JIANGSU MITTEL STEEL INDUSTRIAL LIMITED
| Shape | Round |
| Technique | Hot Rolled |
| Surface Treatment | Bright |
| Diameter Range | OD 6-300mm |
| Production Capacity | 50000kgs |
| Tensile Strength | 1105-1310 MPa |
| Yield Strength | 1000-1170 MPa |
| Elongation | 10-16% |
| Hardness | 28-44 HRC |
| Density | 7750 kg/m³ |
| Thermal Conductivity | 18.4-22.7 W/m.K |
| Specific Heat | 460 J/kg.K |
| Electrical Resistivity | 800 nΩ.m |
| Max Temperature | 572°F (300°C) |
| Certification | ISO, AISI, ASTM, EN, DIN, JIS |
| Model Number | 17-4pH/SUS630 |
View Detail Information
Explore similar products
ASTM A276 Bright Annealing UNS S17400 Stainless Steel Round Bar with OD 6-300mm
Hot Rolled Bright Surface 17-4PH Stainless Steel Round Bar UNS S17400 with OD 6
Grade 201 Stainless Steel Bright Bar Hot Rolled with Diameter 3mm - 50mm
ASTM 276 Grade 304 Bright Polished Stainless Steel Round Bar Diameter 3-150mm
Product Specification
| Shape | Round | Technique | Hot Rolled |
| Surface Treatment | Bright | Diameter Range | OD 6-300mm |
| Production Capacity | 50000kgs | Tensile Strength | 1105-1310 MPa |
| Yield Strength | 1000-1170 MPa | Elongation | 10-16% |
| Hardness | 28-44 HRC | Density | 7750 kg/m³ |
| Thermal Conductivity | 18.4-22.7 W/m.K | Specific Heat | 460 J/kg.K |
| Electrical Resistivity | 800 nΩ.m | Max Temperature | 572°F (300°C) |
| Certification | ISO, AISI, ASTM, EN, DIN, JIS | Model Number | 17-4pH/SUS630 |
| High Light | Hot Rolled Stainless Steel Round Bar ，Bright Surface 17-4PH Round Bar ，OD 6-300mm SUS630 Round Bar | ||
17-4 Precipitation Hardening (Type 630) is a chromium-copper precipitation hardening stainless steel designed for applications requiring high strength and moderate corrosion resistance. This alloy maintains high strength up to approximately 600°F (316°C).
Alloy 17-4 PH is a precipitation hardening martensitic stainless steel with copper and niobium additions. It combines high strength, hardness (up to 572°F/300°C), and excellent corrosion resistance. Mechanical properties can be optimized through heat treatment, achieving very high yield strength up to 1100-1300 MPa (160-190 ksi).
Alloy 17-4 PH provides superior corrosion resistance compared to standard hardenable stainless steels and is comparable to Alloy 304 in most media. For optimal performance in chloride media, aging temperatures above 1022°F (550°C) are recommended, while 1094°F (590°C) is optimal for H2S media applications.
| Element | Content (%) |
|---|---|
| C | 0.07 max |
| Mn | 1.0 max |
| Si | 1.0 max |
| P | 0.04 max |
| S | 0.030 max |
| Cr | 15.0 - 17.5 |
| Ni | 3.0 - 5.0 |
| Cu | 3.0 - 5.0 |
| Nb+Ta | 0.15 - 0.45 |
| Condition | Tensile Strength (MPa) | Yield Strength (MPa) | Elongation (%) | Hardness (HRC) |
|---|---|---|---|---|
| Solution Treated | 1105 typ | 1000 typ | 15 typ | 38 max |
| Condition 900 | 1310 min | 1170 min | 10 min | 40 min |
| Condition 1150 | 930 min | 724 min | 16 min | 28 min |
| Property | Value |
|---|---|
| Density | 7750 kg/m³ |
| Thermal Expansion (0-100°C) | 10.8 µm/m/°C |
| Thermal Conductivity (100°C) | 18.4 W/m·K |
| Specific Heat | 460 J/kg·K |
| Electrical Resistivity | 800 nΩ·m |
Grade 630 stainless steels undergo solution treatment at 1040°C for 0.5 hours followed by air cooling. Age hardening at various temperatures achieves the required mechanical properties with minimal distortion.
| Condition | Hardening Temp (°C) | Time (h) | Typical Hardness (HRC) | Tensile Strength (MPa) |
|---|---|---|---|---|
| A | Ann | - | 36 | 1100 |
| H900 | 482 | 1 | 44 | - |
| H925 | 496 | 4 | 42 | 1170-1320 |
| H1150 | 621 | 4 | 33 | 930-1080 |
Welding: Grade 630 can be welded using all conventional methods without pre-heating requirements.
Machining: Best machined in solution-treated condition with rates similar to grade 304 stainless steel.
Company Details
Business Type:
Manufacturer,Distributor/Wholesaler,Exporter
Total Annual:
>1000000
Employee Number:
>100
Ecer Certification：
Verified Supplier
Our company is located in Wuxi City, China, we are a stainless steel plate, seamless steel pipe, round steel, steel belt, decorative pipe and other products distribution wholesale private enterprise. Our company operates stainless steel plate, seamless steel pipe, round steel, steel belt, decorative... Our company is located in Wuxi City, China, we are a stainless steel plate, seamless steel pipe, round steel, steel belt, decorative pipe and other products distribution wholesale private enterprise. Our company operates stainless steel plate, seamless steel pipe, round steel, steel belt, decorative...
Get in touch with us
Leave a Message, we will call you back quickly!