Wuxi Raymond Steel Co., Ltd.
| Packaging Details | standard export packing |
| Delivery Time | 30 days |
| Payment Terms | L/C, T/T |
| Supply Ability | 100000 |
| Product Name | Hot Dipped Galvanized Steel Coil (GI Coil) |
| Brand | HY |
| Steel Grade | SGCC / SGCD / SGCE / SGCH / DX51D+Z / DX52D+Z / DX53D+Z |
| Thickness | 0.09–3.8 mm |
| Width | 1000–1250 mm |
| Zinc Coating | Z60–Z275 |
| Yield Strength | 195–420 MPa |
| Tensile Strength | 270–500 MPa |
| Elongation | 12–25% |
| Surface Treatment | Chromated / Oiled / Bright / Dry |
| Process | Cold Rolled Base + Hot Dip Galvanizing |
| Standard | ASTM A653 / JIS G3302 / EN 10147 |
| Coil Weight | 3–8 MT |
| Coil ID | 508 mm / 610 mm |
| MOQ | 50 MT |
| Brand Name | HY |
| Place of Origin | China |
| Certification | ISO |
View Detail Information
Explore similar products
508mm ID Hot Dipped Galvanized Steel Coil for Furniture Panels and General Sheet
SGCC ASTM A653 Hot Dipped Galvanized Steel Coil for Furniture Manufacturing and
DX51D+AZ Galvalume Steel Coil with AZ30–AZ150 Coating and 914–1250mm Width for
3.8mm DX51D Hot Dipped Galvanized Steel Coil with 40–450g/m² Zinc Coating for
Product Specification
| Packaging Details | standard export packing | Delivery Time | 30 days |
| Payment Terms | L/C, T/T | Supply Ability | 100000 |
| Product Name | Hot Dipped Galvanized Steel Coil (GI Coil) | Brand | HY |
| Steel Grade | SGCC / SGCD / SGCE / SGCH / DX51D+Z / DX52D+Z / DX53D+Z | Thickness | 0.09–3.8 mm |
| Width | 1000–1250 mm | Zinc Coating | Z60–Z275 |
| Yield Strength | 195–420 MPa | Tensile Strength | 270–500 MPa |
| Elongation | 12–25% | Surface Treatment | Chromated / Oiled / Bright / Dry |
| Process | Cold Rolled Base + Hot Dip Galvanizing | Standard | ASTM A653 / JIS G3302 / EN 10147 |
| Coil Weight | 3–8 MT | Coil ID | 508 mm / 610 mm |
| MOQ | 50 MT | Brand Name | HY |
| Place of Origin | China | Certification | ISO |
| High Light | Width 1000-1250mm Hot Dipped Galvanized Steel Coils ，Yield Strength 195-420N/mm2 HDG Steel Coils ，Tensile Strength 270-500N/mm2 Galvanized Steel Coils | ||
1000–1250mm Width Hot Dipped Galvanized Steel Coil Z60–Z275 with 195–420 MPa Yield Strength for Structural and Manufacturing Use
1. Product Overview
Hot dipped galvanized steel coils are produced by immersing cleaned steel substrate into molten zinc, forming a metallurgically bonded coating. This process provides stable corrosion resistance and consistent surface quality, suitable for structural parts and downstream sheet fabrication.
The width range of 1000–1250 mm aligns with mainstream slitting and forming equipment, improving processing efficiency for manufacturing and construction applications.
2. Technical Solution
Product performance is determined by:
Yield strength 195–420 MPa supports load-bearing applications, while tensile strength 270–500 MPa ensures resistance to deformation during fabrication and service.
3. Specifications
|
Parameter |
Value |
|---|---|
|
Thickness |
0.09–3.8 mm |
|
Width |
1000–1250 mm |
|
Zinc Coating |
Z60–Z275 |
|
Yield Strength |
195–420 MPa |
|
Tensile Strength |
270–500 MPa |
|
Elongation |
12–25% |
|
Surface |
Chromated / Oiled / Bright / Dry |
|
Coil Weight |
3–8 MT |
|
Coil ID |
508 / 610 mm |
|
Standard |
ASTM A653 / JIS G3302 / EN 10147 |
4. Application
5. Processing
6. Advantages
7. How to Choose
8. FAQ
Q1: What coating level should be used for outdoor applications?
Higher zinc coating such as Z200–Z275 is generally used for improved corrosion resistance.
Q2: Can the coils be processed into sheets?
Yes, coils are commonly slit or cut into sheets depending on application.
Q3: What surface treatment is suitable for storage?
Oiled or chromated surfaces are typically used to reduce oxidation during storage and transport.
Q4: Is the material suitable for forming operations?
Yes, elongation 12–25% supports bending, stamping, and roll forming processes.
Q5: What coil sizes are compatible with standard equipment?
Coil IDs of 508 mm and 610 mm are compatible with most industrial processing lines.
Company Details
Business Type:
Manufacturer,Exporter,Trading Company,Seller
Year Established:
2000
Total Annual:
> 10,000,000
Employee Number:
501~1000
Ecer Certification：
Verified Supplier
Wuxi Raymond Steel Co., Ltd. was founded in Oct., 2000, with total investment of 25 million U.S Dollars, which is a large-scale iron and Steel enterprise specialized in producing hot-rolled and cold-rolled steel strip. Wuxi Raymond Steel Co., Ltd. is situated in the region of Shitangwan Industria... Wuxi Raymond Steel Co., Ltd. was founded in Oct., 2000, with total investment of 25 million U.S Dollars, which is a large-scale iron and Steel enterprise specialized in producing hot-rolled and cold-rolled steel strip. Wuxi Raymond Steel Co., Ltd. is situated in the region of Shitangwan Industria...
Get in touch with us
Leave a Message, we will call you back quickly!