | 1KG/bottle |
| Viscosity | High |
| Shelf Life | 6 months |
| Curing Method | Heat |
| Type | Ink |
| Substrates | Silicone rubber, coated fabrics, plastics, etc. |
| Color | Clear |
| Curing Time | 1-2 minutes |
| Application | Screen printing |
| Opacity | Opaque |
| Resistance | Chemical, water, and abrasion |
| Gloss Level | Glossy |
| Curing Temperature | 150-200°C |
| Base Material | Silicone |
| Brand Name | KangLiBang |
| Certification | ROHS，SGS |
| Place of Origin | Guangdong, China |
View Detail Information
Explore similar products
Silicone Rubber Spraying Coating Ink Cured At High Temperature
Kanglibang Two Components Soft Touching Coating for Silicone Rubber General Use
Soft Touch Feel Oil Coating for Silicone Rubber Surface Using Like Bracelet
Kanglibang Two Components Soft Touching Coating for Silicone Rubber Good
Product Specification
| Payment Terms | T/T,Western Union | Delivery Time | 5-8 work days |
| Packaging Details | 1KG/bottle | Viscosity | High |
| Shelf Life | 6 months | Curing Method | Heat |
| Type | Ink | Substrates | Silicone rubber, coated fabrics, plastics, etc. |
| Color | Clear | Curing Time | 1-2 minutes |
| Application | Screen printing | Opacity | Opaque |
| Resistance | Chemical, water, and abrasion | Gloss Level | Glossy |
| Curing Temperature | 150-200°C | Base Material | Silicone |
| Brand Name | KangLiBang | Certification | ROHS，SGS |
| Place of Origin | Guangdong, China | ||
| High Light | food grade silicone spray ink ，soft smooth hand feel ink ，silicone product spray ink | ||
Soft Touch Coating Oil
This two-component system cures at low temperatures and is designed for use as an outer layer on pre-cured silicone rubber surfaces. After application, it requires high-temperature curing (190–220°C). The coating delivers a smooth hand feel, excellent resistance to friction, protection against dust, and superior coverage and adhesion. It is commonly found on silicone rubber keypads, adult products, photocopiers, and household devices such as remote controllers.
Product specifications:
Typical Data
|
Appearance |
Shallow transparent flowing liquid |
|
Solid Contents |
≥55% |
|
Viscosity |
≥10000mPa.s |
Processing methods:
1. Engage the ready silicone rubber in second cure (190℃-200℃, 8-10minutes ), wash clean the surfaces
2. Add 3% of platinum catalyst into the silicone resin for mixture and dilute with solvent(white gas) six times ,try small quantity first followed by mass input of the solvent when diluting the silicone resin.
3. Please filtrate with 300-400 mesh filter screen for twice before uploading in the spraying gun
4. Leave alone the ready silicone resin for 3-8minutes in the dust-free plant before the spraying process.
Baking method
Baking Condition(190-200℃) 8 – 10 min
|
Processing |
Spray |
|
Spraying Viscosity (Iwata2#Cup,25℃). |
8-10 |
|
Spraying Distance cm |
20-25 |
|
Spray Mouth Diameter mm |
0.8/1.0 |
|
Spraying Pressure mPa |
0.2-0.3 |
|
Baking Condition(190-200℃)min |
8-10 |
Attentions:
1. The opened product shall be mixed uniformly. During ink processing, the platinum catalyst is to be added before the ink is diluted.
2. Spraying should be performed in a suitable environment, ideally a dust‑free plant, where the temperature is maintained at 20–30°C and humidity at 55–75%.
3. The silicone rubber must be subjected to a second cure at a temperature above 150°C for 10 to 30 minutes; otherwise, inadequate curing of the paint on the silicone rubber surfaces will occur.
4. The temperature is to be raised slowly throughout the curing stage. Immediate baking after the spraying process results in poor gloss.
5. The mixed silicone resin must be consumed within 12 hours. If stored sealed at a low temperature, its activation period can be extended.
Applications:
About Us
Company Details
Business Type:
Manufacturer
Year Established:
2010
Total Annual:
5000000-10000000
Employee Number:
50~100
Ecer Certification：
Verified Supplier
Shenzhen Kanglibang Science & Technology Co., Ltd was founded in 2010, focusing on the development of new adhesive materials. It is a national-level specialized and special "little giant" enterprise integrating the research and development, manufacturing, sales and service of adhesive ... Shenzhen Kanglibang Science & Technology Co., Ltd was founded in 2010, focusing on the development of new adhesive materials. It is a national-level specialized and special "little giant" enterprise integrating the research and development, manufacturing, sales and service of adhesive ...
Get in touch with us
Leave a Message, we will call you back quickly!