Manufacturer of a wide range of products which include Square Silicon Wafer with Film-Laminated Carrier for Advanced IC, Semiconductor,Custom 4-Inch (100mm) Silicon Wafers: 350μm Thickness, Orientation, DSP/SSP, N,TGV（Through-G...
MOQ: 10
Price:
| Payment Terms | T/T |
| Delivery Time | 2-4 Weeks |
| Material | Prime Grade Monocrystalline Silicon |
| Wafer Type | Square with Film-Laminated Carrier |
| Dimensions | 2″ (50.8mm) standard; custom sizes available |
| Thickness | Customizable up to 725 μm |
| Growth Method | Czochralski (CZ) |
| TTV | <0.3 μm |
| Surface Finish | Single Side Polished (SSP) or Double Side Polished (DSP) |
| Carrier Film | Protective laminated film, removable before processing |
| Brand Name | ZMSH |
| Place of Origin | SHANGHAI,CHINA |
MOQ:
Price:
| Payment Terms | T/T |
| Delivery Time | 4-6 weeks |
| Material | Si single crystal |
| Size | 4 inch |
| Thickness | 350 um |
| Crystal Orientation | <100> |
| Density | 2.4 g/cm3 |
| Doping Type | P type or N type |
| Brand Name | ZMSH |
| Model Number | Si wafer |
| Place of Origin | China |
MOQ:
Price:
| Payment Terms | T/T |
| Delivery Time | In 30 days |
| Hole diameter | 3um/5um/10um/25um |
| Hole pitch | Via diameter x2 |
| Glass thickness | <50um/<100um/<200um/<0.7mm |
| Glass size | ≤ 4"/≤6"/<8"/≤510x510mm |
| Hole Density(Hole/mm) | 25k/10k/2.5k/400 |
| Hole Density(Hole/inch) | 4k/2.5k/1.2k/500 |
| Brand Name | ZMSH |
| Model Number | TGV glass |
| Place of Origin | China |
MOQ: 20
Price:
| Payment Terms | T/T |
| Delivery Time | 2-4 WEEKS |
| Chemical Formula | ZrO₂ |
| Crystal Structure | Monoclinic / Tetragonal / Cubic |
| Density | 5.68 g/cm³ |
| Melting Point | 2,715°C |
| Hardness (Vickers) | 1,200 – 1,400HV |
| Fracture Toughness | 7 – 10MPa·m¹ᐟ² |
| Thermal Conductivity | 2 – 3W/m·K |
| Electrical Resistivity | >10¹²Ω·cm |
| Brand Name | ZMSH |
| Place of Origin | SHANGHAI,CHINA |
MOQ: 10
Price:
| Payment Terms | T/T |
| Delivery Time | 2-4 WEEKS |
| Material | Silicon Carbide (SiC) |
| Purity | ≥ 99% (typical) |
| Density | 3.10 – 3.20 g/cm³ |
| Hardness | ≥ 2500 HV |
| Flexural Strength | ≥ 350 MPa |
| Elastic Modulus | ~410 GPa |
| Thermal Conductivity | 120 – 200 W/m·K |
| Coefficient of Thermal Expansion (CTE) | ~4.0 × 10⁻⁶ /K |
| Brand Name | ZMSH |
| Place of Origin | SHANGHAI,CHINA |
MOQ: 25
Price: By case
| Payment Terms | T/T |
| Delivery Time | 2-4weeks |
| Packaging Details | package in 100-grade cleaning room |
| Size/Shape | Customized |
| Alumina (Al₂O₃) Purity | ≥ 99.6% |
| Bulk Density | ≥ 3.90 g/cm³ |
| Flexural Strength | ≥ 350 MPa |
| Thermal Conductivity | ~25-30 W/(m·K) |
| Volume Resistivity | > 10¹⁴ Ω·cm @ 25°C |
| Surface Roughness (Ra) | < 0.2 μm |
| Applications | Electronics and Power Industry,Medical and Biotechnology |
| Brand Name | ZMSH |
| Model Number | Alumina Ceramic Custom Components |
| Certification | rohs |
| Place of Origin | CHINA |
MOQ: 10
Price:
| Payment Terms | T/T |
| Delivery Time | 2-4 Weeks |
| Material | High-purity Silicon Carbide (SiC) |
| Purity | 99.9% |
| Color | Black |
| Density | 3.0–3.2 g/cm³ |
| Poisson's Ratio | 0.15–0.21 |
| Fracture Toughness | 2–4 MPa·m^1/2 |
| Vickers Hardness | 21–28 GPa |
| Flexural Strength | 400–600 MPa |
| Compressive Strength | 2200 MPa |
| Elastic Modulus | 400–450 GPa |
| Thermal Expansion (20–1000°C) | 4–4.6×10^-6/K |
| Thermal Conductivity | 100–230 W/m·K |
| Maximum Operating Temperature | 1300–1650°C |
| Electrical Resistivity | 1–4×10^5 Ω·cm |
| Brand Name | ZMSH |
| Place of Origin | SHANGHAI,CHINA |
MOQ: 10
Price:
| Payment Terms | T/T |
| Delivery Time | 2-4 Weeks |
| Material | High-purity Silicon Carbide (SiC) |
| Purity | 99.9% |
| Density | 3.0–3.2 g/cm³ |
| Poisson's Ratio | 0.15–0.21 |
| Fracture Toughness | 2–4 MPa·m^1/2 |
| Vickers Hardness | 21–28 GPa |
| Flexural Strength | 400–600 MPa |
| Compressive Strength | 2200 MPa |
| Elastic Modulus | 400–450 GPa |
| Thermal Expansion (20–1000°C) | 4–4.6×10^-6/K |
| Thermal Conductivity | 100–230 W/m·K |
| Maximum Operating Temperature | 1300–1650°C |
| Electrical Resistivity | 1–4×10^5 Ω·cm |
| Brand Name | ZMSH |
| Place of Origin | SHANGHAI,CHINA |
MOQ: 100
Price:
| Payment Terms | T/T |
| Delivery Time | 2-4 Weeks |
| Material | High-purity Zirconia (ZrO₂) |
| Minimum Outer Diameter (OD) | 0.02 mm |
| Maximum Length | 500 mm |
| Surface Roughness | Ra 0.1 µm |
| Tolerance | ±0.001 mm (ultra-precision customization available) |
| Brand Name | ZMSH |
| Place of Origin | SHANGHAI,CHINA |
MOQ: 1000
Price:
| Payment Terms | T/T |
| Delivery Time | 2-4 WEEKS |
| Chemical Formula | SiC |
| Purity | 95% ~ 99% |
| Color | Black |
| Appearance | Smooth, polished surface |
| Size Range | From 0.8mm to 60mm in diameter (Custom sizes available) |
| Density | 3.05 - 3.15 g/cm³ |
| Max Operating Temperature | Up to 1550°C |
| Thermal Conductivity | 120 W/m·K @ 20°C |
| Flexural Strength | Up to 400 MPa |
| Compressive Strength | Up to 2200 MPa |
| Brand Name | ZMSH |
| Place of Origin | SHANGHAI,CHINA |